Variation of the microstructure and fracture strength of cold isostatically pressed alumina ceramics with the alteration of dewaxing procedures

[1]  K. Uematsu,et al.  Formation mechanisms of processing defects and their relevance to the strength in alumina ceramics made by powder compaction process , 1999 .

[2]  K. Uematsu,et al.  Characterization of processing pores and their relevance to the strength in alumina ceramics , 1999 .

[3]  K. Uematsu,et al.  Origin of strength change in ceramics associated with the alteration of spray dryer , 1999 .

[4]  K. Uematsu,et al.  Effect of seasons on density, strength of alumina , 1999 .

[5]  H. Kamiya,et al.  Microscopic analysis on the consolidation process of granule beds , 1998 .

[6]  K. Uematsu.  Immersion microscopy for detailed characterization of defects in ceramic powders and green bodies , 1996 .

[7]  Hideo Takahashi,et al.  Influence of Granule Character and Compaction on the Mechanical Properties of Sintered Silicon Nitride , 1996 .

[8]  Hideo Takahashi,et al.  Influence of Slurry Flocculation on the Character and Compaction of Spray‐Dried Silicon Nitride Granules , 1995 .

[9]  K. Uematsu,et al.  Effect of Moisture on the Structure and Fracture Strength of Ceramic Green Bodies , 1994 .

[10]  H. Takahashi,et al.  Microstructure evolution and mechanical strength of silicon nitride ceramics , 1994 .

[11]  M. Inoue,et al.  Effect of processing conditions on the characteristics of pores in hot isostatically pressed alumina , 1993, Journal of Materials Science.

[12]  Z. Kato,et al.  Effect of Forming Pressure on the Internal Structure of Alumina Green Bodies Examined with Immersion Liquid Technique , 1991 .

[13]  J. S. Reed,et al.  Particle and Granule Parameters Affecting Compaction Efficiency in Dry Pressing , 1988 .