The influence of manufacturing parameters on the properties of macroporous Zirfon® separators

The manufacturing of the macroporous Zirfon® separator is based on the film casting technique. This film casting technique allows different manufacturing steps to be varied in order to adapt both the composition and the structure of the separator to the specific requirements of the application. The Zirfon® separators can be used in alkaline electrochemical cells as a replacement of asbestos. At a temperature of 30 °C the ionic resistance of the separator is as low as about 0.01 Ω. Bubble-Point (BP) pressures as high as 1 MPa could be obtained.

[1] 李幼升,et al. Ph , 1989 .

[2] J. Moreels,et al. Porosity in composite zirfon® membranes , 1996 .

[3] R. Leysen,et al. Evaluation of the Zirfon® separator for use in alkaline water electrolysis and Ni-H2 batteries , 1998 .

[4] Marcel Mulder,et al. Basic Principles of Membrane Technology , 1991 .

[5] H. Yasuda,et al. Pore size of microporous polymer membranes , 1974 .

[6] R. Leysen,et al. Zirfon®: A new separator for NiH2 batteries and alkaline fuel cells , 1996 .

[7] Paul C. Schmitz,et al. European Space Power Conference , 1991 .

[8] S. Hwang,et al. Formation of asymmetric polysulfone membranes by immersion precipitation. Part II. The effects of casting solution and gelation bath compositions on membrane structure and skin formation , 1992 .

[9] Shoichi Doi,et al. Pore size control technique in the spinning of polysulfone hollow fiber ultrafiltration membranes , 1991 .