Determination of mode-I fracture toughness and non-uniformity for GFRP double cantilever beam specimens with an adhesive layer

Abstract The mode-I fracture behavior and non-uniformity coefficient β of an adhesively bonded joint composed of Glass Fiber-reinforced Polymer (GFRP) laminates are investigated using double cantilever beam (DCB) specimens with an adhesive layer. First, the opening displacement of the DCB is solved using the elastic foundation beam method considering the impact of the displacement and the rotation angle of the crack tip. The fracture toughness G Ic is calculated using the compliance method through the critical load ( P c ) obtained from the experiment. During the crack growth in the experiment and in the finite element analysis, a thumbnail-shaped front is observed, which demonstrates that the energy release rate (ERR) is unevenly distributed along the transversal direction. Next, a practical formula for β as a function of the parameters a / b (crack length/width) and n (number of plies) is put forward, which can be applied to DCB specimens composed of isotropic single-ply plates or anti-symmetric angle-laid laminate plates (each leg). Finally, crack propagation is simulated using a modified G Ic ∗ , which includes the non-uniformity coefficient β , from which the simulated P c is in good agreement with the experimental results.

[1]  De Xie,et al.  Strain energy release rate calculation for a moving delamination front of arbitrary shape based on the virtual crack closure technique. Part I: Formulation and validation , 2006 .

[2]  S. S. Wang,et al.  An analysis of the crack tip stress field in DCB adhesive fracture specimens , 1978 .

[3]  J. G. Williams,et al.  The calculation of adhesive fracture energies in mode I: revisiting the tapered double cantilever beam (TDCB) test , 2003 .

[4]  A. P. Vassilopoulos,et al.  Mode I and II fracture behavior of adhesively-bonded pultruded composite joints , 2010 .

[5]  T. Keller,et al.  Joining techniques for fiber reinforced polymer composite bridge deck systems , 2005 .

[6]  Alojz Ivankovic,et al.  Effects of bond gap thickness on the fracture of nano-toughened epoxy adhesive joints , 2012 .

[7]  J. Williams.  End corrections for orthotropic DCB specimens , 1989 .

[8]  R. Olsson.  A simplified improved beam analysis of the DCB specimen , 1992 .

[9]  B.D. Davidson,et al.  An Analytical Investigation of Delamination Front Curvature in Double Cantilever Beam Specimens , 1990 .

[10]  K. N. Shivakumar,et al.  A virtual crack-closure technique for calculating stress intensity factors for cracked three dimensional bodies , 1988, International Journal of Fracture.

[11]  F. E. Penado,et al.  A Closed Form Solution for the Energy Release Rate of the Double Cantilever Beam Specimen with an Adhesive Layer , 1993 .

[12]  M. D. Moura,et al.  Cohesive laws of composite bonded joints under mode I loading , 2013 .

[13]  A. P. Vassilopoulos,et al.  A phenomenological analysis of Mode I fracture of adhesively-bonded pultruded GFRP joints , 2011 .

[14]  G. Verchery,et al.  On the determination of delamination toughness by using multidirectional DCB specimens , 2010 .

[15]  A. B. de Morais,et al.  Double cantilever beam testing of multidirectional laminates , 2003 .

[16]  De Xie,et al.  Strain energy release rate calculation for a moving delamination front of arbitrary shape based on the virtual crack closure technique. Part II: Sensitivity study on modeling details , 2006 .

[17]  Homayoun Hadavinia,et al.  Determination of fracture energy and tensile cohesive strength in Mode I delamination of angle-ply laminated composites , 2008 .

[18]  M. Shokrieh,et al.  Influence of curved delamination front on toughness of multidirectional DCB specimens , 2012 .

[19]  Anthony J. Kinloch,et al.  Measuring the mode I adhesive fracture energy, GIC, of structural adhesive joints: the results of an international round-robin , 2003 .

[20]  M. F. Kanninen,et al.  An augmented double cantilever beam model for studying crack propagation and arrest , 1973, International Journal of Fracture.

[21]  A. Ureña,et al.  Mode-I adhesive fracture energy of carbon fibre composite joints with nanoreinforced epoxy adhesives , 2011 .

[22]  Pedro P. Camanho,et al.  Analysis of crack propagation in double cantilever beam tests of multidirectional laminates , 2003 .

[23]  Arthur J. Helmicki,et al.  CLOSE LOOK AT CONSTRUCTION ISSUES AND PERFORMANCE OF FOUR FIBER-REINFORCED POLYMER COMPOSITE BRIDGE DECKS , 2004 .

[24]  L. Carlsson,et al.  Beam analysis of angle-ply laminate DCB specimens , 1999 .

[25]  P. Davies,et al.  Mixed mode failure criteria for a glass/epoxy composite and an adhesively bonded composite/composite joint , 2000 .

[26]  K. Kondo.  Analysis of double cantilever beam specimen , 1995 .

[27]  Modeling of through-thickness stress state in adhesive joints connecting pultruded FRP bridge decks and steel girders , 2009 .

[28]  M. D. Thouless,et al.  Use of mode-I cohesive-zone models to describe the fracture of an adhesively-bonded polymer-matrix composite , 2005 .