Finite element simulation of steel ring fragmentation under radial expansion

Abstract This paper presents a numerical analysis of the expansion of a mild steel ring with of 50 mm diameter, 1 mm thickness and a cross section of 1 mm2. A hardening relation which takes into account strain, strain rate and temperature is proposed to define precisely the thermoviscoplastic behaviour of the material considered in the study. As a second step, an algorithm to integrate the thermoviscoplastic constitutive equations, including the hardening law, is implemented in the commercial finite element code ABAQUS/Explicit via a user subroutine. Finally, this tool is used to simulate the problem of a ring expanding radially in a broad range of strain rates, covering both low and high initial velocities (from 1 to 370 m/s). The aim is to analyse the effect of loading velocity on the number of fragments resulting from the multiple failure of the ring and also the influence of the hardening behaviour of the material on the number of fragments and on the failure mode of the ring, considering different values of the plastic strain hardening exponent n0. A simple failure criterion was used, based on a critical value of the equivalent strain which depends on the hardening exponent. The numerical predictions, in perfect agreement with the experimental observations, are compared with several analytical or numerical models used to solve the same problem in other materials such as aluminium, steel or copper.

[1]  M. S. Bola,et al.  Dynamic tensile deformation and fracture of metal cylinders at high strain rates , 2002 .

[2]  Ares J. Rosakis,et al.  Partition of plastic work into heat and stored energy in metals , 2000 .

[3]  D. Macdougall,et al.  Determination of the plastic work converted to heat using radiometry , 2000 .

[4]  U. F. Kocks.  Thermodynamics and kinetics of slip , 1975 .

[5]  M. Ortiz,et al.  Computational modelling of impact damage in brittle materials , 1996 .

[6]  P. Krysl,et al.  Finite Element Simulation of Ring Expansion and Fragmentation , 1999 .

[7]  J. Klepaczko.  Thermally activated flow and strain rate history effects for some polycrystalline f.c.c. metals , 1975 .

[8]  D. C. Drucker,et al.  A DEFINITION OF STABLE INELASTIC MATERIAL , 1957 .

[9]  N. Triantafyllidis,et al.  Onset of necking in electro-magnetically formed rings , 2004 .

[10]  Kristina Nilsson.  Effects of elastic unloading on multiple necking in tensile bars , 2004 .

[11]  Ramón Zaera,et al.  Analysis of inertia and scale effects on dynamic neck formation during tension of sheet steel , 2005 .

[12]  Xiaopeng Xu,et al.  Numerical simulations of fast crack growth in brittle solids , 1994 .

[13]  Glenn S. Daehn,et al.  Increased ductility in high velocity electromagnetic ring expansion , 1996 .

[14]  Glenn S. Daehn,et al.  Effect of velocity on flow localization in tension , 1996 .

[15]  A. Molinari,et al.  Analysis of multiple necking in rings under rapid radial expansion , 2004 .

[16]  W. W. Wood.  Experimental mechanics at velocity extremes —Very high strain rates , 1967 .

[17]  Chris J. Pearce,et al.  Viscoplastic Hoffman consistency model for concrete , 2001 .

[18]  A. Molinari,et al.  Predictions of bifurcation and instabilities during dynamic extension , 2003 .

[19]  M. Ortiz,et al.  Adaptive Lagrangian modelling of ballistic penetration of metallic targets , 1997 .

[20]  Piotr Perzyna,et al.  The constitutive equations for rate sensitive plastic materials , 1963 .

[21]  D. E. Grady,et al.  Fragmentation of metal rings by electromagnetic loading , 1983 .

[22]  E. I. Riegner,et al.  The development of orthogonal bicolored moiré fringes , 1972 .

[23]  J. R. Klepaczko,et al.  Shear testing of a sheet steel at wide range of strain rates and a constitutive relation with strain-rate and temperature dependence of the flow stress , 2001 .

[24]  M. Considére.  Mémoire sur l'emploi du fer et de l'acier dans les constructions , 1885 .

[25]  Effects of inertia on dynamic neck formation in tensile bars , 2001 .

[26]  L. Freund,et al.  Unstable neck formation in a ductile ring subjected to impulsive radial loading , 2000 .

[27]  R. Becker,et al.  Ring fragmentation predictions using the Gurson model with material stability conditions as failure criteria , 2002 .

[28]  Frithiof I. Niordson,et al.  A unit for testing materials at high strain rates , 1965 .

[29]  Alan Needleman,et al.  Instability and failure of internally pressurized ductile metal cylinders , 1982 .

[30]  Alain Molinari,et al.  Instability and localization of plastic flow in shear at high strain rates , 1987 .

[31]  M. Ortiz,et al.  FINITE-DEFORMATION IRREVERSIBLE COHESIVE ELEMENTS FOR THREE-DIMENSIONAL CRACK-PROPAGATION ANALYSIS , 1999 .

[32]  P. Krysl,et al.  Finite element simulation of ring expansion and fragmentation: The capturing of length and time scales through cohesive models of fracture , 1999 .

[33]  L. J. Sluys,et al.  Viscoplasticity for instabilities due to strain softening and strain‐rate softening , 1997 .

[34]  J. Fernández-Sáez,et al.  An implicit consistent algorithm for the integration of thermoviscoplastic constitutive equations in adiabatic conditions and finite deformations , 2006 .

[35]  L. Freund,et al.  The dynamics of multiple neck formation and fragmentation in high rate extension of ductile materials , 2002 .

[36]  V. Tvergaard,et al.  Effect of inertia on the necking behaviour of ring specimens under rapid radial expansion , 1995 .

[37]  René de Borst,et al.  A comparison between the Perzyna viscoplastic model and the consistency viscoplastic model , 2002 .

[38]  Wing Kam Liu,et al.  IMPACT - Effects of Fast Transient Loadings , 1988 .