Bacterial cellulose films with controlled microstructure–mechanical property relationships

Bacterial cellulose (BC) films with different porosities have been developed in order to obtain improved mechanical properties. After 13 days of incubation of Gluconobacter xylinum bacteria in static culture, BC pellicles have been set. BC films have been compression molded after water dispersion of BC pellicles and filtration by applying different pressures (10, 50, and 100 MPa) to obtain films with different porosities. Tensile behavior has been analyzed in order to discuss the microstructure–property relationships. Compression pressure has been found as an important parameter to control the final mechanical properties of BC films where slightly enhanced tensile strength and deformation at break are obtained increasing mold compression pressure, while modulus also increases following a nearly linear dependence upon film porosity. This behavior is related to the higher densification by increasing mold compression pressure that reduces the interfibrillar space, thus increasing the possibility of interfibrillar bonding zones. Network theories have been applied to relate film elastic properties with individual nanofiber properties.

[1]  L. Segal',et al.  An Empirical Method for Estimating the Degree of Crystallinity of Native Cellulose Using the X-Ray Diffractometer , 1959 .

[2]  M. Skłodowskiej-Curie.  Applying the WAXS method to estimate the supermolecular structure of cellulose fibres after mercerisation , 2003 .

[3]  L. Gu,et al.  Direct dissolution of cellulose in NaOH/thiourea/urea aqueous solution. , 2007, Carbohydrate research.

[4]  J. Sugiyama,et al.  Structural modification of bacterial cellulose , 2000 .

[5]  Marielle Henriksson,et al.  Cellulose nanopaper structures of high toughness. , 2008, Biomacromolecules.

[6]  V. Kumar,et al.  Effect of compressional force on the crystallinity of directly compressible cellulose excipients. , 1999, International journal of pharmaceutics.

[7]  W. Wan,et al.  Measurement of the elastic modulus of single bacterial cellulose fibers using atomic force microscopy. , 2005, Langmuir : the ACS journal of surfaces and colloids.

[8]  J. Putaux,et al.  Cellulose microfibrils from banana rachis: effect of alkaline treatments on structural and morphological features. , 2009 .

[9]  M. Sain,et al.  Biocomposites from wheat straw nanofibers: Morphology, thermal and mechanical properties , 2008 .

[10]  D. Klemm,et al.  Cellulose: fascinating biopolymer and sustainable raw material. , 2005, Angewandte Chemie.

[11]  A. N. Nakagaito,et al.  Nano-fibrillation of pulp fibers for the processing of transparent nanocomposites , 2007 .

[12]  H. L. Cox.  The elasticity and strength of paper and other fibrous materials , 1952 .

[13]  Stephen J. Eichhorn,et al.  The Young's modulus of a microcrystalline cellulose , 2001 .

[14]  Stephen J. Eichhorn,et al.  An estimation of the Young’s modulus of bacterial cellulose filaments , 2008 .

[15]  J. Keckes,et al.  Tensile properties of cellulose acetate butyrate composites reinforced with bacterial cellulose , 2004 .

[16]  Fredrik Nicklasson,et al.  Effect of pellet size on degree of deformation and densification during compression and on compactability of microcrystalline cellulose pellets , 1998 .

[17]  G. Alderborn,et al.  The effect of shape and porosity on the compression behaviour and tablet forming ability of granular materials formed from microcrystalline cellulose. , 2001, European journal of pharmaceutics and biopharmaceutics : official journal of Arbeitsgemeinschaft fur Pharmazeutische Verfahrenstechnik e.V.

[18]  J. Seferis,et al.  Predictions of limiting mechanical performance for anisotropic crystalline polymers , 1976 .

[19]  Hiroyuki Yano,et al.  The effect of morphological changes from pulp fiber towards nano-scale fibrillated cellulose on the mechanical properties of high-strength plant fiber based composites , 2004 .

[20]  Y. Nishi,et al.  The structure and mechanical properties of sheets prepared from bacterial cellulose , 1989 .

[21]  Y. Nishi,et al.  The structure and mechanical properties of sheets prepared from bacterial cellulose , 1990 .

[22]  Biao Wang,et al.  Cellulose synthesized by Acetobacter xylinum in the presence of multi-walled carbon nanotubes. , 2008, Carbohydrate research.

[23]  H. Yano,et al.  Bacterial cellulose: the ultimate nano-scalar cellulose morphology for the production of high-strength composites , 2005 .

[24]  Kunihiko Watanabe,et al.  Structural Features and Properties of Bacterial Cellulose Produced in Agitated Culture , 1998 .

[25]  J. Gong,et al.  Tubular bacterial cellulose gel with oriented fibrils on the curved surface , 2008 .

[26]  Stephen J. Eichhorn,et al.  Deformation mechanisms in cellulose fibres, paper and wood , 2001 .

[27]  M. Ansell,et al.  The determination of porosity and cellulose content of plant fibers by density methods , 2001 .

[28]  H. Fink,et al.  Relation between structure and elastic constants of man-made cellulosic fibers. I: A two phase anisotropic model with contiguity parameter , 1994 .