Characterization of Heterogeneous Microstructure Evolution in ZrO2–3 mol%Y2O3 during Isothermal Sintering

Pore boundary tessellation and quantitative stereology were used to characterize microstructure evolution in ZrO 2 -3 mol%Y 2 O 3 (3YSZ) that had been pressed to a green density of 46% and isothermally sintered at 1275°C for 0.1-10 h. Scanning electron micrographs showed that, relative to classical sintering models, the sintered 3YSZ microstructure was spatially heterogeneous, and that this heterogeneity affected the way in which the microstructure evolved during sintering. Pore boundary tessellation cell maps revealed the presence of dense regions within the microstructure that grew by the preferential elimination of smaller pores and resulted in larger more widely spaced porosity at longer sintering times. In consequence, the average pore separation distance increased much faster than the average grain size. This would call into question the use of the grain size as a measure of microstructural scale for the prediction of densification kinetics for this material.

[1]  A. Krell,et al.  Effects of the Homogeneity of Particle Coordination on Solid‐State Sintering of Transparent Alumina , 2006 .

[2]  I. Chen,et al.  Two‐Step Sintering of Ceramics with Constant Grain‐Size, I. Y2O3 , 2006 .

[3]  N. Enomoto,et al.  Sintering Kinetics at Constant Rates of Heating: Effect of Al2O3 on the Initial Sintering Stage of Fine Zirconia Powder , 2005 .

[4]  I. Nettleship,et al.  A mesoscale description of microstructure evolution for the sintering of ceramics , 2005 .

[5]  M. Mayo,et al.  Pore Growth during Initial-Stage Sintering , 2004 .

[6]  I. Nettleship,et al.  Microstructural pathways for the densification of slip cast alumina , 2003 .

[7]  Hongwei Ma,et al.  Processing of High‐Density Submicrometer Al2O3 for New Applications , 2003 .

[8]  I. Chen,et al.  Sintering of Fine Oxide Powders: I, Microstructural Evolution , 1996 .

[9]  D. Johnson,et al.  Master Sintering Curve: A Practical Approach to Sintering , 1996 .

[10]  R. P. Rusin,et al.  Combined-Stage Sintering Model , 1992 .

[11]  L. C. Jonghe,et al.  Effect of Green Density on Densification and Creep During Sintering , 1991 .

[12]  R. Raj,et al.  Better sintering through green-state deformation processing , 1990 .

[13]  B. Kellett,et al.  Thermodynamics of densification. II: Grain growth in porous compacts and relation to densification , 1989 .

[14]  B. Kellett,et al.  Thermodynamics of Densification: I, Sintering of Simple Particle Arrays, Equilibrium Configurations, Pore Stability, and Shrinkage , 1989 .

[15]  M. Harmer,et al.  Effect of MgO Solute on Microstructure Development in Al2O3 , 1986 .

[16]  Frederick F. Lange,et al.  Sinterability of Agglomerated Powders , 1984 .

[17]  H. Bowen,et al.  Formation, Packing, and Sintering of Monodisperse TiO2 Powders , 1982 .

[18]  N. A. Pratten The precise measurement of the density of small samples , 1981 .

[19]  W. H. Rhodes,et al.  Agglomerate and Particle Size Effects on Sintering Yttria‐Stabilized Zirconia , 1981 .

[20]  R. L. Coble,et al.  Sintering Crystalline Solids. I. Intermediate and Final State Diffusion Models , 1961 .

[21]  W. Kingery,et al.  Study of the Initial Stages of Sintering Solids by Viscous Flow, Evaporation‐Condensation, and Self‐Diffusion , 1955 .

[22]  H. Verweij,et al.  Grain Growth in Ultrafine-Grained Y-TZP Ceramics , 1997 .

[23]  R. Brook Pore‐Grain Boundary Interactions and Grain Growth , 1969 .