Influence of Adding Modifying Elements and Homogenization Annealing on Laser Melting Process of the Modified AlZnMgCu with 4%Si Alloys

AlZnMgCu, the high-strength aluminum alloy, is unsuitable for laser melting applications due to its high hot cracking sensitivity and large solidification temperature range. Adapting this alloy for laser melting processing is a high-demand research issue for extending its use. Thus, this paper investigates the effect of adding 4%Si, 4%Si-Sc+Zr, 4%Si-Ti+B, and homogenization annealing on the laser melting process (LMP) of AlZnMgCu alloy. Homogenization annealing at 500 °C for 6.5 h was selected to dissolve most of the low melting temperature phases into the grain matrix and perform stable alloys for the LMP. The pulsed laser melting process (PLM) was performed on the as-casted and the homogenized samples. The microstructures of the as-casted, the homogenized alloys, and after the LMP were evaluated. In addition, the hardness of the base metal (BM) and laser melted zone (LMZ) were measured. The results revealed that the microstructure was enhanced and refined in the as-cast state by adding the modifiers due to the increasing nucleation potency of solidification sites and the formation of primary Al3(Ti, Zr, Sc) phases. The average grain size was decreased by 15.6 times when adding 4%Si + 0.4%Zr + 0.29%Sc, while it decreased by 10.2 times when adding 4%Si + 1%Ti + 0.2%B. The LMZ of the as-casted samples exhibited a non-uniform distribution of the grains and the elements after the LMP. This was attributed to the evaporation of Zn, Mg during the high laser power process besides the non-uniform distribution of elements and phases in samples during casting. After the laser treating of the homogenized samples with 4%Si-Sc + Zr, uniform columnar grains were formed in the direction of the laser. The presence of Ti and B changed the crystallization nature, resulting in the LMZ with very fine and equiaxed grains due to forming many nucleation centers during solidification. The hardness values have positively increased due to Si addition and adding a combination of Ti + B and Sc + Zr. The maximum hardness was 153.9 ± 5 HV achieved in the LMZ of the homogenized samples of 4%Si + 1%Ti + 0.2%B.

[1]  Shen‐gen Zhang,et al.  The Advancement of 7XXX Series Aluminum Alloys for Aircraft Structures: A Review , 2021, Metals.

[2]  J. Blandin,et al.  Cracking mechanism and its sensitivity to processing conditions during laser powder bed fusion of a structural aluminum alloy , 2021 .

[3]  Lin Lin,et al.  Effect of Two-Stage Homogenization Heat Treatment on Microstructure and Mechanical Properties of AA2060 Alloy , 2020, Crystals.

[4]  Ahmed O. Mosleh,et al.  Controlling liquation behavior and solidification cracks by continuous laser melting process of AA-7075 aluminum alloy , 2020 .

[5]  T. Yuan,et al.  Microstructure, metallurgical defects and hardness of Al–Cu–Mg–Li–Zr alloy additively manufactured by selective laser melting , 2020 .

[6]  Zhiheng Hu,et al.  A high strength Al–Li alloy produced by laser powder bed fusion: Densification, microstructure, and mechanical properties , 2020 .

[7]  S. Sasaki,et al.  Effects of the addition of silicon to 7075 aluminum alloy on microstructure, mechanical properties, and selective laser melting processability , 2020 .

[8]  M. Bermingham,et al.  A novel method to 3D-print fine-grained AlSi10Mg alloy with isotropic properties via inoculation with LaB6 nanoparticles , 2020 .

[9]  Haihong Zhu,et al.  Effect of Si content on the cracking behavior of selective laser melted Al7050 , 2019, Rapid Prototyping Journal.

[10]  G. Ji,et al.  Effect of nano-TiB2 particles on the anisotropy in an AlSi10Mg alloy processed by selective laser melting , 2019, Journal of Alloys and Compounds.

[11]  Xinhua Wu,et al.  Selective laser melting of a high strength Al Mn Sc alloy: Alloy design and strengthening mechanisms , 2019, Acta Materialia.

[12]  Weidong Huang,et al.  Laser solid forming additive manufacturing TiB2 reinforced 2024Al composite: Microstructure and mechanical properties , 2019, Materials Science and Engineering: A.

[13]  A. Prosviryakov,et al.  The Effect of Isothermal Multi-Directional Forging on the Grain Structure, Superplasticity, and Mechanical Properties of the Conventional Al–Mg-Based Alloy , 2019, Metals.

[14]  B. McWilliams,et al.  Microstructure and tensile property of a novel AlZnMgScZr alloy additively manufactured by gas atomization and laser powder bed fusion , 2019, Scripta Materialia.

[15]  Andres Tovar,et al.  Review of additive manufacturing technologies and applications in the aerospace industry , 2019, Additive Manufacturing for the Aerospace Industry.

[16]  Ahmed O. Mosleh,et al.  Effect of Multidirectional Forging on the Grain Structure and Mechanical Properties of the Al–Mg–Mn Alloy , 2018, Materials.

[17]  M. Bermingham,et al.  Grain refinement of laser remelted Al-7Si and 6061 aluminium alloys with Tibor® and scandium additions , 2018, Journal of Manufacturing Processes.

[18]  Zhiheng Hu,et al.  Effect of Zr content on formability, microstructure and mechanical properties of selective laser melted Zr modified Al-4.24Cu-1.97Mg-0.56Mn alloys , 2018, Journal of Alloys and Compounds.

[19]  T. Niendorf,et al.  A heat treatable TiB2/Al-3.5Cu-1.5Mg-1Si composite fabricated by selective laser melting: Microstructure, heat treatment and mechanical properties , 2018 .

[20]  Z. Fan,et al.  A new concept for growth restriction during solidification , 2018 .

[21]  F. Calignano,et al.  Laser Powder Bed Fusion of a High Strength Al-Si-Zn-Mg-Cu Alloy , 2018 .

[22]  A. Rack,et al.  A Three-Stage Mechanistic Model for Solidification Cracking During Welding of Steel , 2018, Metallurgical and Materials Transactions A.

[23]  T. Pollock,et al.  3D printing of high-strength aluminium alloys , 2017, Nature.

[24]  A. Borisov,et al.  High-strain-rate superplasticity of the Al–Zn–Mg–Cu alloys with Fe and Ni additions , 2017, Physics of Metals and Metallography.

[25]  A. Spierings,et al.  SLM-processed Sc- and Zr- modified Al-Mg alloy: Mechanical properties and microstructural effects of heat treatment , 2017 .

[26]  Zhiheng Hu,et al.  Effect of Zirconium addition on crack, microstructure and mechanical behavior of selective laser melted Al-Cu-Mg alloy , 2017 .

[27]  P. Rometsch,et al.  Characterisation of a novel Sc and Zr modified Al–Mg alloy fabricated by selective laser melting , 2017 .

[28]  Zhiheng Hu,et al.  POROSITY DEVELOPMENT AND CRACKING BEHAVIOR OF Al-Zn-Mg-Cu ALLOYS FABRICATED BY SELECTIVE LASER MELTING , 2017 .

[29]  A. L. Greer.  Overview: Application of heterogeneous nucleation in grain-refining of metals. , 2016, The Journal of chemical physics.

[30]  J. Kruth,et al.  Changing the alloy composition of Al7075 for better processability by selective laser melting , 2016 .

[31]  D. Raabe,et al.  Precipitation Reactions in Age-Hardenable Alloys During Laser Additive Manufacturing , 2016 .

[32]  F. Walther,et al.  Influence of Process Parameters on the Quality of Aluminium Alloy EN AW 7075 Using Selective Laser Melting (SLM) , 2016 .

[33]  S. Kou.  A criterion for cracking during solidification , 2015 .

[34]  T. Watt,et al.  Comparison of Alsi10mg and Al 6061 Processed through Dmls , 2014 .

[35]  Zhilin Liu,et al.  Revisiting the role of peritectics in grain refinement of Al alloys , 2013 .

[36]  Darin Thomas,et al.  Additive Manufacturing for the Aerospace Industry , 2012 .

[37]  Christopher J. Sutcliffe,et al.  Selective laser melting of aluminium components , 2011 .

[38]  I. Polmear,et al.  Light Alloys: From Traditional Alloys to Nanocrystals , 2006 .

[39]  J. Drezet,et al.  A new hot-tearing criterion , 1999 .