Controlled drug release from hydrogel nanoparticle networks.

Monodisperse nanoparticles of poly-N-isopropylacrylamide-co-allylamine (PNIPAM-co-allylamine) and PNIPAM-co-acrylic acid (PNIPAM-co-AA) were synthesized. The close-packed PNIPAM-co-allylamine and PNIPAM-co-AA nanoparticles were converted to three-dimensional gel networks by covalently crosslinking neighboring particles at room temperature and neutral pH using glutaric dialdehyde and adipic acid dihydrazide, respectively. Controlled release studies were conducted using dextran markers of various molecular weights as model macromolecular drugs. Release was quantified under various physical conditions, including a range of temperatures and dextran molecular weights. Dextran, entrapped in cavities in the nanoparticle network, was released with a rate regulated by their molecular weights and cavity size. No release from a conventional bulk PNIPAM gel, with high crosslinking density, was observed. The rate of release from the PNIPAM-co-allylamine network was temperature-dependent, being much faster at room temperature than that at human body temperature. In contrast, release of low molecular weight dextrans from the PNIPAM-co-AA network showed a temperature-independent release profile. These nanoparticle networks have several advantages over conventional bulk gels for controlling the release of high molecular weight biomolecules.

[1]  N. Brandon,et al.  GABAA-receptor-associated protein links GABAA receptors and the cytoskeleton , 1999, Nature.

[2]  Russell J. Stewart,et al.  Hybrid hydrogels assembled from synthetic polymers and coiled-coil protein domains , 1999, Nature.

[3]  Teruo Okano,et al.  Thermally on-off switching polymers for drug permeation and release , 1990 .

[4]  J. Feijen,et al.  Heparin release from thermosensitive hydrogels , 1992 .

[5]  Ronald A. Siegel,et al.  pH-Dependent Equilibrium Swelling Properties of Hydrophobic Polyelectrolyte Copolymer Gels , 1988 .

[6]  Robert Pelton,et al.  Preparation of aqueous latices with N-isopropylacrylamide , 1986 .

[7]  N A Peppas,et al.  New challenges in biomaterials. , 1994, Science.

[8]  Jun Gao,et al.  Polymer Gel Nanoparticle Networks , 2000 .

[9]  B. Chu,et al.  Laser Light Scattering , 1974 .

[10]  Allan S. Hoffman,et al.  Applications of thermally reversible polymers and hydrogels in therapeutics and diagnostics , 1987 .

[11]  Toyoichi Tanaka,et al.  Volume‐phase transitions of ionized N‐isopropylacrylamide gels , 1987 .

[12]  Spinodal decomposition in N‐isopropylacrylamide gel , 2001 .

[13]  T. Okano,et al.  Swelling controlled zero order and sigmoidal drug release from thermo-responsive poly(N-isopropylacrylamide-co-butyl methacrylate) hydrogel. , 1993, Journal of biomaterials science. Polymer edition.

[14]  Zhibing Hu,et al.  Polymer gels with engineered environmentally responsive surface patterns , 1998, Nature.

[15]  T. Okano,et al.  “On–Off” Thermocontrol of Solute Transport. I. Temperature Dependence of Swelling of N-Isopropylacrylamide Networks Modified with Hydrophobic Components in Water , 1991, Pharmaceutical Research.

[16]  Y. Osada,et al.  A polymer gel with electrically driven motility , 1992, Nature.

[17]  T. Okano,et al.  “On–Off“ Thermocontrol of Solute Transport. II. Solute Release from Thermosensitive Hydrogels , 1991, Pharmaceutical Research.

[18]  Zhibing Hu,et al.  Synthesis and Application of Modulated Polymer Gels , 1995, Science.

[19]  Kinam Park,et al.  Environment-sensitive hydrogels for drug delivery , 2001 .

[20]  Toyoichi Tanaka.  Collapse of Gels and the Critical Endpoint , 1978 .

[21]  Jun Gao,et al.  Optical Properties of N-Isopropylacrylamide Microgel Spheres in Water , 2002 .