Study of tribological performance of ECR-CVD diamond-like carbon coatings on steel substrates : Part 2. The analysis of wear mechanism

Abstract This paper describes the tribological performance of diamond-like carbon (DLC) coatings deposited on AISI 440C steel substrates by electron cyclotron resonance chemical vapor deposition (ECR–CVD) process. A variety of analytic techniques were used to characterize the coatings, such as Raman spectroscopy, atomic force microscopy (AFM) and nano-indentation. The sliding wear and friction experiments were carried out by the conventional ball-on-disk tribometry against 100Cr6 steel counterbody at various normal loads (1–10 N) and sliding speeds (2–15 cm/s). All the wear tests were conducted under dry sliding condition in ambient air for a total rotation cycle of 1 × 10 5 (sliding distance ∼2.2 km). Surfaces of the coatings and the steel balls were examined before and after the sliding wear tests. The DLC coatings that had been tested all showed relatively low values of friction coefficient, in the range of 0.1–0.2 at a steady-state stage, and low specific wear rates (on the order of 10 −8  mm 3 /Nm). It was found that higher normal loads or sliding speeds reduced the wear rates of the coatings. Plastic deformation became more evident on the coating surface during the sliding wear test at higher contact stresses. The friction-induced transformation of the coating surface into a graphite-like phase was revealed by micro-Raman analysis, and the flash temperature of the contact asperities was estimated. It was suggested that the structural transformation taking place within the wear tracks was mainly due to the formation of compact wear debris layer rather than the frictional heating effect. On the other hand, an adherent transfer layer (tribolayer) was formed on the counterface, which was closely related to the steady-state friction during sliding and the wear mechanisms. Fundamental knowledge combined with the present tribological study led to the conclusion that adhesive wear along with abrasion was probably the dominant wear mechanism for the DLC/steel sliding systems. Additionally, fatigue processes might also be involved in the wear of the coatings.

[1]  J. Ahn,et al.  Control of ion energy using a screen-grid in an electron cyclotron resonance chemical vapour deposition system , 1999 .

[2]  P. A. Willermet,et al.  Amorphous hydrogenated carbon films for tribological applications I. Development of moisture insensitive films having reduced compressive stress , 1997 .

[3]  A. Tanaka,et al.  The tribological characteristics of diamond-like carbon films at elevated temperatures , 1999 .

[4]  Ali Erdemir,et al.  A study of the wear mechanism of diamond-like carbon films , 1996 .

[5]  G. Fenske,et al.  Characterization of transfer layers forming on surfaces sliding against diamond-like carbon☆ , 1996 .

[6]  G. Berg,et al.  Evaluation of PVD nitride coatings, using impact, scratch and Rockwell-C adhesion tests , 1995 .

[7]  B. Bein,et al.  Photothermal characterization of amorphous thin films , 1999 .

[8]  G. Fenske,et al.  Effect of source gas and deposition method on friction and wear performance of diamondlike carbon films , 1997 .

[9]  George R. Fenske,et al.  Synthesis of diamondlike carbon films with superlow friction and wear properties , 2000 .

[10]  A. Grill,et al.  Friction control of diamond-like carbon coatings , 1997 .

[11]  Y. Lifshitz.  Diamond-like carbon — present status , 1999 .

[12]  C. Ai,et al.  Correlation between three-body wear and tribological characteristics of titanium nitride, titanium carbonitride and titanium carbide coatings , 1997 .

[13]  Verein Deutscher Eisenhüttenleute.  Steel : a handbook for materials research and engineering , 1992 .

[14]  J. Jiang,et al.  On the running-in behaviour of diamond-like carbon coatings under the ball-on-disk contact geometry , 1998 .

[15]  B. Tay,et al.  Tribological behaviour of different diamond-like carbon materials , 1998 .

[16]  J. Tong,et al.  An investigation into the tribological behaviour of DLC coatings deposited on sintered ferrous alloy substrate , 1998 .

[17]  P. Andry,et al.  Comparison of diamond-like carbon film deposition by electron cyclotron resonance with benzene and methane , 1996 .

[18]  K. Enke.  Dry machining and increase of endurance of machine parts with improved doped DLC coatings on steel, ceramics and aluminium , 1999 .

[19]  T. L. Huu,et al.  Transformation of sp3 to sp2 sites of diamond like carbon coatings during friction in vacuum and under water vapour environment , 1996 .

[20]  Jin Tong,et al.  Some special tribological features of DLC coatings deposited on soft substrates , 1997 .

[21]  S. Chizhik,et al.  Application of phase contrast imaging atomic force microscopy to tribofilms on DLC coatings , 2001 .

[22]  C. V. Cooper,et al.  Deposition and mechanical property evaluation of amorphous silicon-containing diamond-like carbon (Si-DLC) coatings on steel , 1996 .

[23]  G. Turban,et al.  Effect of negative bias voltage on a-C:H films deposited in electron cyclotron resonance plasma , 1997 .

[24]  G. Fenske,et al.  Effect of source gas chemistry on tribological performance of diamond-like carbon films. , 1999 .

[25]  T. L. Huu,et al.  Influence of defects and morphology of diamond-like carbon coatings on their tribological behaviour , 1995 .

[26]  Shui-Tong Lee,et al.  Mechanical and tribological properties of diamond-like carbon films prepared on steel by ECR-CVD process , 2001 .

[27]  Rusli,et al.  Effect of pressure on the deposition of hydrogenated amorphous carbon films using the electron cyclotron resonance chemical vapor deposition , 1998 .

[28]  J. Jiang,et al.  The effect of sliding speed on wear of diamond-like carbon coatings , 1998 .

[29]  Yong Sun,et al.  Surface engineering design: modelling surface engineering systems for improved tribological performance , 1998 .

[30]  Andrew Wells Phelps,et al.  Friction induced phase transformation of pulsed laser deposited diamond-like carbon , 1996 .

[31]  M. Hon,et al.  Thermal stability of diamond-like carbon films with added silicon , 1999 .

[32]  H. Ren,et al.  A combined MW/ECR-PACVD apparatus for the deposition of diamond and other hard coatings , 1995 .

[33]  Y. Liu,et al.  Influence of environmental parameters on the frictional behavior of DLC coatings , 1997 .

[34]  Efstathios I. Meletis,et al.  Tribological behavior of DLC coatings with functionally gradient interfaces , 2002 .

[35]  Yan Liu,et al.  Evidence of graphitization of diamond-like carbon films during sliding wear , 1997 .

[36]  H. Fecht,et al.  SPECIFIC HEAT OF SINGLE-, POLY- AND NANOCRYSTALLINE DIAMOND , 1998 .

[37]  W. Meng,et al.  Tribology of metal-containing diamond-like carbon coatings , 1997 .

[38]  A. Anttila,et al.  Tribological characteristics of diamond-like films deposited with an arc-discharge method , 1990 .

[39]  A. Grill,et al.  Tribological and mechanical properties of diamond-like carbon prepared by high-density plasma , 2001 .

[40]  G. Turban,et al.  Mechanical and tribological properties of diamond-like carbon coatings films deposited from an electron cyclotron resonance plasma , 1999 .

[41]  Rusli,et al.  INFLUENCE OF PROCESS PRESSURE ON THE GROWTH OF HYDROCARBON FILMS UNDER DIRECT DC BIAS IN AN ELECTRON CYCLOTRON RESONANCE PLASMA , 1998 .

[42]  A. Grill.  Tribology of diamondlike carbon and related materials: an updated review , 1997 .

[43]  J. Tong,et al.  The effect of substrate properties on tribological behaviour of composite DLC coatings , 1997 .

[44]  H. White,et al.  Low‐Temperature Synthesis of Diamond‐like Carbon Films on Steel Substrates by Electron‐Cyclotron‐Resonance Plasma‐Enhanced Chemical Vapor Deposition , 2005 .

[45]  Y. Liu,et al.  An investigation of the relationship between graphitization and frictional behavior of DLC coatings , 1996 .

[46]  Shui-Tong Lee,et al.  Effect of nitrogen incorporation into diamond-like carbon films by ECR-CVD , 1999 .

[47]  Ali Erdemir,et al.  The role of hydrogen in tribological properties of diamond-like carbon films☆ , 2001 .

[48]  E. Yoon,et al.  Tribological behavior of sliding diamond-like carbon films under various environments , 1998 .

[49]  R. D. Arnell,et al.  The effect of substrate surface roughness on the wear of DLC coatings , 2000 .

[50]  P. Psyllaki,et al.  Pin-on-disc testing of PE-CVD diamond-like carbon coatings on tool steel substrates , 2000 .

[51]  J. Ahn,et al.  The effects of self-generated DC bias on the characteristics of diamond-like carbon films prepared using ECR-CVD , 1998 .

[52]  H. Ronkainen,et al.  Characterization of wear surfaces in dry sliding of steel and alumina on hydrogenated and hydrogen-free carbon films , 1994 .

[53]  G. Turban,et al.  Hydrogen stability in diamond-like carbon films during wear tests , 1999 .

[54]  W. Kulisch,et al.  Mechanisms in ion-assisted deposition of superhard coatings: cubic boron nitride–tetrahedral amorphous carbon , 1997 .

[55]  M. Tamor,et al.  Raman ``fingerprinting'' of amorphous carbon films , 1994 .

[56]  T. J. Tsai,et al.  A study of the wear behavior of diamond-like carbon films under the dry reciprocating sliding contact , 2001 .

[57]  C. Donnet.  Recent progress on the tribology of doped diamond-like and carbon alloy coatings: a review , 1998 .

[58]  A. Grill.  Diamond-like carbon: state of the art , 1999 .

[59]  Dae-Eun Kim,et al.  Optimum film thickness of thin metallic coatings on silicon substrates for low load sliding applications , 1996 .

[60]  A. Tanaka,et al.  Influence of sliding mating materials on the tribological behavior of diamond-like carbon films , 1999 .

[61]  S. T. Lee,et al.  Deposition and properties of a-C:H films on polymethyl methacrylate by electron cyclotron resonance microwave plasma chemical vapor deposition method , 2000 .

[62]  Shui-Tong Lee,et al.  Characterization and optical properties of diamondlike carbon prepared by electron cyclotron resonance plasma , 1999 .

[63]  E. N. Loubnin,et al.  Tribological behaviour of smooth diamond films , 1995 .

[64]  Jože Flašker,et al.  Numerical simulation of surface pitting due to contact loading , 2001 .

[65]  M. Hon,et al.  Growth characterization and properties of diamond-like carbon films by electron cyclotron resonance chemical vapor deposition , 2001 .