Hydrophobic Recovery of Polydimethylsiloxane Elastomer Exposed to Partial Electrical Discharge

The hydrophobic recovery of polydimethylsiloxane elastomers was studied after exposure to partial electrical discharge. Silicone elastomers that were thoroughly extracted of free oligomeric impurities as well as those deliberately contaminated with low molecular weight (LMW) silicone fluids were used for these studies. Contact angle and X-ray photoelectron spectroscopy revealed that the recovery rates of the oxidized extracted samples are strongly influenced by the applied voltage, humidity, and aging condition. The recovery rates increase considerably as the applied voltage and the humidity during discharge increase. Remarkably, the oxidized samples stored under high vacuum (10 i7 Torr) exhibit lower recovery rates than those aged in air. Free silicone fluid, when added to the elastomer, affects the recovery rate as well; however, significant recovery is seen even without any added fluid. These results imply that the LMW species that are formed in situ during electrical discharge are sufficient to cause the hydrophobic recovery of oxidized PDMS elastomers. C ∞ 2000 Academic Press

[1]  R. Hackam,et al.  Suppression mechanism of leakage current on RTV coated porcelain and silicone rubber insulators , 1991 .

[2]  Patrick J. Smith,et al.  Plasma treatment of polydimethylsiloxane , 1994 .

[3]  M. Strobel,et al.  Aging of air-corona-treated polypropylene film , 1991 .

[4]  M. Strobel,et al.  Low-molecular-weight materials on corona-treated polypropylene , 1989 .

[5]  Ernesto Occhiello,et al.  On the aging of oxygen plasma-treated polydimethylsiloxane surfaces , 1990 .

[6]  Ulf W. Gedde,et al.  Hydrophobicity Recovery of Polydimethylsiloxane after Exposure to Corona Discharges , 1998 .

[7]  A quantitative model for the surface restructuring of repeatedly plasma treated silicone rubber , 1997 .

[8]  W. Feast,et al.  Investigation of the ageing of plasma oxidized PEEK , 1991 .

[9]  A. E. Vlastos,et al.  Surface structural changes of naturally aged silicone and EPDM composite insulators , 1991 .

[10]  J. Andrade.  Surface and Interfacial Aspects of Biomedical Polymers , 1985 .

[11]  J. Newton,et al.  Surface modification of a contact lens co‐polymer by plasma‐discharge treatments , 1987 .

[12]  Chi Ming Chan,et al.  Polymer surface modification and characterization , 1993 .

[13]  M. Urban,et al.  DMA and ATR FT‐IR studies of gas plasma modified silicone elastomer surfaces , 1990 .

[14]  George G. Karady,et al.  Aging in silicone rubber used for outdoor insulation , 1992 .

[15]  M. Chaudhury,et al.  Estimation of Adhesion Hysteresis at Polymer/Oxide Interfaces Using Rolling Contact Mechanics , 1998 .

[16]  Robert H. Reamey,et al.  Reconstruction of the interface of oxidatively functionalized polyethylene and derivatives on heating , 1987 .

[17]  D. Briggs,et al.  Surface modification of poly(ethylene terephthalate) by electrical discharge treatment , 1980 .

[19]  T. Gengenbach,et al.  Quantitative Analysis of Polymer Surface Restructuring , 1995 .

[20]  I. Bertóti,et al.  Oxidative damage and recovery of silicone rubber surfaces. I. X‐ray photoelectron spectroscopic study , 1994 .