Delamination buckling: A finite element study with realistic delamination shapes, multiple delaminations and fibre fracture cracks

This paper presents a finite element model of a carbon fibre composite laminate with multiple delaminations of realistic shape and including fibre fracture cracks loaded under compression. The modelling technique is initially applied on circular and elliptical delaminations of single ply sublaminates, which are compared with existing analytical solutions. The techniques are then applied to models with multiple delaminations of realistic shape and their behaviour in buckling and post-buckling is captured. An inverse method is used to determine the stiffness reduction caused by the damage, and shows significant stiffness reduction caused by peanut shaped delaminations. When fibre fracture cracks are added, their contribution to further stiffness reduction is minimal but they have some significant effects on the buckling shapes.

[1]  Finite element study of compressively loaded fibres fractured during impact , 2009 .

[2]  John D. Whitcomb,et al.  Buckling of a Sublaminate in a Quasi-Isotropic Composite Laminate , 1985 .

[3]  R. Olsson,et al.  Nonlinear compressive stiffness in impacted composite laminates determined by an inverse method , 2009 .

[4]  John D. Whitcomb,et al.  Analysis of a Laminate with a Postbuckled Embedded Delamination, Including Contact Effects , 1992 .

[5]  Aniello Riccio,et al.  Modeling Damage Propagation in Composite Plates with Embedded Delamination under Compressive Load , 2008 .

[6]  Hiroshi Suemasu,et al.  Effects of Multiple Delaminations on Compressive Buckling Behaviors of Composite Panels , 1993 .

[7]  Z. Gürdal,et al.  BUCKLING AND POSTBUCKLING OF CIRCULAR PLATES CONTAINING CONCENTRIC PENNY-SHAPED DELAMINATIONS , 1995 .

[8]  John D. Whitcomb,et al.  Strain-Energy Release Rate Analysis of Plates with Postbuckled Delaminations , 1989 .

[9]  Guoqiang Li,et al.  Local buckling analysis of composite laminate with large delaminations induced by low velocity impact , 1999 .

[10]  Leif Asp,et al.  An experimental investigation of the influence of delamination growth on the residual strength of impacted laminates , 2001 .

[11]  T. S. Ramamurthy,et al.  Estimation of impact-induced damage in CFRP laminates through ultrasonic imaging , 1998 .

[12]  Hiroshi Suemasu,et al.  Postbuckling Behaviors of Composite Panels with Multiple Delaminations , 1993 .

[13]  M. Pavier,et al.  Finite element prediction of the post-impact compressive strength of fibre composites , 1996 .

[14]  Silvestre T. Pinho,et al.  Material and structural response of polymer-matrix fibre-reinforced composites: Part B , 2012 .

[15]  Hiroshi Suemasu,et al.  Compressive behavior of multiply delaminated composite laminates. Part 2 : Finite element analysis , 1998 .

[16]  R. Olsson,et al.  Investigation of Impact Damage in Multi-Directional Tape Laminates and its Effect on Local Tensile Stiffness , 2008 .

[17]  Hiroshi Suemasu,et al.  Compressive Behavior of Multiply Delaminated Composite Laminates Part 1: Experiment and Analytical Development , 1998 .

[18]  W. Yin.  The Effects of Laminated Structure on Delamination Buckling and Growth , 1988 .

[19]  C. D. Babcock,et al.  Two-Dimensional Modelling of Compressive Failure in Delaminated Laminates , 1985 .

[20]  S. Abrate.  Impact on Laminated Composite Materials , 1991 .

[21]  Robin Olsson,et al.  Impact on composite structures , 2004, The Aeronautical Journal (1968).

[22]  Janis Varna,et al.  Experimental determination of elastic properties of impact damage in carbon fibre/epoxy laminates , 2001 .

[23]  Artificial damage techniques for low velocity impact in carbon fibre composites , 1993 .

[24]  Robin Olsson,et al.  Tensile stiffness distribution in impacted composite laminates determined by an inverse method , 2008 .

[25]  B. Davidson.  Delamination Buckling: Theory and Experiment , 1991 .

[26]  Dahsin Liu,et al.  Impact-Induced Delamination—A View of Bending Stiffness Mismatching , 1988 .

[27]  D. Guedra-Degeorges.  Recent advances to assess mono- and multi-delaminations behaviour of aerospace composites , 2006 .