Morphology and mechanisms of formation of natural patinas on archaeological Cu–Sn alloys

Abstract Natural patinas on archaeological bronzes (Cu–Sn alloys) have been classified and characterized in order to get a deeper insight into their formation mechanisms. From examinations of cross-sections on archaeological artefacts, two classes of corrosion structures were defined (Type I and Type II), using both optical and electron microscopies, EDSX, XRD, IRS and a statistical treatment of data (Principal Components Analysis). A Type I structure (even surface) is defined as a two-layer passivating deposit due to an internal oxidation with a decuprification process (i.e. selective dissolution of copper). A Type II structure (coarse surface) corresponds to more severe attacks, such as pitting but also general uneven corrosion; it is modelled by a three-layer structure, characterized by the presence of cuprous oxide and by an increase in the chloride content at the internal layer/alloy interface related with selective dissolution of copper. A phenomenological model to explain the formation of bronze patinas is developed on the basis of a decuprification phenomenon.

[1]  R. Garrels,et al.  Solutions, Minerals and Equilibria , 1965 .

[2]  L. G. Blackwood.  Factor Analysis in Chemistry (2nd Ed.) , 1994 .

[3]  W. Oddy,et al.  Unusual phenomena in the corrosion of ancient bronzes , 1982 .

[4]  D. T. Hawkins.  THE RESTORATION OF METAL MONUMENTS: A BIBLIOGRAPHY, 1933-1986 , 1987 .

[5]  M. Urquidi-Macdonald,et al.  Theory of Steady‐State Passive Films , 1990 .

[6]  V. F. Lucey,et al.  Developments Leading to the Present Understanding of the Mechanism of Pitting Corrosion of Copper , 1972 .

[7]  T. Weisser.  THE DE-ALLOYING OF COPPER ALLOYS , 1975 .

[8]  R. F. Tylecote,et al.  The effect of soil conditions on the long-term corrosion of buried tin-bronzes and copper , 1979 .

[9]  N. Tennent,et al.  Bronze disease: synthesis and characterisation of botallackite, paratacamite and atacamite by infra-red spectroscopy , 1981 .

[10]  W. Geilmann,et al.  Verwitterung von Bronzen im Sandboden. Ein Beitrag zur Korrosionsforschung , 1956 .

[11]  J. P. Franey,et al.  On the corrosion resistance of certain ancient chinese bronze artifacts , 1983 .

[12]  S. J. Fleming,et al.  Recent applications of PIXE spectrometry in archaeology I. Characterization of bronzes with special consideration of the influence of corrosion processes on data reliability , 1992 .

[13]  D. Macdonald.  The Point Defect Model for the Passive State , 1992 .

[14]  N. Meeks.  Surface studies of Roman bronze mirrors, comparative high-tin bronze Dark Age material and black Chinese mirrors , 1988 .

[15]  S. Turgoose,et al.  The Corrosion of lead and tin: before and after excavation , 1985 .

[16]  H. Fischmeister,et al.  The passivity of iron-chromium alloys , 1989 .

[17]  L. Shreir.  1.6 – Localised Corrosion , 1976 .

[18]  Melvin Romanoff,et al.  Circular of the Bureau of Standards no. 579:: underground corrosion , 1957 .

[19]  Daniel Hanson,et al.  Chill-Cast Tin Bronzes , 1951 .

[20]  T. Stambolov,et al.  The Corrosion and Conservation of Metallic Antiquities and Works of Art , 1987 .

[21]  N. Meeks.  TIN‐RICH SURFACES ON BRONZE–SOME EXPERIMENTAL AND ARCHAEOLOGICAL CONSIDERATIONS , 1986 .

[22]  R. J. Gettens.  MINERAL ALTERATION PRODUCTS ON ANCIENT METAL OBJECTS , 1961 .

[23]  Richard I. Macphail,et al.  Soils and Micromorphology in Archaeology , 1990 .

[24]  R. Taylor,et al.  Corrosion of Bronzes on Shipwrecks , 1985 .

[25]  Rutherford J. Gettens,et al.  The corrosion products of an ancient Chinese bronze , 1951 .