Plastic dye-sensitized photo-supercapacitor using electrophoretic deposition and compression methods

Abstract A plastic photo-rechargeable capacitor is studied using a three-electrode configuration, separating a flexible dye-sensitized solar cell (DSSC) and a supercapacitor by sharing a common Pt electrode. The thick and uniform TiO2 film is formed by using commercially available TiO2 nanocrystals, which are treated in an isopropyl alcohol without surfactant by the electrophoretic deposition (EPD) to deposit the mesoporous TiO2 photoanode film with good adherence onto the plastic substrate. Afterward, a static mechanical compression technique as the post-treatment is employed to the electrophoretic deposited film in order to enhance the particles connection. In addition, a supercapacitor using PEDOT (poly(3,4-ethylenedioxythiophene)), which is potentiostatically electropolymerized to form a thick film, is fabricated to store the energy. The flexible DSSC part is fabricated with a TiO2 film of 10.9 μm thickness and it can provide photoelectric conversion efficiency up to 4.37% under 1 sun illumination. The photocapacitor is made with such a flexible DSSC and a supercapacitor with ca. 0.5 mm thick PEDOT film, which provides a specific capacitance of 0.52 F cm−2.

[1]  Hasitha C. Weerasinghe,et al.  Fabrication of efficient solar cells on plastic substrates using binder-free ball milled titania slurries , 2009 .

[2]  Anders Hagfeldt,et al.  Optimization of dye-sensitized solar cells prepared by compression method , 2002 .

[3]  Takehito Mitate,et al.  Modeling of an equivalent circuit for dye-sensitized solar cells , 2004 .

[4]  Tsutomu Miyasaka,et al.  A high-voltage dye-sensitized photocapacitor of a three-electrode system. , 2005, Chemical communications.

[5]  Guido Viscardi,et al.  Combined experimental and DFT-TDDFT computational study of photoelectrochemical cell ruthenium sensitizers. , 2005, Journal of the American Chemical Society.

[6]  Kurt D. Benkstein,et al.  Relation between Particle Coordination Number and Porosity in Nanoparticle Films: Implications to Dye-Sensitized Solar Cells , 2001 .

[7]  Michael Grätzel,et al.  Investigation of Sensitizer Adsorption and the Influence of Protons on Current and Voltage of a Dye-Sensitized Nanocrystalline TiO2 Solar Cell , 2003 .

[8]  Kuo-Chuan Ho,et al.  EIS analysis on low temperature fabrication of TiO2 porous films for dye-sensitized solar cells , 2008 .

[9]  Anders Hagfeldt,et al.  A new method to make dye-sensitized nanocrystalline solar cells at room temperature , 2001 .

[10]  Tsutomu Miyasaka,et al.  The photocapacitor: An efficient self-charging capacitor for direct storage of solar energy , 2004 .

[11]  Man Gu Kang,et al.  Chemical Sintering of Nanoparticles: A Methodology for Low‐Temperature Fabrication of Dye‐Sensitized TiO2 Films , 2005 .

[12]  Aurelien Du Pasquier,et al.  Aqueous coating of efficient flexible TiO2 dye solar cell photoanodes , 2009 .

[13]  Tsutomu Miyasaka,et al.  Low-Temperature Fabrication of Dye-Sensitized Plastic Electrodes by Electrophoretic Preparation of Mesoporous TiO2 Layers , 2004 .

[14]  Michael Dürr,et al.  Low-temperature fabrication of dye-sensitized solar cells by transfer of composite porous layers , 2005, Nature materials.

[15]  Tsutomu Miyasaka,et al.  Highly Efficient Plastic Dye-sensitized Photoelectrodes Prepared by Low-temperature Binder-free Coating of Mesoscopic Titania Pastes , 2007 .

[16]  Glenn Amatucci,et al.  Characteristics and performance of 500 F asymmetric hybrid advanced supercapacitor prototypes , 2003 .

[17]  Yuan Wang,et al.  Enhance the optical absorptivity of nanocrystalline TiO2 film with high molar extinction coefficient ruthenium sensitizers for high performance dye-sensitized solar cells. , 2008, Journal of the American Chemical Society.

[18]  K. Sumathy,et al.  An analytical study of the porosity effect on dye-sensitized solar cell performance , 2006 .

[19]  Larissa Grinis,et al.  Influence of sintering temperature, pressing, and conformal coatings on electron diffusion in electrophoretically deposited porous TiO2 , 2006 .

[20]  Ashraful Islam,et al.  Modeling of an equivalent circuit for dye-sensitized solar cells : improvement of efficiency of dye-sensitized solar cells by reducing internal resistance , 2006 .

[21]  Y. Sung,et al.  Electrophoretically deposited TiO2 photo-electrodes for use in flexible dye-sensitized solar cells , 2005 .

[22]  Tsutomu Miyasaka,et al.  Photovoltaic Performance of Plastic Dye-Sensitized Electrodes Prepared by Low-Temperature Binder-Free Coating of Mesoscopic Titania , 2007 .

[23]  Michael Grätzel,et al.  Conversion of sunlight to electric power by nanocrystalline dye-sensitized solar cells , 2004 .

[24]  A. Zaban,et al.  Electrophoretic deposition and compression of titania nanoparticle films for dye-sensitized solar cells , 2008 .

[25]  S. Uchida,et al.  Preparation of TiO2 nanocrystalline electrode for dye-sensitized solar cells by 28 GHz microwave irradiation , 2004 .

[26]  L. Carlos,et al.  A simple route towards low-temperature processing of nanoporous thin films using UV-irradiation: Application for dye solar cells , 2009 .

[27]  Michael Grätzel,et al.  Low cost photovoltaic modules based on dye sensitized nanocrystalline titanium dioxide and carbon powder , 1996 .

[28]  H. Arakawa,et al.  Highly efficient plastic substrate dye-sensitized solar cells using a compression method for preparation of TiO(2) photoelectrodes. , 2007, Chemical communications.

[29]  N. Mermilliod,et al.  Capacitive Charge and Noncapacitive Charge in Conducting Polymer Electrodes , 1987 .

[30]  Anders Hagfeldt,et al.  A New Method for Manufacturing Nanostructured Electrodes on Plastic Substrates , 2001 .

[31]  Derek J. Fray,et al.  Achieving high electrode specific capacitance with materials of low mass specific capacitance : Potentiostatically grown thick micro-nanoporous PEDOT films , 2007 .