저온하에서 레일강의 피로균열진전거동

Among rail defects, the transverse crack, which has been the most dangerous fatigue damage, is developed from shelling near the rail running face and grows perpendicular to the rail surface. Moreover, the crack has occurred frequently fatigue damage during winter. Therefore, to assure the safety of railway vehicles, it is necessary to investigate growth behavior of transverse crack for rail steel. In this study, fatigue crack growth behavior of rail steel and its gas pressure welded part at room and low temperature are performed. The fatigue crack growth rate of the welded part was lower than that of the base part within a lower ?K region at both room and low temperature, and this difference decreases with increasing the ?K due to the decrease of the fracture toughness.