Temperature-sensitive PVA/PNIPAAm semi-IPN hydrogels with enhanced responsive properties.

A series of temperature-sensitive hydrogels of semi-interpenetrating polymeric networks (semi-IPN) composed of poly(N-isopropylacrylamide) (PNIPAAm) and poly(vinyl alcohol) (PVA) were prepared by radical polymerization. The PNIPAAm networks were cross-linked by N,N'-methylenebisacrylamide in the presence of linear PVA. The reaction processes were investigated by rheometry using oscillatory deformation tests. It was found that gelations were very fast and the modulus reached equilibrium within about 12.5min. The prepared semi-IPN hydrogels were characterized for their morphologies and thermal behaviors by scanning electron microscopy and differential scanning calorimetry, respectively. The interior network structures of the semi-IPN matrix became more porous with increasing PVA. In comparison to the conventional PNIPAAm gel, the newly reported semi-IPN hydrogels exhibited the same lower critical solution temperature. Their swelling properties, such as temperature dependence of equilibrium swelling ratio, shrinking kinetics and reswelling kinetics in water, were also studied. Experimental data indicated that the shrinking and reswelling rates of the semi-IPN hydrogels were much faster than those of the conventional PNIPAAm hydrogels. With this novel approach, water absorption and response properties could be adjusted by tuning the feed ratio of NIPAAm and PVA. These fast responsive hydrogels exhibited improved temperature sensitivity and swelling properties compared to the conventional PNIPAAm hydrogel, which would be critical and desirable for a gel to find potential applications in biomedical fields, such as drug delivery systems and sensors.

[1]  R. Zhuo,et al.  Temperature sensitive poly[N-isopropylacrylamide-co-(acryloyl beta-cyclodextrin)] for improved drug release. , 2005, Macromolecular bioscience.

[2]  J. Feijen,et al.  Mutual influence of pH and temperature on the swelling of ionizable and thermosensitive hydrogels , 1992 .

[3]  Oscar Chiantore,et al.  Solution properties of poly(N‐isopropylacrylamide) , 1979 .

[4]  Yi Yan Yang,et al.  Preparation and characterization of fast response macroporous poly(N-isopropylacrylamide) hydrogels , 2001 .

[5]  R. Zhuo,et al.  Poly(vinyl alcohol)/poly(N-isopropylacrylamide) semi-interpenetrating polymer network hydrogels with rapid response to temperature changes , 2003 .

[6]  A. F. Rubira,et al.  Thermo-sensitive hydrogels membranes from PAAm networks and entangled PNIPAAm: effect of temperature, cross-linking and PNIPAAm contents on the water uptake and permeability , 2004 .

[7]  R. Zhuo,et al.  Poly(N‐isopropylacrylamide) Nanoparticle‐Incorporated PNIPAAm Hydrogels with Fast Shrinking Kinetics , 2005 .

[8]  K. Jandt,et al.  A Novel Approach to Prepare Porous Poly(N‐isopropylacrylamide) Hydrogel with Superfast Shrinking Kinetics , 2008 .

[9]  Takashi Miyata,et al.  A reversibly antigen-responsive hydrogel , 1999, Nature.

[10]  R. Zhuo,et al.  Macroporous poly(N-isopropylacrylamide) hydrogels with fast response rates and improved protein release properties. , 2003, Journal of biomedical materials research. Part A.

[11]  E. Ruckenstein,et al.  Pervaporation of ethanol-water mixtures through polyvinyl alcohol-polyacrylamide interpenetrating polymer network membranes unsupported and supported on polyethersulfone ultrafiltration membranes: a comparison , 1996 .

[12]  M. Shibayama,et al.  Kinetics of Volume Phase Transition in Poly(N-isopropylacrylamide-co-acrylic acid) Gels , 1998 .

[13]  Toyoichi Tanaka,et al.  Kinetics of discontinuous volume-phase transition of gels , 1988 .

[14]  R. Zhuo,et al.  Preparation and properties of poly(N-isopropylacrylamide)/poly(N-isopropylacrylamide) interpenetrating polymer networks for drug delivery , 2004 .

[15]  N. Satarkar,et al.  Hydrogel nanocomposites as remote-controlled biomaterials. , 2008, Acta biomaterialia.

[16]  Zhibing Hu,et al.  Phase behavior and stabilization of microgel arrays , 2007 .

[17]  Georges Geuskens,et al.  Compressive Elastic Modulus of Polyacrylamide Hydrogels and Semi-IPNs with Poly(N-isopropylacrylamide) , 2001 .

[18]  Kiyotaka Sakai,et al.  Rapid Deswelling Response of Poly(N-isopropylacrylamide) Hydrogels by the Formation of Water Release Channels Using Poly(ethylene oxide) Graft Chains , 1998 .

[19]  Nikolaos A. Peppas,et al.  Structure and Applications of Poly(vinyl alcohol) Hydrogels Produced by Conventional Crosslinking or by Freezing/Thawing Methods , 2000 .

[20]  M. Shibayama,et al.  Shrinking Kinetics of Poly(N-isopropylacrylamide) Gels T-Jumped across Their Volume Phase Transition Temperatures , 1999 .

[21]  J. Wong,et al.  Rheological Monitoring of Polyacrylamide Gelation: Importance of Cross-Link Density and Temperature , 2004 .

[22]  Y. Hsieh,et al.  Dual temperature‐ and pH‐sensitive hydrogels from interpenetrating networks and copolymerization of N‐isopropylacrylamide and sodium acrylate , 2004 .

[23]  Xiao Huang,et al.  Biodegradable thermoresponsive hydrogels for aqueous encapsulation and controlled release of hydrophilic model drugs. , 2005, Biomacromolecules.

[24]  Seoung Gil Yoon,et al.  Electrical sensitive behavior of poly(vinyl alcohol)/poly (diallyldimethylammonium chloride) IPN hydrogel , 2003 .

[25]  T. Okano,et al.  Sigmoidal Swelling Profiles for Temperature-Responsive Poly(N-Isopropylacrylamide-Co-Butyl Methacrylate) Hydrogels , 1994 .

[26]  M. Márquez,et al.  Controlled release from and tissue response to physically bonded hydrogel nanoparticle assembly , 2005 .

[27]  R. Zhuo,et al.  Preparation of macroporous poly(N-isopropylacrylamide) hydrogel with improved temperature sensitivity , 2003 .

[28]  Jing Zhang,et al.  Synthesis and Characterization of pH- and Temperature-Sensitive Poly(methacrylic acid)/Poly(N-isopropylacrylamide) Interpenetrating Polymeric Networks , 2000 .

[29]  K. Otake,et al.  Thermal analysis of the volume phase transition with N-isopropylacrylamide gels , 1990 .

[30]  R. Zhuo,et al.  Temperature‐Sensitive Poly(N‐isopropylacrylamide) Hydrogels with Macroporous Structure and Fast Response Rate , 2003 .

[31]  Paul Yager,et al.  Synthesis and characterization of thermally reversible macroporous poly(N‐isopropylacrylamide) hydrogels , 1992 .

[32]  T. Okano,et al.  Thermo-sensitive polymers as on-off switches for drug release , 1987 .

[33]  Louise E. Smith,et al.  Examination of the effects of poly(N-vinylpyrrolidinone) hydrogels in direct and indirect contact with cells. , 2006, Biomaterials.

[34]  S. L. Wright,et al.  Drug diffusion and binding in ionizable interpenetrating networks from poly(vinyl alcohol) and poly(acrylic acid). , 1998, European journal of pharmaceutics and biopharmaceutics : official journal of Arbeitsgemeinschaft fur Pharmazeutische Verfahrenstechnik e.V.

[35]  Kinam Park,et al.  Smart Polymeric Gels: Redefining the Limits of Biomedical Devices. , 2007, Progress in polymer science.

[36]  S. Hirotsu,et al.  Kinetics of volume phase transition in poly(N-isopropylacrylamide) gels , 2002 .

[37]  K. Jandt,et al.  Mineralisation of chitosan scaffolds with nano-apatite formation by double diffusion technique. , 2006, Acta biomaterialia.

[38]  W. Oppermann,et al.  Polyacrylamide-clay nanocomposite hydrogels : Rheological and light scattering characterization , 2007 .

[39]  Yasuzo Sakai,et al.  Wide-Range Control of Deswelling Time for Thermosensitive Poly(N-isopropylacrylamide) Gel Treated by Freeze-Drying , 2003 .