Managing trace elements in Portland cement – Part I: Interactions between cement paste and heavy metals added during mixing as soluble salts

Abstract The aim of this work is to investigate the effect of the addition of Cu, Cd, Ni, Pb and Zn nitrate salts on the compressive strength of a CEM I Portland cement. Concentrations of 0.018 or 0.18 mol/kg of cement of each trace element were tested. After 2 days age, the compressive strength was reduced by various extents by addition of heavy metals, with the exception of Ni. This difference is due to a delay in tricalcium silicate hydration (C 3 S) as shown by an isothermal calorimetry test. Trace elements also influence the 28-days compressive strength, whereas the measured degree of hydration of these cement pastes is the same. As shown by scanning electron microscopy and X-ray diffraction, Cu and Pb are predominantly absorbed in the calcium silicate hydrate gel (C–S–H) while Cd, Ni and Zn are mainly precipitated as hydroxides within the intergranular porosity. Thus, trace elements precipitated as hydroxides have only a slight effect on the compressive strength. In contrast, Cu and Pb cause an increase in mechanical resistance by changing the C–S–H nanometric assembly and its density.

[1]  M. T. Blanco-Varela,et al.  Influencia de la adicin del BaCO 3 sobre la hidratacin del cemento portland , 1999 .

[2]  C. Tashiro,et al.  The effects of several heavy metal oxides on the formation of ettringite and the microstructure of hardened ettringite , 1979 .

[3]  Angel Irabien,et al.  Influence of lead, zinc, iron (III) and chromium (III) oxides on the setting time and strength development of Portland cement , 2001 .

[4]  N. Katyal,et al.  Influence of titania on the formation of tricalcium silicate , 1999 .

[5]  A. Marion,et al.  Study Of The Leaching Behaviour Of Paving Concretes: Quantification Of Heavy Metal Content In Leachates Issued From Tank Test Using Demineralized Water , 2005 .

[6]  N. Katyal,et al.  Effect of Cr2O3 on the formation of C3S in 3CaO :1SiO2 :xCr2O3 system , 2000 .

[7]  Christel Kupsch,et al.  Impact of the use of waste on trace element concentrations in cement and concrete , 2005, Waste management & research : the journal of the International Solid Wastes and Public Cleansing Association, ISWA.

[8]  N. Katyal,et al.  Effect of barium on the formation of tricalcium silicate , 1999 .

[9]  A. Roy,et al.  A study of the effects of nickel chloride and calcium chloride on hydration of portland cement , 1993 .

[10]  D. Knöfel,et al.  Influence of Cr, Ni, and Zn on the properties of pure clinker phases: Part II. C3A and C4AF , 1999 .

[11]  John H. Sharp,et al.  The chemical composition and microstructure of hydration products in blended cements , 2004 .

[12]  John H. Sharp,et al.  Retardation of cement hydration caused by heavy metals present in ISF slag used as aggregate , 2008 .

[13]  N. Labhasetwar,et al.  Ca2+ ⇌ Pb2+ exchange reaction of calcium silicate hydrate: Ca5Si6O18H2 · 4H2O , 1989 .

[14]  E. Moudilou.  Cinétiques et mécanismes de relargage des métaux lourds présents en traces dans les matrices cimentaires , 2002 .

[15]  F. Medici,et al.  Inertization of toxic metals in cement matrices: Effects on hydration, setting and hardening , 1995 .

[16]  F. Andrade,et al.  INCORPORATION OF V, ZN AND PB INTO THE CRYSTALLINE PHASES OF PORTLAND CLINKER , 2003 .

[17]  G. Kakali,et al.  Investigation of the effect of Zn oxide on the formation of Portland cement clinker , 1995 .

[18]  A. Bentur,et al.  Structural Properties of Calcium Silicate Pastes: II, Effect of Curing Temperature , 1979 .

[19]  D. Knöfel,et al.  High intakes of Cr, Ni, and Zn in clinker: Part II. Influence on the hydration properties , 1999 .

[20]  D. Knöfel,et al.  High intakes of Cr, Ni, and Zn in clinker: Part I. Influence on burning process and formation of phases , 1999 .

[21]  C. M. Sangha,et al.  Long-term leaching of toxic trace metals from Portland cement concrete , 1999 .

[22]  John H. Sharp,et al.  Effect of temperature on the hydration of the main clinker phases in portland cements: part ii, blended cements , 1998 .

[23]  M. Murat,et al.  Effect of large additions of Cd, Pb, Cr, Zn, to cement raw meal on the composition and the properties of the clinker and the cement , 1996 .

[24]  Rachel J. Detwiler,et al.  Reaction kinetics of portland cement mortars hydrated at different temperatures , 1992 .

[25]  P. West,et al.  Stabilization of Heavy Metals in Portland Cement Matrix: Effects on Paste Properties , 1996 .

[26]  Caijun Shi,et al.  Stabilization and Solidification of Hazardous, Radioactive, and Mixed Wastes , 2004 .

[27]  Yiying Jin,et al.  Comparison of the fixation of heavy metals in raw material, clinker and mortar using a BCR sequential extraction procedure and NEN7341 test , 2008 .

[28]  K. Kolovos,et al.  SEM examination of clinkers containing foreign elements , 2005 .

[29]  N. L. Thomas,et al.  The effect of lead nitrate on the early hydration of portland cement , 1981 .

[30]  Rachel J. Detwiler,et al.  Pore structure of plain cement pastes hydrated at different temperatures , 1990 .

[31]  D. Cocke,et al.  Solidification of hazardous substances‐a TGA and FTIR study of Portland cement containing metal nitrates , 1989 .

[32]  G. Kakali,et al.  A study on the grindability of portland cement clinker containing transition metal oxides , 1997 .

[33]  Roger Perry,et al.  Permeability study on the cement based solidification process for the disposal of hazardous wastes , 1986 .

[34]  Rachel J. Detwiler,et al.  DEVELOPMENT OF MICROSTRUCTURES IN PLAIN CEMENT PASTES HYDRATED AT DIFFERENT TEMPERATURES , 1991 .

[35]  A. Macías,et al.  Characterization of cement-stabilized Cd wastes , 1997 .

[36]  D. Knöfel,et al.  Influence of Cr, Ni, and Zn on the properties of pure clinker phases: Part I. C3S , 1999 .