Catalytic degradation of high density polyethylene over nanocrystalline HZSM-5 zeolite

Abstract High density polyethylene (HDPE) was catalytically degraded using a laboratory fluidised bed reactor in order to obtain high yield of gas fractions at mild temperatures, between 350 and 550 °C. The catalyst used was nanocrystalline HZSM-5 zeolite. High yields of butenes (25%) were found in the gas fractions, which were composed mainly of olefins. Waxes were wholly composed of linear and branched paraffins, with components between C 10 and C 20 . The effects of both temperature and polymer to catalyst ratio on the product yield were studied. Gas conversion was dramatically decreased when the operation temperature was low (below 450 °C) or when the polymer to catalyst ratio was greatly increased (9.2). Gas and wax compositions significantly altered over 500 °C, showing that a part of the HDPE was degraded thermally, increasing the olefin concentration in the waxes. The same variation was observed in the experiments carried out at high polymer to catalyst ratios, obtaining a 50% olefinic concentration in the waxes. The differences observed in product distributions can be attributed to both thermal and catalytic degradations.

[1]  Jerzy Walendziewski,et al.  Thermal and catalytic conversion of waste polyolefines , 2001 .

[2]  José M. Escola,et al.  Feedstock recycling of agriculture plastic film wastes by catalytic cracking , 2004 .

[3]  Longya Xu,et al.  Catalytic cracking of C4 alkenes to propene and ethene : Influences of zeolites pore structures and Si/Al2 ratios , 2005 .

[4]  Angela N. García,et al.  Study of the gases obtained in thermal and catalytic flash pyrolysis of HDPE in a fluidized bed reactor , 2005 .

[5]  P. Sharratt,et al.  Deactivation of US-Y zeolite by coke formation during the catalytic pyrolysis of high density polyethylene , 1997 .

[6]  Paul N. Sharratt,et al.  Production of hydrocarbons by catalytic degradation of high density polyethylene in a laboratory fluidised-bed reactor , 1998 .

[7]  Duckshin Park,et al.  Catalytic degradation of polyethylene over solid acid catalysts , 1999 .

[8]  Ulises Sedran,et al.  Conversion of waste plastics into fuels: Recycling polyethylene in FCC , 2002 .

[9]  G. Manos,et al.  Thermogravimetric study of polymer catalytic degradation over microporous materials , 2004 .

[10]  R. Van Grieken,et al.  Thermal and catalytic cracking of polyethylene under mild conditions , 2001 .

[11]  N. Viswanadham,et al.  Studies on acidity, activity and coke deactivation of ZSM-5 during n-heptane aromatization , 2001 .

[12]  Paul T. Williams,et al.  Catalytic pyrolysis of polyethylene , 2002 .

[13]  Dae-Hyun Shin,et al.  Investigation of catalytic degradation of high-density polyethylene by hydrocarbon group type analysis , 2003 .

[14]  J. M. Arandes,et al.  Effect of HZSM-5 Zeolite Addition to a Fluid Catalytic Cracking Catalyst. Study in a Laboratory Reactor Operating under Industrial Conditions , 2000 .

[15]  A. Garforth,et al.  Conversion of Polyethylene into Gasoline-Range Fuels by Two-Stage Catalytic Degradation Using Silica−Alumina and HZSM-5 Zeolite , 1999 .

[16]  J. M. Arandes,et al.  RECICLADO DE RESIDUOS PLÁSTICOS , 2004 .

[17]  N. P. Evmiridis,et al.  Performance of ZSM-5 as a Fluid Catalytic Cracking Catalyst Additive: Effect of the Total Number of Acid Sites and Particle Size , 1999 .

[18]  A. Al-Arfaj,et al.  Catalytic cracking of polyethylene over all-silica MCM-41 molecular sieve , 2002 .

[19]  Colomba Di Blasi,et al.  Transition between regimes in the degradation of thermoplastic polymers , 1999 .

[20]  Jong‐Ho Kim,et al.  The effect of pore shape on the catalytic performance of zeolites in the liquid-phase degradation of HDPE , 2002 .

[21]  Elias Klemm,et al.  Catalytic degradation of polyethylene using thermal gravimetric analysis and a cycled-spheres-reactor , 2001 .

[22]  Avelino Corma,et al.  The role of different types of acid site in the cracking of alkanes on zeolite catalysts , 1985 .

[23]  J. Ceamanos,et al.  Fluidized bed thermal degradation products of HDPE in an inert atmosphere and in air–nitrogen mixtures , 2003 .

[24]  V. Kazansky.  Adsorbed carbocations as transition states in heterogeneous acid catalyzed transformations of hydrocarbons , 1999 .

[25]  A. Holmen,et al.  Influence of Coke Deposition on Selectivity in Zeolite Catalysis , 1997 .

[26]  Juan A. Conesa,et al.  Catalyst addition in polyethylene pyrolysis , 2001 .

[27]  László Bartha,et al.  Thermal and thermo-catalytic degradation of high-density polyethylene waste , 2004 .

[28]  M. Guisnet,et al.  "Coke" molecules trapped in the micropores of zeolites as active species in hydrocarbon transformations , 2002 .

[29]  José M. Escola,et al.  Catalytic cracking of a polyolefin mixture over different acid solid catalysts , 2000 .

[30]  D. Serrano,et al.  Influence of nanocrystalline HZSM-5 external surface on the catalytic cracking of polyolefins , 2004 .

[31]  Y. Uemichi,et al.  Product distribution from catalytic degradation of polyethylene over H-gallosilicate , 2000 .