Turbidimetric studies of aqueous poly(vinyl alcohol) solutions

A freezing-thawing process of aqueous poly(vinyl alcohol), (PVA) solutions was undertaken to study the supermolecular PVA structures produced. Aqueous solutions of 2,5 to 15 wt.-% PVA were frozen at −20°C for 45 to 120min and were subsequently thawed for long periods of time (up to 12h) at 23 ± 1°C. The transmittance of visible light was recorded as a function of thawing time. Determination of the parameters of the supermolecular particles in the PVA solutions was done by application of Klenin's theory. The average radii of the particles were in the order of 1,6–2,3 μm. Ein Gefrier-/Auftauprozes von wasrigen Poly(vinyl alcohol), (PVA)-Losungen wurde angewendet, um die auftretenden ubermolekularen PVA-Strukturen zu untersuchen. Wasrige Losungen von 2,5–15 Gew.-% PVA wurden fur die Dauer von 45–120min bei −20°C zum Gefrieren gebracht und wurden anschliesend fur lange Zeitperioden (biszu 12h) bei 23 ± 1°C aufgetaut. Die Durchlassigkeit von sichtbarem Licht wurde als Funktion der Auftauzeit aufgezeichnet. Die Bestimmung der Parameter der ubermolekularen Teilchen in den PVA Losungen wurde durch Anwendung der Theorie von Klenin durchgefuhrt und ergab mittlere Radien in einer Grosenordnung von 1,6–2,3 μm.