CF4 plasma-modified omniphobic electrospun nanofiber membrane for produced water brine treatment by membrane distillation

Abstract This study describes the development and performance of an omniphobic poly(vinylidene fluoride) (PVDF) membrane by electrospinning and CF 4 plasma surface modification for air gap membrane distillation (AGMD). The effect of different duration of plasma treatment on the nanofiber membrane characteristics was investigated. The AGMD performance of the membranes was evaluated using real reverse osmosis (RO) brine produced from coal seam gas (CSG) water that was added with low surface tension liquid (surfactant) as feed solution. Results indicated the formation of new CF 2 -CF 2 and CF 3 bonds after plasma treatment, which lowered the surface energy of the membrane, providing omniphobic property, as indicated by its wetting resistance to different low surface tension liquids such as methanol, mineral oil and ethylene glycol. Though no appreciative changes in morphology of the membrane were observed after plasma treatment, optimal treatment condition of 15 min (i.e., P/CF-15 membrane) exhibited lotus effect membrane surface with increased liquid entry pressure of 187 kPa compared to 142 kPa for neat membrane. AGMD performance showed stable normalized flux (initial flux of 15.3 L/m 2 h) and rejection ratio (100%) for P/CF-15 even with the addition of up to 0.7 mM sodium dodecyl sulfate surfactant to the RO brine from CSG produced water feed, while commercial PVDF membrane suffered membrane wetting after 0.3 mM of surfactant addition. Based on the results, the present omniphobic membrane has good potential for producing clean water from challenging waters containing high salinity and organic contaminants.

[1]  M. R. M. Abed,et al.  Progress in the production and modification of PVDF membranes , 2011 .

[2]  C. J. Oss.  Development and applications of the interfacial tension between water and organic or biological surfaces. , 2007 .

[3]  Abraham Marmur,et al.  The Lotus effect: superhydrophobicity and metastability. , 2004, Langmuir : the ACS journal of surfaces and colloids.

[4]  H. Shon,et al.  Electrospun dual-layer nonwoven membrane for desalination by air gap membrane distillation , 2017 .

[5]  H. Shon,et al.  Characteristics of membrane fouling by consecutive chemical cleaning in pressurized ultrafiltration as pre-treatment of seawater desalination , 2015 .

[6]  F. Guittard,et al.  Branched Hydrocarbon Low Surface Energy Materials for Superhydrophobic Nanoparticle Derived Surfaces. , 2016, ACS applied materials & interfaces.

[7]  Youngjin Kim,et al.  Graphene/PVDF flat-sheet membrane for the treatment of RO brine from coal seam gas produced water by air gap membrane distillation , 2016 .

[8]  Peter Walzel,et al.  Wetting and self-cleaning properties of artificial superhydrophobic surfaces. , 2005, Langmuir : the ACS journal of surfaces and colloids.

[9]  Yasukiyo Ueda,et al.  The Lowest Surface Free Energy Based on −CF3 Alignment , 1999 .

[10]  J. Badyal,et al.  Super-hydrophobic Surfaces Produced by Plasma Fluorination of Polybutadiene Films , 2003 .

[11]  L. Nghiem,et al.  Coal seam gas produced water treatment by ultrafiltration, reverse osmosis and multi-effect distillation: A pilot study , 2015 .

[12]  Jan Feijen,et al.  Selective etching of semicrystalline polymers CF4 gas plasma treatment of poly(ethylene) , 1999 .

[13]  Jack Gilron,et al.  CF4 plasma-modified superhydrophobic PVDF membranes for direct contact membrane distillation , 2014 .

[14]  Menachem Elimelech,et al.  Direct contact membrane distillation with heat recovery: Thermodynamic insights from module scale modeling , 2014 .

[15]  J. Badyal,et al.  CF4 plasma treatment of asymmetric polysulfone membranes , 1996 .

[16]  N. Hilal,et al.  Membrane distillation: A comprehensive review , 2012 .

[17]  Stefan Seeger,et al.  Silicone Nanofilaments and Their Application as Superhydrophobic Coatings , 2006 .

[18]  Xueting Zhao,et al.  Hierarchically engineered membrane surfaces with superior antifouling and self-cleaning properties , 2013 .

[19]  Alidad Amirfazli,et al.  Understanding of sliding and contact angle results in tilted plate experiments , 2008 .

[20]  Jongho Lee,et al.  Engineering Surface Energy and Nanostructure of Microporous Films for Expanded Membrane Distillation Applications. , 2016, Environmental science & technology.

[21]  W. Zisman,et al.  Properties of Films of Adsorbed Fluorinated Acids , 1954 .

[22]  Guangzhi Zuo,et al.  Novel membrane surface modification to enhance anti-oil fouling property for membrane distillation application , 2013 .

[23]  T. He,et al.  Effective evaporation of CF4 plasma modified PVDF membranes in direct contact membrane distillation , 2015 .

[24]  Jongho Lee,et al.  Development of Omniphobic Desalination Membranes Using a Charged Electrospun Nanofiber Scaffold. , 2016, ACS applied materials & interfaces.

[25]  H. Busscher,et al.  Interaction of fibroblasts and polymer surfaces: relationship between surface free energy and fibroblast spreading. , 1983, Journal of biomedical materials research.

[26]  Won Ho Park,et al.  Superhydrophobicity of cellulose triacetate fibrous mats produced by electrospinning and plasma treatment , 2009 .

[27]  Menachem Elimelech,et al.  Omniphobic Membrane for Robust Membrane Distillation , 2014 .

[28]  Tao He,et al.  CF4 plasma surface modification of asymmetric hydrophilic polyethersulfone membranes for direct contact membrane distillation , 2012 .

[29]  Anita J. Hill,et al.  Nanocrack-regulated self-humidifying membranes , 2016, Nature.

[30]  Jianfeng Song,et al.  CF4 plasma modified highly interconnective porous polysulfone membranes for direct contact membrane distillation (DCMD) , 2015 .

[31]  Enrico Drioli,et al.  Water desalination using graphene-enhanced electrospun nanofiber membrane via air gap membrane distillation , 2016 .

[32]  M. Chan-Park,et al.  CF4 plasma treatment of poly(dimethylsiloxane): effect of fillers and its application to high-aspect-ratio UV embossing. , 2005, Langmuir : the ACS journal of surfaces and colloids.

[33]  E. R. Fisher,et al.  Contributions of CF and CF2 Species to fluorocarbon film composition and properties for C(x)F(y) plasma-enhanced chemical vapor deposition. , 2012, ACS applied materials & interfaces.

[34]  Jin Zhai,et al.  Super-Hydrophobic PDMS Surface with Ultra-Low Adhesive Force† , 2005 .

[35]  Rong Wang,et al.  Electrospun superhydrophobic membranes with unique structures for membrane distillation. , 2014, ACS applied materials & interfaces.

[36]  M. Elimelech,et al.  Engineering flat sheet microporous PVDF films for membrane distillation , 2015 .

[37]  Bharat Bhushan,et al.  Natural and biomimetic artificial surfaces for superhydrophobicity, self-cleaning, low adhesion, and drag reduction , 2011 .

[38]  Peng Wang,et al.  A new-generation asymmetric multi-bore hollow fiber membrane for sustainable water production via vacuum membrane distillation. , 2013, Environmental science & technology.

[39]  Enrico Drioli,et al.  Membrane distillation: Recent developments and perspectives , 2015 .