Synthesis and crystal structure of nitrate enclathrated sodalite Na8[AlSiO4]6(NO3)2

Abstract The hydrothermal formation of sodalites in the system Na2O2SiO2Al2O3NaNO3H2O has been investigated. Besides temperature and pressure, the initial materials of synthesis were varied to obtain the most perfect single crystals of nitrate enclathrated in sodalite. The alkaline transformation of Zeolite A as the starting aluminosilicate at a temperature of 648 K and a pressure of 0.1 GPa has been proved to be the best method for sodalite synthesis. A single crystal structure refinement, as well as MAS NMR of the nucleus 23Na of nitrate sodalite, have been carried out to determine the position of the enclathrated nitrate anions in the open sodalite structure. The nitrogen atoms are located in an off-centre position within the sodalite cages. One of the three oxygen atoms of the nitrate group is positioned near the centre of a face of the tetrahedron formed by the sodium cations. The two remaining oxygen atoms of the nitrate group are located near the middle of the edges of the sodium tetrahedron. This arrangement of the nitrate anions is responsible for two split-positions of the sodium cations according to an occupancy ratio of 3:1.

[1]  J.-Ch. Buhl,et al.  The properties of salt-filled sodalites part 2. Synthesis, decomposition reactions and phase transitions of nitrate sodalite Na8[AlSiO4]6(NO3)2 , 1991 .

[2]  J. Buhl Basic nitrite sodalite—Na8[AlSiO4]6(OH · H2O)(NO2)—A suitable material for the uptake of carbon dioxide , 1991 .

[3]  J.-Ch. Buhl,et al.  The properties of salt-filled sodalites: I. Thermal decomposition reactions of hydroxoborate sodalite , 1990 .

[4]  C. Baerlocher,et al.  Synthese und Kristallstruktur von Tetramethylammonium‐Sodalith , 1969 .

[5]  James A. Ibers,et al.  International tables for X-ray crystallography , 1962 .

[6]  C. Baerlocher,et al.  X-ray powder diffraction crystal structure analysis and 29Si, 23Na MAS n.m.r. studies of nitrite sodalite, Na8[AlSiO4]6 (NO2)2, at 295 K , 1991 .

[7]  G. Engelhardt,et al.  Synthesis, X-ray diffraction, and MAS n.m.r. characteristics of tetrahydroxoborate sodalite, Na8[AlSiO4]6[B(OH)4]2 , 1989 .

[8]  T. Veit,et al.  Hydrothermal synthesis, characterization and structure refinement of chlorate- and perchlorate-sodalite , 1991 .

[9]  J. Löns,et al.  Strukturverfeinerung von Sodalith, Na8Si6Al6O24Cl2 , 1967 .

[10]  É. Lippmaa,et al.  High-resolution NMR of quadrupolar nuclei in rotating solids , 1981 .

[11]  D. Taylor,et al.  The thermal expansion behaviour of the framework silicates , 1972, Mineralogical Magazine.

[12]  Von S. Göttlicher,et al.  Zur Kristallstruktur von Natriumnitrat , 1978 .

[13]  J. Buhl Hydrothermal synthesis and characterization of nitrite sodalite single crystals , 1991 .