Realization of low contact resistance close to theoretical limit in graphene transistors

AbstractRealizing low contact resistance between graphene and metal electrodes remains a well-known challenge for building high-performance graphene devices. In this work, we attempt to reduce the contact resistance in graphene transistors and further explore the resistance limit between graphene and metal contacts. The Pd/graphene contact resistance at room temperature is reduced below the 100 Ω·μm level both on mechanically exfoliated and chemical-vapor-deposition graphene by adopting high-purity palladium and high-quality graphene and controlling the fabrication process to not contaminate the interface. After excluding the parasitic series resistances from the measurement system and electrodes, the retrieved contact resistance is shown to be systematically and statistically less than 100 Ω·μm, with a minimum value of 69 Ω·μm, which is very close to the theoretical limit. Furthermore, the contact resistance shows no clear dependence on temperature in the range of 77–300 K; this is attributed to the saturation of carrier injection efficiency between graphene and Pd owing to the high quality of the graphene samples used, which have a sufficiently long carrier mean-free-path.

[1]  K. L. Shepard,et al.  One-Dimensional Electrical Contact to a Two-Dimensional Material , 2013, Science.

[2]  Luigi Colombo,et al.  Contact resistance in few and multilayer graphene devices , 2010 .

[3]  D. Goldhaber-Gordon,et al.  Evidence of the role of contacts on the observed electron-hole asymmetry in graphene , 2008, 0804.2040.

[4]  X. Liang,et al.  Ultraviolet/ozone treatment to reduce metal-graphene contact resistance , 2012, 1212.0838.

[5]  C. Kocabas,et al.  Rapid thermal annealing of graphene-metal contact , 2012 .

[6]  S. Banerjee,et al.  Realization of a high mobility dual-gated graphene field-effect transistor with Al2O3 dielectric , 2009, 0901.2901.

[7]  F. Xia,et al.  The origins and limits of metal-graphene junction resistance. , 2011, Nature nanotechnology.

[8]  Q. Fu,et al.  Repeated growth and bubbling transfer of graphene with millimetre-size single-crystal grains using platinum , 2012, Nature Communications.

[9]  R. Dong,et al.  Record maximum oscillation frequency in C-face epitaxial graphene transistors. , 2013, Nano letters.

[10]  Tomonori Nishimura,et al.  Systematic Investigation of the Intrinsic Channel Properties and Contact Resistance of Monolayer and Multilayer Graphene Field-Effect Transistor , 2010 .

[11]  Masashi Shiraishi,et al.  Transfer characteristics in graphene field-effect transistors with Co contacts , 2008 .

[12]  A. Toriumi,et al.  Metal/graphene contact as a performance Killer of ultra-high mobility graphene analysis of intrinsic mobility and contact resistance , 2009, 2009 IEEE International Electron Devices Meeting (IEDM).

[13]  K. Novoselov,et al.  A roadmap for graphene , 2012, Nature.

[14]  S. Xiao,et al.  Intrinsic and extrinsic performance limits of graphene devices on SiO2. , 2007, Nature nanotechnology.

[15]  Sheng Wang,et al.  Contact length scaling in graphene field-effect transistors , 2012 .

[16]  Joachim Knoch,et al.  Properties of Metal–Graphene Contacts , 2012, IEEE Transactions on Nanotechnology.

[17]  Deji Akinwande,et al.  Impact of contact resistance on the transconductance and linearity of graphene transistors , 2011 .

[18]  Seung-Hwan Lee,et al.  Plasma treatments to improve metal contacts in graphene field effect transistor , 2011 .

[19]  Lianmao Peng,et al.  Direct extraction of carrier mobility in graphene field-effect transistor using current-voltage and capacitance-voltage measurements , 2012 .

[20]  Zhiyong Zhang,et al.  Batch-fabricated high-performance graphene Hall elements , 2013, Scientific Reports.

[21]  Observation of negative contact resistances in graphene field-effect transistors , 2012, 1204.4315.

[22]  C. Dimitrakopoulos,et al.  Reducing contact resistance in graphene devices through contact area patterning. , 2013, ACS nano.