Influence of process induced defects on the failure of composite T-joint specimens

An experimental investigation of the failure load of T-joint structures has been undertaken, with a focus on the influence of process induced defects within the deltoid area. Static pull-off tension tests have been conducted for a comparative assessment. An extensive literature review on the subject to place is also presented. The role of the deltoid area in stabilizing the primary load bearing plies and minimising the volume fraction reduction in the off-axis plies is critical to maximise the failure load and minimise the performance variability of the T-joint structures. A deltoid area reduction of 25%, with no change in the external geometry, yielded a similar mechanical performance to the nominal baseline specimen but with increased variability. However, a reduction of 50% in the deltoid area yielded a strength reduction of 33%. The findings of this study suggest that the reduction in the deltoid area can be tolerated within certain limits.

[1]  J. Xiong,et al.  Mechanical Properties of RTM-made Composite Cross-joints , 2009 .

[2]  Recep Gunes,et al.  Thermal non-linear elastic stress analysis of an adhesively bonded T-joint , 2003 .

[3]  Damage tolerance of laminated tee joints in FRP structures , 1998 .

[4]  M. Kemal Apalak,et al.  Effect of adhesive free-end geometry on the initiation and propagation of damaged zones in adhesively bonded lap joints , 2004 .

[5]  M. Apalak,et al.  Thermal and Geometrically Nonlinear Stress Analyses of an Adhesively Bonded Composite Tee Joint with Double Support , 2004 .

[6]  B. Hill,et al.  The design and fabrication of 3D multi-layer woven T-section reinforcements , 1999 .

[7]  J. Ankersen,et al.  Virtual testing of realistic aerospace composite structures , 2008 .

[8]  M. Wisnom,et al.  Numerical investigation into failure of laminated composite T-piece specimens under tensile loading , 2012 .

[9]  Wing Kong Chiu,et al.  Disbond detection in adhesively bonded composite structures using vibration signatures , 2006 .

[10]  S. John,et al.  Applicability of the crack tip element analysis for damage prediction of composite T-joints , 2008 .

[11]  R. Pipes,et al.  Design of the composite spar-wingskin joint , 1982 .

[12]  V. Rao,et al.  Behaviour of composite wing T‐joints in hygrothermal environments , 2004 .

[13]  P. Sinha,et al.  Finite Element Analysis of Composite Wing T-Joints , 2002 .

[14]  R. A. Shenoi,et al.  Progressive damage analysis of tee joints with viscoelastic inserts , 2001 .

[15]  Michael R Wisnom,et al.  Variability, fibre waviness and misalignment in the determination of the properties of composite materials and structures , 2008 .

[16]  R. A. Shenoi,et al.  Influence of material and geometry variations on the behaviour of bonded tee connections in FRP ships , 1992 .

[17]  G. Allegri,et al.  On the delamination and debond suppression in structural joints by Z-fibre pinning , 2007 .

[18]  M. Wisnom,et al.  Prediction of delamination in braided composite T-piece specimens , 2009 .

[19]  G.A.O. Davies,et al.  Predicting delamination and debonding in modern aerospace composite structures , 2006 .

[20]  L. Limmer,et al.  Construction and analysis of three-dimensional woven composite materials , 1995 .

[21]  R. A. Shenoi,et al.  A Study of Structural Composite Tee Joints in Small Boats , 1990 .

[22]  Dan Zenkert,et al.  Testing and analysis of ultra thick composites , 2010 .

[23]  S. K. Panigrahi,et al.  Delamination Damage Analyses of FRP Composite Spar Wingskin Joints with Modified Elliptical Adhesive Load Coupler Profile , 2008 .

[24]  Sabu John,et al.  Damage detection in T-joint composite structures , 2006 .