Improvement in high temperature proton exchange membrane fuel cells cathode performance with ammonium carbonate

Abstract Proton exchange membrane (PEM) fuel cells with optimized cathode structures can provide high performance at higher temperature (120 °C). A “pore-forming” material, ammonium carbonate, applied in the unsupported Pt cathode catalyst layer of a high temperature membrane electrode assembly enhanced the catalyst activity and minimized the mass-transport limitations. The ammonium carbonate amount and Nafion ® loading in the cathode were optimized for performance at two conditions: 80 °C cell temperature with 100% anode/75% cathode R.H. and 120 °C cell temperature with 35% anode/35% cathode R.H., both under ambient pressure. A cell with 20 wt.% ammonium carbonate and 20 wt.% Nafion ® operating at 80 °C and 120 °C presented the maximum cell performance. Hydrogen/air cell voltages at a current density of 400 mA cm −2 using the Ionomem/UConn membrane as the electrolyte with a cathode platinum loading of 0.5 mg cm −2 were 0.70 V and 0.57 V at the two conditions, respectively. This was a 19% cell voltage increase over a cathode without the “pore-forming” ammonium carbonate at the 120 °C operating condition.

[1]  S. Gojković,et al.  Methanol oxidation on an ink type electrode using Pt supported on high area carbons , 2001 .

[2]  Tae-Hee Lee,et al.  Influence of pore-size distribution of diffusion layer on mass-transport problems of proton exchange membrane fuel cells , 2002 .

[3]  Shimshon Gottesfeld,et al.  Effect of Ammonia as Potential Fuel Impurity on Proton Exchange Membrane Fuel Cell Performance , 2002 .

[4]  Jean St-Pierre,et al.  Low Cost Electrodes for Proton Exchange Membrane Fuel Cells Performance in Single Cells and Ballard Stacks , 1997 .

[5]  Pierre Millet,et al.  Preparation and characterization of SPE composites forelectrolyzers and fuel cells , 1989 .

[6]  G. Squadrito,et al.  Nafion content in the catalyst layer of polymer electrolyte fuel cells: effects on structure and performance , 2001 .

[7]  J. Jindra,et al.  Porosity and catalyst utilization of thin layer cathodes in air operated PEM-fuel cells , 1998 .

[8]  R. Masel,et al.  Effects of Nafion as a binding agent for unsupported nanoparticle catalysts , 2003 .

[9]  H. R. Kunz,et al.  The Effect of Ammonia on Hydrogen‐Air Phosphoric Acid Fuel Cell Performance , 1980 .

[10]  Wei Tu,et al.  Study of the powder/membrane interface by using the powder microelectrode technique I. The Pt-black/Nafion® interfaces , 1998 .

[11]  Alexander Wokaun,et al.  Fundamental investigation of catalyst utilization at the electrode/solid polymer electrolyte interface: Part I. Development of a model system , 2003 .

[12]  Peter S. Fedkiw,et al.  An Impregnation‐Reduction Method to Prepare Electrodes on Nafion SPE , 1989 .

[13]  Hubert A. Gasteiger,et al.  Handbook of fuel cells : fundamentals technology and applications , 2003 .

[14]  Shimshon Gottesfeld,et al.  The Water Content Dependence of Electro-Osmotic Drag in Proton-Conducting Polymer Electrolytes , 1995 .

[15]  E. Passalacqua,et al.  Influence of Nafion loading in the catalyst layer of gas-diffusion electrodes for PEFC , 1999 .

[16]  Sanjeev Mukerjee,et al.  Effects of Nafion impregnation on performances of PEMFC electrodes , 1998 .

[17]  Hubert A. Gasteiger,et al.  Dependence of PEM fuel cell performance on catalyst loading , 2004 .

[18]  A. John Appleby,et al.  Recent progress in performance improvement of the proton exchange membrane fuel cell (PEMFC) , 2002 .

[19]  Z. Qi,et al.  Low Pt loading high performance cathodes for PEM fuel cells , 2003 .