Experimental Investigation of Material Removal Characteristics in Silicon Chemical Mechanical Polishing

The material removal characteristics of a silicon wafer were experimentally investigated with respect to the chemical dissolution and mechanical abrasion of the wafer during silicon chemical mechanical polishing (CMP) using an alkali-based slurry. The silicon surface without native oxide is rapidly dissolved by the slurry containing an amine agent, which effectively leads to the reduced hardness of the loaded silicon wafer due to Si–Si bond breaking during polishing. The abrasive particles in the slurry easily remove the reacted silicon surface, and the removal rate and wafer non-uniformity for abrasive concentrations of 1.5 – 3 wt % are better than those for other concentrations because of the low and steady coefficient of friction (COF) owing to the evenness of abrasive particles between the wafer and pad. Also, it was found that a high slurry flow rate of 700 –1000 cm 3 /min improves wafer non-uniformity owing to the reduced temporal variation of temperature, because the slurry acts as a good cooling source during polishing. However, the removal rate remains almost constant upon varying the slurry flow rate because of the effective dissolution characteristic of the slurry with abundant amine as an accelerator, regardless of the reduction of average temperature with increasing slurry flow rate. In the break-in process used to stabilize the material removal, the viscoelastic behaviors of the pad and the ground wafer surface with native oxide and wheel marks cause a temporal change of the friction force during polishing, which is related to the removal rate and wafer non-uniformity. As a result, the stabilization of removal rate and wafer non-uniformity is achieved through a steady-state process with elevated temperature and reduced COF after a total polishing time of 60 min, based on the removal process of the wafer surface and the permanent deformation in the viscoelastic behavior of the pad. # 2009 The Japan Society of Applied Physics

[1]  T. Kikkawa,et al.  Influence of CMP Chemicals on the Properties of Porous Silica Low-k Films , 2006 .

[2]  Tribochemical Reactions of Silicon: An In Situ Infrared Spectroscopy Characterization , 1998 .

[3]  Chemical boundary lubrication in chemical–mechanical planarization , 2005 .

[4]  Hyoungjae Kim,et al.  Heat and its effects to chemical mechanical polishing , 2006 .

[5]  L. Cook.  Chemical processes in glass polishing , 1990 .

[6]  Yongwu Zhao,et al.  A micro-contact and wear model for chemical-mechanical polishing of silicon wafers , 2002 .

[7]  Kyu-Kab Cho,et al.  CMP Pad Break-in Time Reduction in Silicon Wafer Polishing , 2007 .

[8]  Michael R. Oliver,et al.  Chemical-mechanical planarization of semiconductor materials , 2004 .

[9]  Effects of Slurry Particles on Silicon Dioxide CMP , 2004 .

[10]  L. Keer,et al.  A 3D EHL Simulation of CMP Theoretical Framework of Modeling , 2005 .

[11]  Brigid Mullany,et al.  The effect of slurry viscosity on chemical–mechanical polishing of silicon wafers , 2003 .

[12]  T. Cale,et al.  Von Mises Stress in Chemical‐Mechanical Polishing Processes , 1997 .

[13]  David Dornfeld,et al.  Material removal regions in chemical mechanical planarization for submicron integrated circuit fabrication: coupling effects of slurry chemicals, abrasive size distribution,and wafer-pad contact area , 2003 .

[14]  D. Lim,et al.  The effect of CeO2 abrasive size on dishing and step height reduction of silicon oxide film in STI–CMP , 2005 .

[15]  Joon-Yong Yoon,et al.  Chemical mechanical polishing by colloidal silica-based slurry for micro-scratch reduction , 2004 .

[16]  Experimental investigation on mechanisms of silicon chemical mechanical polishing , 2004 .

[17]  K. Kamei,et al.  AFM Studies on the Difference in Wear Behavior Between Si and SiO2 in KOH Solution , 2000 .

[18]  Ara Philipossian,et al.  Effect of Slurry Flow Rate on Tribological, Thermal, and Removal Rate Attributes of Copper CMP , 2004 .

[19]  Hyoungjae Kim,et al.  Effect of Process Parameters on Friction Force and Material Removal in Oxide Chemical Mechanical Polishing , 2008 .

[20]  X. Zhang.  Electrochemistry of silicon and its oxide , 2001 .

[21]  Ara Philipossian,et al.  Fundamental Tribological and Removal Rate Studies of Inter-Layer Dielectric Chemical Mechanical Planarization , 2003 .

[22]  W. Stickle,et al.  Handbook of X-Ray Photoelectron Spectroscopy , 1992 .

[23]  Masaharu Kinoshita,et al.  Pad Surface Treatment to Control Performance of Chemical Mechanical Planarization , 2008 .

[24]  Markus Forsberg,et al.  Effect of process parameters on material removal rate in chemical mechanical polishing of Si(100) , 2005 .

[25]  Kazuaki Yoshida.  Abrasive properties of nano silica particles prepared by a sol–gel method for polishing silicon wafers , 2007 .

[26]  R. Singh,et al.  pH and Down Load Effects on Silicon Dioxide Dielectric CMP , 2004 .

[27]  David Dornfeld,et al.  Material removal mechanism in chemical mechanical polishing: theory and modeling , 2001 .