Quantitative description of a very high critical current density Nb-Ti superconductor during its final optimization strain. II: Flux pinning mechanisms

Flux pinning by α‐Ti precipitates has been studied in a carefully made Nb 48 wt. % Ti composite having very high critical current density and a macroscopically rather uniform precipitate array. The pinning was studied as a function of field (0–15 T) and temperature (2.3 K—Tc) for a ratio of the precipitate thickness (tppt) and the coherence length (ξ) which was varied between 10 and 0.1 by a large drawing strain. Surprisingly, the maximum bulk pinning force (Fp) occurred for tppt/2ξ≂0.1 and a precipitate spacing about one‐eighth the fluxon spacing, suggesting that the flux pinning occurs at clusters of precipitates. In contrast to earlier studies, strict temperature scaling of Fp was not observed; the peak of the pinning force shifted to lower reduced fields as the temperature increased. The effect was largest for the finest scale microstructure. This nonscaling is interpreted in terms of two pinning mechanisms having different field and temperature dependencies. At low reduced fields, and at temperatures...

[1]  J. E. Evetts,et al.  Flux vortices and transport currents in type II superconductors , 2001 .

[2]  D. Larbalestier,et al.  Quantitative description of a high Jc Nb-Ti superconductor during its final optimization strain. I: Microstructure, Tc, Hc2, and resistivity , 1989 .

[3]  D. Larbalestier,et al.  Determination of the flux pinning force of α-Ti ribbons in Nb46.5wt% Ti produced by heat treatments of varying temperature, duration and frequency , 1988 .

[4]  K. Gray,et al.  Experimental study of the ultimate limit of flux pinning and critical currents in superconductors , 1988 .

[5]  T. Matsushita,et al.  Superconducting critical current of Nb‐Ti wire with anisotropic defect structure. II. , 1988 .

[6]  T. Matsushita,et al.  Enhancement of the superconducting critical current from saturation in Nb‐Ti wire. I. , 1988 .

[7]  W. Warnes.  A model for the resistive critical current transition in composite superconductors , 1988 .

[8]  H. Jones,et al.  Analysis of the general structure of the EI characteristic of high current superconductors with particular reference to a NbTi SRM wire , 1987 .

[9]  D. Larbalestier,et al.  Development of nanometer scale structures in composites of NbTi and their effect on the superconducting critical current density , 1987 .

[10]  W. Sampson,et al.  Importance of spacing in the development of high current densities in multifilamentary superconductors , 1987 .

[11]  D. Dew-Hughes.  The role of grain boundaries in determining J c in high-field high-current superconductors , 1987 .

[12]  D. Larbalestier,et al.  Development of high critical current densities in niobium 46.5 wt% titanium , 1987 .

[13]  D. Larbalestier,et al.  Critical current distributions in superconducting composites , 1986 .

[14]  S. Murase,et al.  Enhanced high-field current carrying capacities and pinning behavior of NbTi-based superconducting alloys , 1985 .

[15]  B. Zeitlin,et al.  High critical current densities in industrial scale composites made from high homogeneity Nb 46.5 Ti , 1985, IEEE Transactions on Magnetics.

[16]  D. Larbalestier,et al.  New perspectives on flux pinning in niobium-titanium composite superconductors , 1984 .

[17]  K. Osamura,et al.  Role of α precipitates in flux pinning in a superconducting Ti-Nb-Ta-Zr quaternary alloy , 1984 .

[18]  E. Thuneberg,et al.  Elementary-flux-pinning potential in type-II superconductors , 1984 .

[19]  D. Pattanayak,et al.  Influence of ternary additions and precipitation on the critical current density and other superconducting properties in Nb‐65 wt. %Ti , 1983 .

[20]  D. Larbalestier,et al.  α-Ti precipitates in high current density multifilamentary Niobium Titanium composites , 1983 .

[21]  E. Kramer,et al.  Grain-boundary flux pinning by the electron-scattering mechanism , 1982 .

[22]  D. Larbalestier.  Superconducting materials--A review of recent advances and current problems in practical materials , 1981 .

[23]  E. Kramer,et al.  The proximity effect in flux pinning , 1980 .

[24]  C. Koch,et al.  Flux pinning by small perturbations in the superconducting order parameter in type-II superconductors , 1980 .

[25]  G. Fuchs.  Pinning Mechanism in Superconducting NbTi Alloys at High Magnetic Fields , 1979 .

[26]  A. Larkin,et al.  Pinning in type II superconductors , 1979 .

[27]  J. Ekin.  Critical currents in granular superconductors , 1975 .

[28]  M. Mathur,et al.  Scaling laws for flux pinning in Nb and NbTi multifilamentary conductors , 1974 .

[29]  D. Dew-Hughes.  Flux pinning mechanisms in type II superconductors , 1974 .

[30]  K. Wohlleben,et al.  Influence of proton irradiation on the critical current densityjc(B, T) of NbTi , 1973 .

[31]  Edward J. Kramer,et al.  Scaling laws for flux pinning in hard superconductors , 1973 .

[32]  W. Webb,et al.  Hysteresis in Superconducting Alloys-Temperature and Field Dependence of Dislocation Pinning in Niobium Alloys , 1969 .

[33]  I Pfeiffer,et al.  Der einfluss der struktur auf die supraleitungseigenschaften von Nbti 50 und Nbti 65 , 1968 .

[34]  J. Livingston.  FLUX PINNING BY SUPERCONDUCTING PRECIPITATES , 1966 .

[35]  Y. Shapira,et al.  Upper critical fields of Nb--Ti alloys: evidence for the influence of Pauli paramagnetism , 1965 .

[36]  T. Matsushita.  Elementary pinning force of normal precipitates in a superconductor , 1983 .

[37]  M. T. Taylor,et al.  Critical supercurrents and the pinning of vortices in commercial Ng-60 at% Ti , 1972 .

[38]  P. Gennes.  Boundary Effects in Superconductors , 1964 .