Effect of hydroxyl concentration on Yb 3+ luminescence properties in a peraluminous lithium-alumino-silicate glass

Ytterbium doped lithium-alumino-silicate glasses suitable for diode-pumped laser applications were investigated concerning the hydroxyl quenching of the Yb3+ fluorescence. Glasses of the nominal composition 18 mol% Li2O, 22 mol% Al2O3 and 60 mol% SiO2 with variable OH concentrations NOH (between 0.04 and 6.01 ∙ 1019 cm−3) and Yb3+ concentrations NYb (between 0.1 and 9 ∙ 1020 cm−3) were produced and a direct correlation between spontaneous emission decay rate and the product NYb ∙ NOH was observed. The radiative spontaneous emission rate in the glass host is around 1,000 s−1 (radiative lifetime 1.0 ms) and the microparameter for Yb-Yb energy migration, CYb-Yb, was found to be 1.358∙10−38 cm6 s−1. It was calculated that on average 17% of the OH groups in the glass contribute to the quenching of the Yb3+ fluorescence. By analysis of the UV edge of the glass it was concluded that melting under inert conditions leads to reduction of iron impurities to Fe2+, which can act as quenching sites for the Yb3+ ions and therefore may additionally reduce the energy storage capability of the laser material.

[1]  T. Mocek,et al.  Spectroscopic characterization of Yb3+-doped laser materials at cryogenic temperatures , 2014 .

[2]  Markus P. Hehlen,et al.  Spectroscopic properties of Er 3+ - and Yb 3+ -doped soda-lime silicate and aluminosilicate glasses , 1997 .

[3]  Pieter G. Kik,et al.  Concentration quenching in erbium implanted alkali silicate glasses , 1996 .

[4]  Joachim Hein,et al.  Fluorescence and thermal stress properties of Yb3+-doped alumino silicate glasses for ultra high peak power laser applications , 2014 .

[5]  Danping Chen,et al.  Influence of Al3+ and P5+ ion contents on the valence state of Yb3+ ions and the dispersion effect of Al3+ and P5+ ions on Yb3+ ions in silica glass , 2014 .

[6]  Ferenc Krausz,et al.  Terawatt diode-pumped Yb:CaF2 laser. , 2008, Optics letters.

[7]  Joachim Hein,et al.  POLARIS: An All Diode-Pumped Ultrahigh Peak Power Laser for High Repetition Rates , 2006 .

[8]  J. Hein,et al.  Broad-band regenerative laser amplification in ytterbium-doped calcium fluoride (Yb:CaF2) , 2007 .

[9]  Joachim Hein,et al.  Magnesium aluminosilicate glasses as potential laser host material for ultrahigh power laser systems , 2013 .

[10]  Y. Kondo,et al.  Influence of water on non-radiative decay of Yb3+–2F5/2 level in phosphate glass , 2010 .

[11]  M. Bell,et al.  Energy transfer processes and heat generation in Yb3+-doped phosphate glasses , 2006 .

[12]  Johannes Kirchhof,et al.  Broadband, diode pumped Yb:SiO2 multicomponent glass laser. , 2012, Optics letters.

[13]  Edward M. Stolper,et al.  Water in silicate glasses: An infrared spectroscopic study , 1982 .

[14]  Joachim Hein,et al.  High-intensity, high-contrast laser pulses generated from the fully diode-pumped Yb:glass laser system POLARIS. , 2013, Optics letters.

[15]  C. Rüssel,et al.  High strength glass–ceramics in the system MgO/Y2O3/Al2O3/SiO2/ZrO2 without quartz as crystalline phase , 2013, Journal of Materials Science.

[16]  Joachim Hein,et al.  Measurement of temperature-dependent absorption and emission spectra of Yb:YAG, Yb:LuAG, and Yb:CaF_2 between 20 °C and 200 °C and predictions on their influence on laser performance , 2012 .

[17]  Georges Boulon,et al.  Spectroscopic properties, concentration quenching, and laser investigations of Yb 3+ -doped calcium aluminosilicate glasses , 2011 .

[18]  C. Rüssel,et al.  Sm3+-doped La2O3–Al2O3–SiO2-glasses: structure, fluorescence and thermal expansion , 2013, Journal of Materials Science.

[19]  C. Patzig,et al.  High-strength glass-ceramics in the system MgO/Al2O3/SiO2/ZrO2/Y2O3 – microstructure and properties , 2013 .

[20]  Lili Hu,et al.  Concentration quenching in erbium-doped tellurite glasses , 2006 .

[21]  Jack H. Campbell,et al.  Nonradiative Energy Losses and Radiation Trapping in Neodymium‐Doped Phosphate Laser Glasses , 2004 .

[22]  Doris Ehrt,et al.  Fluoroaluminate glasses for lasers and amplifiers , 2003 .

[23]  J. Hein,et al.  Diode-pumped lasers for ultra-high peak power , 2008 .

[24]  J. Jewell,et al.  Effects of water content on the properties of sodium aluminosilicate glasses , 1992 .

[25]  Takahiro Murata,et al.  Compositional Dependence of Absorption and Fluorescence of b3+ in Oxide Glasses , 2005 .

[26]  C. Rüssel,et al.  The effect of composition on UV-vis-NIR spectra of iron doped glasses in the systems Na2O/MgO/SiO2 and Na2O/MgO/Al2O3/SiO2 , 2007 .

[27]  L. Cook,et al.  Ultraviolet Transmission Characteristics of a Fluorophosphate Laser Glass , 1982 .

[28]  D. Ehrt,et al.  Dehydration of phosphate glasses , 1993 .

[29]  D. Ehrt.  UV-absorption and radiation effects in different glasses doped with iron and tin in the ppm range , 2002 .

[30]  Markus P. Hehlen,et al.  Model of laser cooling in theYb3+-doped fluorozirconate glass ZBLAN , 2007 .

[31]  Long Zhang,et al.  The effect of OH− on IR emission of Nd3+, Yb3+ and Er3+ doped tetraphosphate glasses , 2002 .

[32]  Ulrich Schramm,et al.  PEnELOPE: a high peak-power diode-pumped laser system for laser-plasma experiments , 2013, Europe Optics + Optoelectronics.

[33]  Qiang Zeng,et al.  Hydroxyl-contents and hydroxyl-related concentration quenching in erbium-doped aluminophosphate, aluminosilicate and fluorosilicate glasses , 2001 .

[34]  D. Ehrt,et al.  GLASS FOR HIGH PERFORMANCE OPTICS AND LASER TECHNOLOGY , 1991 .

[35]  L. Norin,et al.  Preventing photodarkening in ytterbium-doped high power fiber lasers; correlation to the UV-transparency of the core glass. , 2008, Optics express.

[36]  M. Bell,et al.  Effects of non-radiative processes on the infrared luminescence of Yb3+ doped glasses , 2005 .

[37]  J. Hein,et al.  Diode-pumped chirped pulse amplification to the joule level , 2004 .

[38]  D. L. Dexter.  A Theory of Sensitized Luminescence in Solids , 1953 .

[39]  D. Mccumber,et al.  Einstein Relations Connecting Broadband Emission and Absorption Spectra , 1964 .

[40]  Lloyd L. Chase,et al.  Infrared cross-section measurements for crystals doped with Er/sup 3+/, Tm/sup 3+/, and Ho/sup 3+/ , 1992 .