Natural Weathering Effects on the Mechanical, Rheological, and Morphological Properties of Magnetorheological Elastomer (MRE) in Tropical Climate

Magnetorheological elastomer (MRE) materials have the potential to be used in a wide range of applications that require long-term service in hostile environments. These widespread applications will result in the emergence of MRE-specific durability issues, where durability refers to performance under in-service environmental conditions. In response, the outdoor tropical climatic environment, combined with the effects of weathering, will be the primary focus of this paper, specifically the photodegradation of the MRE. In this study, MRE made of silicone rubber (SR) and 70 wt% micron-sized carbonyl iron particles (CIP) were prepared and subjected to mechanical and rheological testing to evaluate the effects under natural weathering. Magnetorheological elastomer samples were exposed to the natural weathering conditions of a tropical climate in Kuala Lumpur, Malaysia, for 30 days. To obtain a comprehensive view of MRE degradation during natural weathering, mechanical testing, rheology, and morphological evaluation were all performed. The mechanical and rheological properties test results revealed that after 30 days of exposure and known meteorological parameters, Young’s modulus and storage modulus increased, while elongation at break decreased. The degradation processes of MRE during weathering, which are responsible for their undesirable change, were given special attention. With the help of morphological evidence, the relationship between these phenomena and the viscoelastic properties of MRE was comprehensively defined and discussed.

[1]  S. Mazlan,et al.  Reprocessed magnetorheological elastomers with reduced carbon footprint and their piezoresistive properties , 2022, Scientific Reports.

[2]  R. A. Rashid,et al.  Temperature Dependent on Mechanical and Rheological Properties of EPDM-Based Magnetorheological Elastomers Using Silica Nanoparticles , 2022, Materials.

[3]  S. Mazlan,et al.  Declining Performance of Silicone-Based Magnetorheological Elastomers after Accelerated Weathering , 2021, Materials.

[4]  S. Mazlan,et al.  The Effect of Microparticles on the Storage Modulus and Durability Behavior of Magnetorheological Elastomer , 2021, Micromachines.

[5]  A. Arias,et al.  Influence of elastomeric matrix and particle volume fraction on the mechanical response of magneto-active polymers , 2021 .

[6]  M. Nasef,et al.  Microstructural behavior of magnetorheological elastomer undergoing durability evaluation by stress relaxation , 2021, Scientific Reports.

[7]  Seung-bok Choi,et al.  Thermal Aging Rheological Behavior of Magnetorheological Elastomers Based on Silicone Rubber , 2020, International journal of molecular sciences.

[8]  Nurhazimah Nazmi,et al.  An Overview of Durability Evaluations of Elastomer-Based Magnetorheological Materials , 2020, IEEE Access.

[9]  Z. M. Mohd Ishak,et al.  Accelerated Weathering and Water Absorption Behavior of Kenaf Fiber Reinforced Acrylic Based Polyester Composites , 2020, Frontiers in Materials.

[10]  T. Nam,et al.  Experimental characterization and viscoelastic modeling of isotropic and anisotropic magnetorheological elastomers , 2020 .

[11]  M. Mrlík,et al.  Reprocessing of injection-molded magnetorheological elastomers based on TPE matrix , 2019, Composites Part B: Engineering.

[12]  F. Mortier,et al.  Fatigue of natural rubber under different temperatures , 2019, International Journal of Fatigue.

[13]  Kwang-Hee Lee,et al.  Effect of Temperature and Relative Humidity on Friction and Wear Properties of Silicone-Based Magnetorheological Elastomer , 2018 .

[14]  B. Fox,et al.  Mechanical, Thermal, and Morphological Behavior of Silicone Rubber during Accelerated Aging , 2018 .

[15]  Abeer Samy Yousef Mohamed,et al.  Smart Materials Innovative Technologies in architecture; Towards Innovative design paradigm , 2017 .

[16]  B Subba Reddy,et al.  Studies on high temperature vulcanized silicone rubber insulators under arid climatic aging , 2017, IEEE Transactions on Dielectrics and Electrical Insulation.

[17]  Erwan Verron,et al.  Fatigue resistance of natural rubber in seawater with comparison to air , 2016 .

[18]  L. Kari,et al.  Measurements on the Temperature, Dynamic Strain Amplitude and Magnetic Field Strength Dependence of the Dynamic Shear Modulus of Magnetosensitive Elastomers in a Wide Frequency Range , 2013 .

[19]  I. Hudeč,et al.  Influence of thermo-oxidative and ozone ageing on the properties of elastomeric magnetic composites , 2012 .

[20]  Wei Zhang,et al.  Investigation of the durability of anisotropic magnetorheological elastomers based on mixed rubber , 2010 .

[21]  H. Ismail,et al.  Natural Weathering Test of Styrene Butadiene Rubber and Recycled Acrylonitrile Butadiene Rubber (SBR/NBRr) Blends , 2010 .

[22]  Seong Beom Lee,et al.  Useful Lifetime Prediction of Rubber Components Using Accelerated Testing , 2010, IEEE Transactions on Reliability.

[23]  H. Ismail,et al.  Natural Weathering of Polypropylene and Waste Tire Dust (PP/WTD) Blends , 2008 .

[24]  M. Mariatti,et al.  Effects of Natural Weathering on Properties of Recycled Newspaper-filled Polypropylene (PP)/Natural Rubber (NR) Composites , 2008 .

[25]  H. Gu Degradation of glass fibre/polyester composites after ultraviolet radiation , 2008 .

[26]  C. Naddeo,et al.  Photooxidation of spherilene linear low-density polyethylene films subjected to environmental weathering. 1. Changes in mechanical properties , 2004 .

[27]  D. Feldman,et al.  Polymer Weathering: Photo-Oxidation , 2002 .

[28]  Y. Nishimoto,et al.  Analysis of weathering of a thermoplastic polyester elastomer. II. Factors affecting weathering of a polyether-polyester elastomer , 1999 .

[29]  A. Stevenson On the durability of rubber/metal bonds in seawater , 1985 .