Hydrogen embrittlement susceptibility of tempered 9%Cr–1%Mo steel

Abstract The influence of the subsurface hydrogen activity on the hydrogen embrittlement (HE) susceptibility of a tempered 9%Cr–1%Mo ferritic-martensitic steel (T91) has been studied by constant extension rate tests (CERT) performed under cathodic charging during straining at 20 °C. Changes in the hydrogen activity on the surface were obtained by varying the cathodic current density imposed during a tensile test completed to fracture. The broken samples were observed by scanning electron microscopy (SEM). The results show a strong dependence of the extent of the brittle zone with the subsurface hydrogen activity. This effect could be attributed to an enhancement of the apparent diffusion coefficient of hydrogen when increasing H activity. Increasing H activity could enhance both the trapping rate on pre-existing and strain-induced traps and H dragging by moving traps such as dislocations.

[1]  Thorsten Michler,et al.  Microstructural aspects upon hydrogen environment embrittlement of various bcc steels , 2010 .

[2]  S. Saroja,et al.  Influence of microstructure on the hydrogen permeability of 9%Cr–1%Mo ferritic steel , 1999 .

[3]  A. Brass,et al.  Fragilisation des aciers par l’hydrogène : étude et prévention , 2000, Corrosion Vieillissement.

[4]  M. Dadfarnia,et al.  Hydrogen interaction with multiple traps: Can it be used to mitigate embrittlement? , 2011 .

[5]  H. Ullmaier,et al.  Fatigue of DIN 1.4914 martensitic stainless steel in a hydrogen environment , 1994 .

[6]  M. Iino.  A more generalized analysis of hydrogen trapping , 1982 .

[7]  Chien-Yu Chen,et al.  Mechanical properties of modified 9Cr-1Mo steel welds with notches , 2003 .

[8]  R. Latanision,et al.  Theoretical study of hydrogen transport during plastic deformation in iron , 1988 .

[9]  F. Guillon,et al.  Quantification of hydrogen diffusion and trapping in 2.25Cr-1Mo and 3Cr-1Mo-V steels with the electrochemical permeation technique and melt extractions , 2004 .

[10]  Zhidan Sun,et al.  Fatigue crack propagation under gaseous hydrogen in a precipitation-hardened martensitic stainless steel , 2011 .

[11]  P. Bruzzoni,et al.  Effect of microstructure on hydrogen diffusion and trapping in a modified 9%Cr–1%Mo steel , 2010 .

[12]  R. K. Dayal,et al.  Hydrogen embrittlement in power plant steels , 2003 .

[13]  J. Chêne,et al.  Influence of tensile straining on the permeation of hydrogen in low alloy Cr-Mo steels. , 2006 .