Ultraviolet light test and evaluation methods for encapsulants of photovoltaic modules

Photovoltaic (PV) modules are exposed to harsh conditions of heat, humidity, high voltage, mechanical stress, thermal cycling, and ultraviolet (UV) radiation. The current qualification tests (e.g. IEC 61215) do not require UV exposure sufficient to evaluate a lifespan of 20 years or more. Methods to quickly evaluate the UV durability of photovoltaic materials are needed. The initial performance and cost of encapsulant materials must be taken into account, but equally important is their ability to maintain adhesion and transmissivity under UV exposure. This can be evaluated under highly accelerated conditions with light from a xenon arc lamp using glass that transmits more UV radiation than a module would normally see. The use of highly UV transmissive glass (no Ce to block UV-B radiation) results in a UV dose that is about 3.8 times greater with regard to adhesion than a Ce-containing glass. With this configuration, the effect of 20 years of exposure, as compared with the use of UV-B blocking glass, can be simulated in just over 6 months using standard commercial accelerated stress chambers. This also indicates that the use of non-UV blocking glass may significantly reduce the long-term adhesive stability of PV materials.

[1]  J. Pitts,et al.  Ultra accelerated testing of PV module components , 1998 .

[2]  M. Kempe.  Modeling of rates of moisture ingress into photovoltaic modules , 2006 .

[3]  M. Vázquez,et al.  Photovoltaic module reliability model based on field degradation studies , 2008 .

[4]  A. Andrady.  Wavelength sensitivity in polymer photodegradation , 1997 .

[5]  D. Tarrant,et al.  Stress induced degradation modes in CIGS mini-modules , 2008, 2008 33rd IEEE Photovoltaic Specialists Conference.

[6]  L. Moore,et al.  Five years of operating experience at a large, utility‐scale photovoltaic generating plant , 2008 .

[7]  A L Andrady,et al.  Effects of increased solar ultraviolet radiation on materials. , 1998, Journal of photochemistry and photobiology. B, Biology.

[8]  Michael Rubin,et al.  Optical Properties of Soda Lime Silica Glasses , 1985 .

[9]  R. G. Ross,et al.  Electrochemical degradation of amorphous-silicon photovoltaic modules , 1985 .

[10]  William Q. Meeker,et al.  Pitfalls of accelerated testing , 1998 .

[11]  Optical changes in cerium-containing glass as a result of accelerated exposure testing [of PV modules] , 1997, Conference Record of the Twenty Sixth IEEE Photovoltaic Specialists Conference - 1997.

[12]  D. L. King,et al.  Commonly observed degradation in field-aged photovoltaic modules , 2002, Conference Record of the Twenty-Ninth IEEE Photovoltaic Specialists Conference, 2002..

[13]  T. J. McMahon.  Accelerated testing and failure of thin‐film PV modules , 2004 .

[14]  D. L. King,et al.  Photovoltaic module performance and durability following long‐term field exposure , 2000 .

[15]  Xing-fang Hu.  Wavelength sensitivity of photo-oxidation of polyamide 6 , 1998 .

[16]  L. Olsen,et al.  Effects of buffer layers on SSI CIGSS-absorber transient I-V and C-V behavior , 2000, Conference Record of the Twenty-Eighth IEEE Photovoltaic Specialists Conference - 2000 (Cat. No.00CH37036).

[17]  C. Platzer‐Björkman,et al.  The influence of buffer layer on the transient behavior of thin film chalcopyrite devices , 2004 .

[18]  Z. Gu.  Spectroscopic properties of doped silica glasses , 1982 .

[19]  M. Ezrin,et al.  Investigation into the causes of browning in EVA encapsulated flat plate PV modules , 1994, Proceedings of 1994 IEEE 1st World Conference on Photovoltaic Energy Conversion - WCPEC (A Joint Conference of PVSC, PVSEC and PSEC).

[20]  T. Saitoh,et al.  Effect of illumination conditions on Czochralski-grown silicon solar cell degradation , 2003 .

[21]  M. DeBergalis.  Fluoropolymer films in the photovoltaic industry , 2004 .

[22]  P. Longrigg.  An investigation into the use of inorganic coatings for thin film photovoltaic modules , 1989 .

[23]  D. Myers.  Predicting Temperatures of Exposure Panels: Models and Empirical Data , 1999 .

[24]  E. Dunlop,et al.  The performance of crystalline silicon photovoltaic solar modules after 22 years of continuous outdoor exposure , 2006 .

[25]  David R. Bauer,et al.  Service life prediction of organic coatings : a systems approach , 1999 .

[26]  Cheryl E. Kennedy,et al.  Acetic acid production and glass transition concerns with ethylene-vinyl acetate used in photovoltaic devices , 2007 .

[27]  Hu Xingzhou.  Wavelength sensitivity of photo-oxidation of polyethylene , 1997 .

[28]  F. Pern,et al.  Improved photostability of NREL-developed EVA pottant formulations for PV module encapsulation , 1997, Conference Record of the Twenty Sixth IEEE Photovoltaic Specialists Conference - 1997.

[29]  A. Torikai,et al.  Wavelength effect on the accelerated photodegradation of polymethylmethacrylate , 1998 .