Novel sodium alginate-poly(N-isopropylacrylamide) semi-interpenetrating polymer network membranes for pervaporation separation of water + ethanol mixtures

Abstract Novel semi-interpenetrating polymer network (semi-IPN) membranes of sodium alginate (NaAlg) and thermoresponsive poly( N- isopropylacrylamide) (PNIPAAm) were prepared by free radical polymerization using potassium persulfate as an initiator. Membranes were crosslinked with glutaraldehyde and used in pervaporation (PV) separation of water–ethanol mixtures at varying feed compositions and temperatures. Membranes were characterized by Fourier transform infrared spectroscopy (FTIR) to assess intermolecular interactions. Thermogravimetry (TGA) was used to study their thermal stability. PV separation characteristics of the membranes showed a dependence on thermosensitive nature of NIPAAm. Increasing the NIPAAm content of the semi-IPN network resulted in an increased selectivity with a decreased permeation flux. The membrane containing 30 wt.% NIPAAm showed the highest selectivity of 18,881 with a flux of 0.137 kg/m 2  h at 40 °C, i.e., the above lower critical solution temperature (LCST) of NIPAAm, but below its LCST, i.e., at 25 °C, it exhibited considerably a lower selectivity of 92 with a flux of 0.185 kg/m 2  h for 15 wt.% water containing feed. Selectivity decreased with decreasing temperature at 15 wt.% water in the feed mixture below the LCST region, i.e., at 30 °C due to increase in the membrane pore size, thereby affecting the membrane selectivity with a considerable increase in flux of up to 0.225 kg/m 2  h. The reported membranes are of the first kind in the membrane literature, wherein a thermoresponsive NIPAAm polymer is used with a hydrophilic NaAlg polymer to form the semi-IPN membrane for PV dehydration of ethanol.

[1]  Q. Nguyen,et al.  Novel membranes made from a semi‐interpenetrating polymer network for ethanol–ETBE separation by pervaporation , 1997 .

[2]  T. Nonaka,et al.  Preparation of poly(vinyl alcohol)‐graft‐N‐isopropylacrylamide copolymer membranes and permeation of solutes through the membranes , 1994 .

[3]  T. Okano,et al.  Comb-type grafted hydrogels with rapid deswelling response to temperature changes , 1995, Nature.

[4]  Teruo Okano,et al.  Temperature dependence of swelling of crosslinked poly(N,N′-alkyl substituted acrylamides) in water , 1990 .

[5]  R. Huang,et al.  Pervaporation membrane separation processes , 1991 .

[6]  Richard W. Baker,et al.  'Membrane Separation Systems : Recent Developments and Future Directions , 1991 .

[7]  T. Aminabhavi,et al.  Preparation and characterization of filled matrix membranes of sodium alginate incorporated with aluminum-containing mesoporous silica for pervaporation dehydration of alcohols , 2007 .

[8]  R. Bischoff,et al.  Polysiloxanes in macromolecular architecture , 1999 .

[9]  Young Moo Lee,et al.  pH/temperature-responsive behaviors of semi-IPN and comb-type graft hydrogels composed of alginate and poly(N-isopropylacrylamide) , 2001 .

[10]  C. Yeom,et al.  Characterization of sodium alginate membrane crosslinked with glutaraldehyde in pervaporation separation , 1998 .

[11]  Robert Y. M. Huang,et al.  Novel two-ply composite membranes of chitosan and sodium alginate for the pervaporation dehydration of isopropanol and ethanol , 1999 .

[12]  Jan Feijen,et al.  Effect of comonomer hydrophilicity and ionization on the lower critical solution temperature of N-isopropylacrylamide copolymers , 1993 .

[13]  E. Jeon,et al.  IPN Membranes for the Pervaporation of Ethanol/Water Mixture , 1991 .

[14]  Allan S. Huffman,et al.  Thermally reversible hydrogels: II. Delivery and selective removal of substances from aqueous solutions , 1986 .

[15]  T. Aminabhavi,et al.  Sodium alginate–poly(hydroxyethylmethacrylate) interpenetrating polymeric network membranes for the pervaporation dehydration of ethanol and tetrahydrofuran , 2006 .

[16]  Richard W. Baker,et al.  The separation of dissolved organics from water by pervaporation , 1990 .

[17]  Young Keun Lee,et al.  Cationic/anionic interpenetrating polymer network membranes for the pervaporation of ethanol-water mixture , 1990 .

[18]  A. Buyanov,et al.  Cellulose-poly(acrylamide or acrylic acid) interpenetrating polymer network membranes for the pervaporation of water-ethanol mixtures , 1998 .

[19]  T. Aminabhavi,et al.  Microporous alumino-phosphate (AlPO4-5) molecular sieve-loaded novel sodium alginate composite membranes for pervaporation dehydration of aqueous-organic mixtures near their azeotropic compositions , 2006 .

[20]  J. Feijen,et al.  Molecular separation by thermosensitive hydrogel membranes , 1991 .

[21]  T. Aminabhavi,et al.  Mesoporous molecular sieve (MCM-41)-filled sodium alginate hybrid nanocomposite membranes for pervaporation separation of water–isopropanol mixtures , 2006 .

[22]  T. Aminabhavi,et al.  Synthesis of graft copolymeric membranes of poly(vinyl alcohol) and polyacrylamide for the pervaporation separation of water/acetic acid mixtures , 2002 .

[23]  Leslie H. Sperling,et al.  Interpenetrating Polymer Networks and Related Materials , 1981 .

[24]  T. Okano,et al.  A new thermo-sensitive hydrogel: Interpenetrating polymer networks from N-acryloylpyrrolidine and poly(oxyethylene) , 1988 .

[25]  S. B. Sawant,et al.  Pervaporative dehydration of organic solvents , 1997 .

[26]  C. Yeom,et al.  Characterization of relaxation phenomena and permeation behaviors in sodium alginate membrane during pervaporation separation of ethanol–water mixture , 1996 .

[27]  L. Pohorecky,et al.  Pharmacology of ethanol. , 1988, Pharmacology & therapeutics.

[28]  Y. Lee,et al.  Pervaporation separation of methanol/methyl t-butyl ether through chitosan composite membrane modified with surfactants , 1999 .

[29]  Mahaveer D. Kurkuri,et al.  Syntheses and characterization of blend membranes of sodium alginate and poly(vinyl alcohol) for the pervaporation separation of water + isopropanol mixtures , 2002 .

[30]  T. Aminabhavi,et al.  Novel sodium alginate composite membranes incorporated with SBA-15 molecular sieves for the pervaporation dehydration of aqueous mixtures of isopropanol and 1,4-dioxane at 30 °C , 2006 .

[31]  Teruo Okano,et al.  Thermally on-off switching polymers for drug permeation and release , 1990 .

[32]  T. Matsuura,et al.  Effect of surface-modifying macromolecules and solvent evaporation time on the performance of polyethersulfone membranes for the separation of chloroform/water mixtures by pervaporation , 1994 .