Deformation and Failure Modes of Soft Steel Projectiles Impacting Harder Steel Targets at Increasing Velocity

The present paper describes an experimental and numerical study concerning the impact of blunt steel projectiles against harder steel plates, at impact velocities between 200 and 800 m/s. In contrast with previously published observations, three modes of deformation and failure of the soft steel projectiles were observed in the present study. These included: Taylor cylinder mushrooming, sunflower-like petalling and plugging perforation. Individual velocity ranges and the transitions between the deformation/failure modes are identified by both experiments and numerical simulations. Complex material failure mechanisms of projectile and target play conflicting roles in the various penetration stages. Johnson–Cook models of strength and accumulative damage failure are employed in 3D numerical simulation to describe material behavior of both projectile and target. Computational evolutions of each scenario are offered in detail to understand the deformation and failure of projectile and target plate.

[1]  Tore Børvik,et al.  Observations on shear plug formation in Weldox 460 E steel plates impacted by blunt-nosed projectiles , 2001 .

[2]  William James Stronge,et al.  Plate perforation by deformable projectiles — A plastic wave theory , 1983 .

[3]  M. Langseth,et al.  Effect of target thickness in blunt projectile penetration of Weldox 460 E steel plates , 2003 .

[4]  Rodney F. Recht,et al.  Taylor ballistic impact modelling applied to deformation and mass loss determinations , 1978 .

[5]  Chen Gang,et al.  Investigation and validation on plastic constitutive parameters of 45 steel , 2005 .

[6]  Odd Sture Hopperstad,et al.  Perforation of 12 mm thick steel plates by 20 mm diameter projectiles with flat, hemispherical and conical noses: Part II: numerical simulations , 2002 .

[7]  Qingming Li,et al.  Shear plugging and perforation of ductile circular plates struck by a blunt projectile , 2003 .

[8]  XU Ai-ming.  Three modes of penetration mechanics of A3 steel cylindrical projectiles impact onto 45 steel plates , 2006 .

[9]  Tomasz Wierzbicki,et al.  Numerical prediction of fracture in the Taylor test , 2005 .

[10]  Xiao Wei Chen,et al.  Three Modes of Penetration Mechanisms of A3 Steel Cylindrical Projectiles Impact onto 45 Steel Plates , 2007 .

[11]  Dongquan Liu,et al.  Ballistic limit of metal plates struck by blunt deformable missiles : experiments , 2000 .

[12]  Qingming Li,et al.  Perforation of a thick plate by rigid projectiles , 2003 .

[13]  T. Wierzbicki,et al.  On fracture locus in the equivalent strain and stress triaxiality space , 2004 .

[14]  S. Dey,et al.  The effect of target strength on the perforation of steel plates using three different projectile nose shapes , 2004 .

[15]  M. J. Forrestal,et al.  Perforation experiments on HY-100 steel plates with 4340 Rc 38 and maraging T-250 steel rod projectiles , 1999 .

[16]  G. R. Johnson,et al.  Fracture characteristics of three metals subjected to various strains, strain rates, temperatures and pressures , 1985 .

[17]  Tore Børvik,et al.  Perforation of 12 mm thick steel plates by 20 mm diameter projectiles with flat, hemispherical and c , 2002 .

[18]  Ahmed Benallal,et al.  Flow and fracture characteristics of aluminium alloy AA5083–H116 as function of strain rate, temperature and triaxiality , 2004 .