Enhanced chemical stability of VO2 nanoparticles by the formation of SiO2/VO2 core/shell structures and the application to transparent and flexible VO2-based composite foils with excellent thermochromic properties for solar heat control

Vanadium dioxide is a key material for thermochromic smart windows that can respond to environmental temperature and modulate near infrared irradiation by changing from a transparent state at low temperature to a more reflective state at high temperature, while maintaining visible transmittance. VO2 thermochromism is commonly used in films on glass that function as smart windows. Flexible VO2 nanocomposite foils are able to combine the intrinsic properties of VO2 nanoparticles with the added functionalities contributed by nanoscale and interface effects, such as increased visible transparency and infrared modulation ability. These foils are promising for applications in construction and automotive glasses to increase energy efficiency. However, VO2 nanoparticles may be unstable, and they are difficult to prepare in stable dispersive suspensions. In this paper, we report a novel all-solution process that can be used to prepare transparent, stable and flexible VO2-based composite films. These films exhibit UV-shielding properties and an excellent temperature-responsive thermochromism in the near infrared region. A typical film has a solar modulation efficiency of 13.6%, which is the highest value for VO2 thermochromic films with comparable visible transmittance. Coating the VO2 nanoparticles with a thin SiO2 shell significantly improved their anti-oxidation and anti-acid abilities. This result represents an important breakthrough in VO2 thermochromism, and it may have applications for near infrared modulation of glass used in construction or cars.

[1]  Yanfeng Gao,et al.  Thermochromic VO2 thin films: solution-based processing, improved optical properties, and lowered phase transformation temperature. , 2010, Langmuir : the ACS journal of surfaces and colloids.

[2]  A. S. Barker,et al.  Infrared Optical Properties of Vanadium Dioxide Above and Below the Transition Temperature , 1966 .

[3]  Claes-Göran Granqvist,et al.  Thermochromic multilayer films of VO2 and TiO2 with enhanced transmittance , 2009 .

[4]  Gang Xu,et al.  Optimization of antireflection coating for VO2-based energy efficient window , 2004 .

[5]  Gang Xu,et al.  A VO2-Based Multifunctional Window with Highly Improved Luminous Transmittance , 2002 .

[6]  Guoqiang Tan,et al.  VO2-based double-layered films for smart windows: Optical design, all-solution preparation and improved properties , 2011 .

[7]  A. Polity,et al.  Annealing effects on VO2 thin films deposited by reactive sputtering , 2006 .

[8]  Christina Graf,et al.  A General Method To Coat Colloidal Particles with Silica , 2003 .

[9]  Y. Mai,et al.  Facile Synthesis of Highly Transparent Polymer Nanocomposites by Introduction of Core–Shell Structured Nanoparticles , 2008 .

[10]  D. Gu,et al.  Synthesis and stabilization of ZnS nanoparticles embedded in silica nanospheres , 2005 .

[11]  Zhenda Lu,et al.  Synthesis and thermochromic properties of vanadium dioxide colloidal particles , 2011 .

[12]  S. K. Bhaumik,et al.  Adsorption behaviour of polyvinyl pyrrolidone on oxide surfaces , 2000 .

[13]  Ok-Kyung Park,et al.  Synthesis of TiO 2 Nanoparticles Coated with SiO 2 for Suppression of Photocatalytic Activity and Increased Dispersion Stability , 2004 .

[14]  Yanfeng Gao,et al.  A novel solution process for the synthesis of VO2 thin films with excellent thermochromic properties. , 2009, ACS applied materials & interfaces.

[15]  F. Guinneton,et al.  Comparative study between nanocrystalline powder and thin film of vanadium dioxide VO2: electrical and infrared properties , 2001 .

[16]  Younan Xia,et al.  Hydrothermal Synthesis of Monoclinic VO2 Micro- and Nanocrystals in One Step and Their Use in Fabricating Inverse Opals , 2010 .

[17]  Feng Zhao,et al.  Reactive formation of zircon inclusion pigments by deposition and subsequent annealing of a zirconia and silica double shell. , 2009, Langmuir : the ACS journal of surfaces and colloids.

[18]  D. W. Sheel,et al.  Tungsten‐Doped Vanadium Oxides Prepared by Direct Liquid Injection MOCVD , 2007 .

[19]  F. J. Morin,et al.  Oxides Which Show a Metal-to-Insulator Transition at the Neel Temperature , 1959 .

[20]  F. Gan,et al.  Structure and optical property changes of sol‐gel derived VO2 thin films , 1997 .

[21]  J. Gavarri,et al.  Vanadium dioxide/polymer composites : thermochromic behaviour and modelling of optical transmittance , 1994 .

[22]  A. Blaaderen,et al.  Synthesis and Characterization of Monodisperse Core−Shell Colloidal Spheres of Zinc Sulfide and Silica , 2001 .

[23]  Ivan P. Parkin,et al.  Intelligent thermochromic windows , 2006 .

[24]  Rakel Wreland Lindström,et al.  Thin films of vanadium oxide grown on vanadium metal: oxidation conditions to produce V2O5 films for Li‐intercalation applications and characterisation by XPS, AFM, RBS/NRA , 2006 .