Healing of low-velocity impact damage in vascularised composites

Abstract This research has sought to characterise damage formation and self-healing efficiency within vascularised carbon fibre reinforced polymer (CFRP) laminates over a range of low velocity impact energies. Using ultrasonic C-scanning and compression after impact (CAI) analysis, vascularised laminates were shown to conform to the same damage size to residual compression strength relationship established for conventional laminates. The damage tolerance level of the host laminate was carefully determined, an important consideration in selection of the most appropriate vascule spacing for a reliable self-healing system. The healing functionality imparted full recovery of post impact compression strength over the range of impact energies tested (2.5–20 J), via healing of matrix cracking and delamination damage. The successful implementation of this technology could substantially enhance the integrity, reliability and robustness of composite structures, whilst offering benefits through reduced operational costs and extended lifetimes. However, establishing the benefits of such novel systems to existing design criteria is challenging, suggesting that bespoke design tools will be required to fully attain the potential benefits of self-healing technologies.

[1]  William F. Cole.  Technical justification of repairs to composite laminates , 1999 .

[2]  Ian P Bond,et al.  Self-healing sandwich panels: Restoration of compressive strength after impact , 2008 .

[3]  F. L. Matthews,et al.  A review of the strength of joints in fibre-reinforced plastics. Part 2. Adhesively bonded joints , 1982 .

[4]  Emile S. Greenhalgh,et al.  The assessment of novel materials and processes for the impact tolerant design of stiffened composite aerospace structures , 2003 .

[5]  S. Singh,et al.  Mixed-mode fracture in an interleaved carbon-fibre/epoxy composite , 1995 .

[6]  Robin Olsson,et al.  Impact on composite structures , 2004, The Aeronautical Journal (1968).

[7]  F. L. Matthews,et al.  A review of the strength of joints in fibre-reinforced plastics: Part 1. Mechanically fastened joints , 1980 .

[8]  Ian P Bond,et al.  Self‐Healing Fibre Reinforced Composites via a Bioinspired Vasculature , 2011 .

[9]  Jingshen Wu,et al.  Healing of impact damage in woven glass fabric reinforced epoxy composites , 2008 .

[10]  H. Razi,et al.  PRINCIPLES FOR ACHIEVING DAMAGE TOLERANT PRIMARY COMPOSITE AIRCRAFT STRUCTURES , 1996 .

[11]  R S Trask,et al.  Characterization and analysis of carbon fibre-reinforced polymer composite laminates with embedded circular vasculature , 2010, Journal of The Royal Society Interface.

[12]  Michael Mohaghegh,et al.  Evolution of Structures Design Philosophy and Criteria , 2004 .

[13]  S. Hayes,et al.  Self-healing of damage in fibre-reinforced polymer-matrix composites , 2007, Journal of The Royal Society Interface.

[14]  Ian P Bond,et al.  A probabilistic approach for design and certification of self-healing advanced composite structures , 2011 .

[15]  Ian P Bond,et al.  Interactions between propagating cracks and bioinspired self-healing vascules embedded in glass fibre reinforced composites , 2011 .

[16]  D. Hull,et al.  Damage mechanism characterization in composite damage tolerance investigations , 1993 .

[17]  A. Baker,et al.  Damage tolerance of graphite/epoxy composites , 1985 .

[18]  N. Sottos,et al.  Autonomic healing of polymer composites , 2001, Nature.

[19]  R S Trask,et al.  Bioinspired engineering study of Plantae vascules for self-healing composite structures , 2010, Journal of The Royal Society Interface.

[20]  Adrian P. Mouritz,et al.  Review of z-pinned composite laminates , 2007 .

[21]  R. Rao,et al.  Post Impact Compression Strength (PICS) Evaluation of Glass/Epoxy Composite Using a Novel Approach — Effect of Delamination Area , 2007 .

[22]  Constantinos Soutis,et al.  Structural health monitoring techniques for aircraft composite structures , 2010 .

[23]  Pedro P. Camanho,et al.  Effects of ply clustering in laminated composite plates under low-velocity impact loading , 2011 .

[24]  Puhui Chen,et al.  Damage Tolerance Analysis of Cracked Stiffened Composite Panels , 2001 .

[25]  Walter L. Bradley,et al.  Relating Resin Mechanical Properties to Composite Delamination Fracture Toughness , 1989 .

[26]  R S Trask,et al.  Self-healing polymer composites: mimicking nature to enhance performance , 2007, Bioinspiration & biomimetics.

[27]  Nancy R. Sottos,et al.  Autonomic healing of low-velocity impact damage in fiber-reinforced composites , 2009 .

[28]  M. Richardson,et al.  Review of low-velocity impact properties of composite materials , 1996 .

[29]  Ian P Bond,et al.  Compression after impact assessment of self-healing CFRP , 2009 .

[30]  Robin Olsson,et al.  Analytical prediction of large mass impact damage in composite laminates , 2001 .

[31]  Chun H. Wang,et al.  On the design methodology of scarf repairs to composite laminates , 2008 .

[32]  Ian P Bond,et al.  The Role Of Embedded Bioinspired Vasculature On Damage Formation In Self-Healing Carbon Fibre Reinforced Composites , 2011 .

[33]  Ian P Bond,et al.  Autonomous stimulus triggered self-healing in smart structural composites , 2012 .

[34]  Dahsin Liu,et al.  Repairability of Impact-Induced Damage in SMC Composites , 1993 .

[35]  John Morton,et al.  The impact resistance of composite materials — a review , 1991 .

[36]  Masaki Hojo,et al.  Modes I and II interlaminar fracture toughness and fatigue delamination of CF/epoxy laminates with self-same epoxy interleaf , 2006 .

[37]  I. Bond,et al.  A hollow fibre reinforced polymer composite encompassing self-healing and enhanced damage visibility , 2005 .

[38]  S. Sánchez-Sáez,et al.  Compression after impact of thin composite laminates , 2005 .

[39]  J. C. Prichard,et al.  The role of impact damage in post-impact compression testing , 1990 .

[40]  Ajit K. Mal,et al.  New Thermally Remendable Highly Cross-Linked Polymeric Materials , 2003 .

[41]  N. Sottos,et al.  Pressurized vascular systems for self-healing materials , 2012, Journal of The Royal Society Interface.