Magnetic Properties of Cobalt‐Samarium with a 24‐MG Oe Energy Product

The magnetic moment and hysteresis properties of a high‐density nearly completely oriented Co5Sm magnet alloy have been measured from 300 to 4.2 K and in applied fields up to 140 kOe. A saturation moment per gram of 98 G cm3/g is measured at 300 K and shows a slight increase as temperature is decreased. After adjustment for voids and oxide, the saturation moment per gram of the Co–Sm alloy is 102 G cm3/g, or equivalent to 11 000 G for the saturation magnetization 4πJs. An energy product of approximately 24 MG Oe is attained at 300 K.

[1]  Y. Fujimura,et al.  Preparation of Samarium Cobalt Permanent Magnet by Compacting with Solid Pressure Media , 1971 .

[2]  D. Martin,et al.  Measurement of magnetic properties of cobalt-rare earth permanent magnets , 1971 .

[3]  K. Strnat,et al.  SINTERING OF PrCo5 PERMANENT MAGNETS , 1971 .

[4]  H. Fujii,et al.  SATURATION MAGNETIC MOMENT AND CRYSTALLINE ANISOTROPY OF SINGLE CRYSTALS OF LIGHT RARE EARTH COBALT COMPOUNDS RCo5 , 1971 .

[5]  D. Martin,et al.  COBALT‐SAMARIUM PERMANENT MAGNETS PREPARED BY LIQUID PHASE SINTERING , 1970 .

[6]  D. Das,et al.  Twenty million energy product samarium-cobalt magnet , 1969 .

[7]  W. Luiten,et al.  High‐Energy‐Product Permanent Magnets , 1969 .

[8]  K. Buschow,et al.  Magnetic and Crystallographic Properties of Some Rare Earth Cobalt Compounds with CaZn5 Structure , 1968 .

[9]  Simon Foner,et al.  Very Low Frequency Integrating Vibrating Sample Magnetometer (VLFVSM) with High Differential Sensitivity in High dc Fields , 1968 .

[10]  G. Hoffer,et al.  A Family of New Cobalt‐Base Permanent Magnet Materials , 1967 .

[11]  R. Joseph,et al.  Ballistic Demagnetizing Factor in Uniformly Magnetized Cylinders , 1966 .

[12]  R. Sherwood,et al.  Magnetic Moments of Compounds of Cobalt with Rare-Earth Elements Having a Cu5Ca Structure , 1961 .

[13]  K. Nassau,et al.  Intermetallic compounds between lanthanons and transition metals of the first long period: I—Preparation, existence and structural studies☆☆☆ , 1960 .