Abstract Thin film composite (TFC) reverse osmosis membrane containing polyamide active layer on porous polysulfone support was developed at the scale of 1 m width × 100 m long in a batch using semi-automated mechanical casting and coating machines. The polysulfone support was made according to phase inversion method at the rate of 3−6 m/min., and the polyamide active layer on the polysulfone support was prepared by interfacial polymerization method at the rate of 0.3−0.5 m/min under different conditions. Since desalination of brackish water does not require the membrane with very high salt rejection efficiency, emphasis was placed on increase in the flux while maintaining the salt rejection at 94 ± 2%. The membrane preparation conditions and structure−performance relationships were correlated by different techniques like porometry, infrared spectra, scanning electron microscopy and atomic force microscopy. The TFC membranes exhibited 94−96% salt rejection with water flux of 50−65 L/m 2 .h when tested with 5000−1500 ppm salt solution at 250 psi. Surface modification of the TFC membrane with polymers containing hydrophilic groups was carried out to impart fouling resistance. Spiral modules of 4040 and 8040 size were made and tested them extensively in the field conditions in 500−2000 LPH brackish and sea water desalination plants.

[1]  V. Freger,et al.  TFC polyamide membranes modified by grafting of hydrophilic polymers: an FT-IR/AFM/TEM study , 2002 .

[2]  J. E. Cadotte,et al.  Interfacial Synthesis in the Preparation of Reverse Osmosis Membranes , 1981 .

[3]  V. Freger.  Kinetics of film formation by interfacial polycondensation. , 2005, Langmuir : the ACS journal of surfaces and colloids.

[4]  Huanting Wang,et al.  Recent developments in reverse osmosis desalination membranes , 2010 .

[5]  C. Bartels,et al.  Structure-performance relationships of composite membranes: Porous support densification , 1987 .

[6]  Yiming Cao,et al.  A novel method of surface modification on thin-film composite reverse osmosis membrane by grafting poly(ethylene glycol) , 2007 .

[7]  T. Matsuura,et al.  Surface modifications for antifouling membranes. , 2010, Chemical reviews.

[8]  P. R. Buch,et al.  Preparation, characterization and chlorine stability of aromatic–cycloaliphatic polyamide thin film composite membranes , 2008 .

[9]  Masaru Kurihara,et al.  Development of crosslinked fully aromatic polyamide ultra-thin composite membranes for seawater desalination , 1994 .

[10]  J. E. Cadotte,et al.  A new thin-film composite seawater reverse osmosis membrane , 1980 .

[11]  W. Krantz,et al.  Formation and Characterization of Polyamide Membranes via Interfacial Polymerization , 1994 .

[12]  Il Juhn Roh,et al.  Investigation of the specific role of chemical structure on the material and permeation properties of ultrathin aromatic polyamides , 2002 .

[13]  S. A. Sundet.  Morphology of the rejecting surface of aromatic polyamide membranes for desalination , 1993 .

[14]  R. Rangarajan,et al.  Interfacially synthesized thin film composite RO membranes for seawater desalination , 1997 .

[15]  T. Matsuura,et al.  Development of antifouling thin-film-composite membranes for seawater desalination , 2011 .

[16]  O. Kedem,et al.  Surface modification of commercial composite polyamide reverse osmosis membranes , 1998 .

[17]  A. Ahmad,et al.  Preparation and characterization of co-polyamide thin film composite membrane from piperazine and 3,5-diaminobenzoic acid , 2003 .

[18]  S. V. Joshi,et al.  Fouling resistant membranes in desalination and water recovery , 2005 .

[19]  T. Matsuura,et al.  Preparation of thin-film-composite polyamide membranes for desalination using novel hydrophilic surface modifying macromolecules , 2008 .

[20]  A. Greenberg,et al.  Synthesis and characterization of interfacially polymerized polyamide thin films , 2006 .

[21]  Paul W. Morgan,et al.  Condensation polymers: by interfacial and solution methods , 1965 .

[22]  S. V. Joshi,et al.  CSMCRI experience with reverse osmosis membranes and desalination: case studies** , 2004 .

[23]  Eric M.V. Hoek,et al.  Impacts of reaction and curing conditions on polyamide composite reverse osmosis membrane properties , 2008 .

[24]  R. Rangarajan,et al.  Development of fabric reinforced polysulfone membranes , 1991 .

[25]  T. Arnot,et al.  A review of reverse osmosis membrane materials for desalinationDevelopment to date and future poten , 2011 .

[26]  A. Reddy.  Synthesis and characterization of poly(amide–imide)s and their precursors as materials for membranes , 2000 .

[27]  Yujun Song,et al.  Mechanisms of structure and performance controlled thin film composite membrane formation via interfacial polymerization process , 2005 .

[28]  B. McCarry,et al.  Polysulfonamide thin-film composite reverse osmosis membranes , 1998 .

[29]  S. V. Joshi,et al.  A case study of long-term RO plant operation without chemical pretreatment , 2004 .

[30]  Jong-Gyu Kim,et al.  The changes of membrane performance with polyamide molecular structure in the reverse osmosis process , 2000 .

[31]  Viatcheslav Freger,et al.  Nanoscale Heterogeneity of Polyamide Membranes Formed by Interfacial Polymerization , 2003 .

[32]  S. V. Joshi,et al.  Probing the structural variations of thin film composite RO membranes obtained by coating polyamide over polysulfone membranes of different pore dimensions , 2006 .

[33]  R. J. Petersen,et al.  Composite reverse osmosis and nanofiltration membranes , 1993 .

[34]  S. D. Arthur.  Structure-property relationship in a thin film composite reverse osmosis membrane , 1989 .

[35]  R. L. Riley,et al.  Transport properties of cellulose acetate osmotic membranes , 1965 .

[36]  C. K. Kim,et al.  Effects of the polyamide molecular structure on the performance of reverse osmosis membranes , 1998 .

[37]  C. V. Devmurari,et al.  Structure–performance correlation of polyamide thin film composite membranes: effect of coating conditions on film formation , 2003 .

[38]  Zhou Yong,et al.  Polyamide thin film composite membrane prepared from m-phenylenediamine and m-phenylenediamine-5-sulfonic acid , 2006 .