Cross-linked graphene layer embedded carbon film prepared using electron irradiation in ECR plasma sputtering

Abstract A new path to prepare cross-linked graphene layers embedded carbon (GLEC) films has been reported by introducing electron irradiation during the mirror-confinement electron cyclotron resonance (ECR) plasma sputtering process. The electron irradiation in the ECR plasma was identified by using Langmuir single probe equipped with a designed simulated substrate and the irradiation mode was found to be controlled directly by altering the substrate bias voltage. Cross-linked GLEC film was prepared using the electron irradiation in the pressure of 0.04 Pa and positive bias voltage of 50 V, and the nanostructure and binding configuration of the film were analyzed by high resolution transmission electron microscope (HRTEM) and X-ray photoelectron spectroscopy (XPS). The results showed that GLEC film contains cross-linked graphene layers grown normally to the substrate surface when the content of sp2 hybridized carbon atoms in the film is more than 70%. The tribological behaviors of both cross-linked GLEC films and amorphous carbon films were compared using a Pin-on-Disk tribometer, and the mechanism for low friction coefficient was discussed by using HRTEM observation on wear track. The HRTEM results indicated that the cross-linked GLEC film has the potential to achieve low friction at the beginning of the friction.

[1]  Y. Liu,et al.  Influence of environmental parameters on the frictional behavior of DLC coatings , 1997 .

[2]  A. Erdemir,et al.  Solid Lubricant Coatings: Recent Developments and Future Trends , 2004 .

[3]  I. L. Singer,et al.  Role of the Transfer Film on the Friction and Wear of Metal Carbide Reinforced Amorphous Carbon Coatings During Run-in , 2009 .

[4]  D. Mckenzie,et al.  The structural phases of non-crystalline carbon prepared by physical vapour deposition , 2009 .

[5]  I. Alexandrou,et al.  Carbon films with a novel sp2 network structure , 1999, cond-mat/9905130.

[6]  Shui-Tong Lee,et al.  Study of tribological performance of ECR-CVD diamond-like carbon coatings on steel substrates: Part 1. The effect of processing parameters and operating conditions , 2005 .

[7]  K. Matsuda,et al.  Electronic properties of super-hard carbon nanocrystallite film , 2003 .

[8]  Y. Liu,et al.  An investigation of the relationship between graphitization and frictional behavior of DLC coatings , 1996 .

[9]  R. Kaneko,et al.  Superhard conductive carbon nanocrystallite films , 2002 .

[10]  A. Grill,et al.  How to restore superlow friction of DLC: the healing effect of hydrogen gas , 2004 .

[11]  S. Lau,et al.  Thermally induced sp2 clustering in tetrahedral amorphous carbon (ta-C) films , 2004 .

[12]  A. Erdemir,et al.  Tribology of diamond-like carbon films , 2008 .

[13]  John B. Shoven,et al.  I , Edinburgh Medical and Surgical Journal.

[14]  A. Grill,et al.  The respective role of oxygen and water vapor on the tribology of hydrogenated diamond-like carbon coatings , 1998 .

[15]  Ali Erdemir,et al.  A study of the wear mechanism of diamond-like carbon films , 1996 .

[16]  Andrew G. Glen,et al.  APPL , 2001 .

[17]  A. Grill,et al.  Tribochemistry between hydrogen and diamond-like carbon films , 2001 .

[18]  Chang-long Cai,et al.  Carbon films deposited by MCECR plasma sputtering , 2006 .

[19]  A. Erdemir,et al.  Tribology of diamond-like carbon films : fundamentals and applications , 2008 .

[20]  A. Erdemir,et al.  Friction-induced structural transformations of diamondlike carbon coatings under various atmospheres , 2003 .

[21]  B. Tay,et al.  Abrupt stress induced transformation in amorphous carbon films with a highly conductive transition phase. , 2008, Physical review letters.