A Small-Angle X-ray Scattering Study of the Structure of Aqueous Laponite Dispersions

Two Laponite clays, of general formula [Mn+]x/n [Lix Mg6-x Si8 O20 Fy (OH)4-y], were prepared with different Li+ levels (0.57 and 0.70% w/w) and F- levels (9.5 and 9.9% w/w). The clays were characterized by measurements of nitrogen adsorption isotherms, cation exchange capacity, and conductometric titration data. The clay with higher Li+ and F- levels had a higher (more negative) face charge and a lower (less negative) edge charge. Small-angle X-ray scattering (SAXS) data obtained from dilute aqueous dispersions indicate that both clays are of similar particle size (diameter ca. 40 nm and thickness ca. 3.5 nm). Experimental structure factors for concentrated Laponite dispersions were calculated using the ratio of scattered X-ray intensities from concentrated and dilute dispersions. Maxima in the experimental structure factors were observed at scattering angles of 0.14−0.2 nm-1 under favorable solution conditions (pH ≥ 9 and ionic strength ca. 5 × 10-3 mol dm-3) for one of the Laponite clays. These results...