Field emission of electrons by carbon nanotube twist-yarns

Field emission with high current density at low operating voltage was found for the yarns obtained by solid state spinning process from forest of vertically aligned multiwall carbon nanotubes. The nanotube forest was produced catalytically by CVD method. It is found that only a small fraction of carbon nanotubes from their total amount in the yarn yields to electron emission from its free end. This led to resistive heating of the emitting tubes and limiting of the emission current. The field emission microscopy pictures of MWNT yarn in free-end geometry appears to be very different from that of the conventional non-yarn carbon nanotube-based cathodes described in all previous studies. The FEM patterns are found to consist of the set of line and arc segments rather than a set of spots. Possible explanation of this effect is presented and discussed. The field emission from the lateral side of the yarns showed the self-enhanced currents increasing with operation time. We assume that this current increase may be due to untwisting and unwrapping of yarns resulted of application of the electric field. The lowest threshold field of about 0.7 V/μm was obtained after a few cycles of applied field increase. The prototypes of cathodoluminescent lamps and alphanumerical indicators based on MWNT twist-yarn cold cathodes are demonstrated.

[1]  C. Journet,et al.  Modelization of resistive heating of carbon nanotubes during field emission , 2002 .

[2]  Vu Thien Binh,et al.  Hot nanotubes: stable heating of individual multiwall carbon nanotubes to 2000 k induced by the field-emission current. , 2002, Physical review letters.

[3]  H. Dai,et al.  Self-oriented regular arrays of carbon nanotubes and their field emission properties , 1999, Science.

[4]  Sashiro Uemura,et al.  Field emission of carbon nanotubes and its application as electron sources of ultra-high luminance light-source devices , 2002 .

[5]  Riichiro Saito,et al.  Electronic structure of chiral graphene tubules , 1992 .

[6]  K. R. Atkinson,et al.  Multifunctional Carbon Nanotube Yarns by Downsizing an Ancient Technology , 2004, Science.

[7]  John Robertson,et al.  Growth process conditions of vertically aligned carbon nanotubes using plasma enhanced chemical vapor deposition , 2001 .

[8]  R. Gomer,et al.  Field Emission and Field Ionization , 1961 .

[9]  L. Forró,et al.  Field emission from carbon nanotubes: perspectives for applications and clues to the emission mechanism , 1999 .

[10]  P. Gustafson.  An evaluation of the thermodynamic properties and the P, T phase diagram of carbon , 1986 .

[11]  G. V. Torgashov,et al.  Field emitter arrays on nanotube carbon structure films , 1995 .

[12]  Kunio Uchida,et al.  Conical beams from open nanotubes , 1997, Nature.

[13]  Mei Zhang,et al.  Spark light radiation coupled with the field electron emission from carbon nanotube forests , 2006 .

[14]  K. Jiang,et al.  Efficient fabrication of field electron emitters from the multiwalled carbon nanotube yarns , 2006 .

[15]  P. Nordlander,et al.  Unraveling Nanotubes: Field Emission from an Atomic Wire , 1995, Science.

[16]  G. V. Torgashov,et al.  Electron field emission from nanofilament carbon films , 1995 .

[17]  E. Campbell,et al.  Electron field emission from multi-walled carbon nanotubes , 2004 .

[18]  Jun Chen,et al.  Mechanism responsible for initiating carbon nanotube vacuum breakdown. , 2004, Physical review letters.

[19]  Kenneth A. Dean,et al.  The environmental stability of field emission from single-walled carbon nanotubes , 1999 .

[20]  Y. Lamy,et al.  High brightness electron beam from a multi-walled carbon nanotube , 2002, Nature.

[21]  A. Zakhidov,et al.  Field emission characteristics of nanostructured thin film carbon materials , 2003 .

[22]  A. Dinsdale.  SGTE data for pure elements , 1991 .