Spent limestone sorbent from calcium looping cycle as a raw material for the cement industry

Abstract It has been found that a spent limestone sorbent, coming from a pilot-scale calcium looping fluidized bed (CaL-FB) plant and purged after 60 cycles of calcination and carbonation, can be successfully employed in the Portland cement clinker manufacture in place of natural limestone. Laboratory measurements showed that the burnability index for a clinker-generating raw mixture consisting of commercial clay and the exhausted sorbent was better than that of a reference mixture containing the same clay and fresh limestone. The results of the burnability test were confirmed by (i) the mineralogical composition data on the synthetic clinkers obtained from both raw mixtures at 1500 °C and (ii) the hydration rate of the related Portland cements, evaluated by means of X-ray diffraction analysis and simultaneous differential thermal-thermogravimetric analysis, respectively. Preliminary and novel results reported in this communication show that the utilization of the spent limestone sorbent as a raw material for making cement can have a very favorable effect not only on the economics of the CaL-FB process, but also on the cement manufacture in terms of (i) reduced generation of carbon dioxide and pollutants, (ii) saving of raw materials and fuel, (iii) decreased flow rate of gaseous emissions.

[1]  P. Fennell,et al.  Investigation into potential synergy between power generation, cement manufacture and CO2 abatement using the calcium looping cycle , 2011 .

[2]  Ajay R. Bidwe,et al.  Parametric investigation of the calcium looping process for CO2 capture in a 10kWth dual fluidized bed , 2010 .

[3]  N Rodríguez,et al.  Process for capturing CO2 arising from the calcination of the CaCO3 used in cement manufacture. , 2008, Environmental science & technology.

[4]  Fabio Montagnaro,et al.  Fluidized bed calcium looping: The effect of SO2 on sorbent attrition and CO2 capture capacity , 2012 .

[5]  Paul S. Fennell,et al.  The calcium looping cycle for large-scale CO2 capture , 2010 .

[6]  T. Shimizu,et al.  A twin fluid-bed reactor for removal of CO2 from combustion processes , 1999 .

[7]  John E. Oakey,et al.  CO2 Capture Technologies for Cement Industry , 2009 .

[8]  Robin W. Hughes,et al.  Ca-based sorbent looping combustion for CO2 capture in pilot-scale dual fluidized beds , 2008 .

[9]  Fabio Montagnaro,et al.  Utilization of Coal Combustion Ashes for the Synthesis of Ordinary and Special Cements , 2010 .

[10]  Fabio Montagnaro,et al.  Reactivation by water hydration of the CO2 capture capacity of a calcium looping sorbent , 2014 .

[11]  Luis M. Romeo,et al.  Reduction of greenhouse gas emissions by integration of cement plants, power plants, and CO2 capture systems , 2011 .

[12]  E. J. Anthony,et al.  Fluidized bed combustion systems integrating CO2 capture with CaO. , 2005, Environmental science & technology.

[13]  E. J. Anthony,et al.  Capture of CO2 from combustion gases in a fluidized bed of CaO , 2004 .

[14]  Graziella Bernardo,et al.  The use of oil well-derived drilling waste and electric arc furnace slag as alternative raw materials in clinker production , 2007 .

[15]  Fabio Montagnaro,et al.  Fluidized bed calcium looping cycles for CO2 capture under oxy-firing calcination conditions: Part 2. Assessment of dolomite vs. limestone , 2013 .

[16]  T. Naik,et al.  Use of FBC bottom ash as a raw material for the synthesis of low-CO2 cements , 2012 .

[17]  Adolfo Garza,et al.  CO2 capture and sequestration in the cement industry , 2011 .