An experimental study of impact-induced failure events in homogeneous layered materials using dynamic photoelasticity and high-speed photography

Abstract The generation and the subsequent evolution of dynamic failure events in homogeneous layered materials that occur within microseconds after impact were investigated experimentally. Tested configurations include three-layer and two-layer, bonded Homalite specimens featuring different bonding strengths. High-speed photography and dynamic photoelasticity were utilized to study the nature, sequence and interaction of failure modes. A series of complex failure modes was observed. In most cases, and at the early stages of the impact event, intra-layer failure (or bulk matrix failure) appeared in the form of cracks radiating from the impact point. These cracks were opening-dominated and their speeds were less than the crack branching speed of the Homalite. Subsequent crack branching in several forms was also observed. Mixed-mode inter-layer cracking (or interfacial debonding) was initiated when the intra-layer cracks approached the interface with a large incident angle. The dynamic interaction between inter-layer crack formation and intra-layer crack growth (or the so-called “Cook–Gordon Mechanism”) was visualized for the first time. Interfacial bonding played a significant role in impact damage spreading. Cracks arrested at weak bonds and the stress wave intensity was reduced dramatically by the use of a thin but ductile adhesive layer.

[1]  Ares J. Rosakis,et al.  Impact failure characteristics in sandwich structures: Part I: Basic failure mode selection , 2002 .

[2]  A. Rosakis,et al.  Cracks faster than the shear wave speed , 1999, Science.

[3]  Philippe H. Geubelle,et al.  Intersonic crack propagation in homogeneous media under shear-dominated loading: Theoretical analysis , 2001 .

[4]  J. W. Dally,et al.  A photoelastic analysis of stress wave propagation in a layered model , 1966 .

[5]  Serge Abrate,et al.  Impact on Laminated Composites: Recent Advances , 1994 .

[6]  Ares J. Rosakis,et al.  Dynamic crack deflection and penetration at interfaces in homogeneous materials: experimental studies and model predictions , 2003 .

[7]  J. Dally.  Dynamic photoelastic studies of fracture , 1979 .

[8]  L. E. Malvern,et al.  Delamination-crack propagation in ballistically impacted glass/epoxy composite laminates , 1982 .

[9]  Z. Suo,et al.  Mixed mode cracking in layered materials , 1991 .

[10]  Said Rechak,et al.  Effect of Adhesive Layers on Impact Damage in Composite Laminates , 1988 .

[11]  Their Composites,et al.  Composite Materials: Testing and Design (Eighth Conference) , 1988 .

[12]  Gao,et al.  How fast can cracks propagate? , 2000, Physical review letters.

[13]  Alan Needleman,et al.  An analysis of intersonic crack growth under shear loading , 1999 .

[14]  S. Mall,et al.  Dynamic fracture toughness of Homalite-100 , 1978 .

[15]  Albert S. Kobayashi,et al.  Mechanics of crack curving and branching — a dynamic fracture analysis , 1985 .

[16]  Horacio Dante Espinosa,et al.  A Novel Technique for Penetrator Velocity Measurement and Damage Identification in Ballistic Penetration Experiments , 1998 .

[17]  Ares J. Rosakis,et al.  Intersonic shear crack growth along weak planes , 2000 .

[18]  Ares J. Rosakis,et al.  Subsonic and intersonic shear rupture of weak planes with a velocity weakening cohesive zone , 2002 .

[19]  J. E. Gordon,et al.  The New Science of Strong Materials , 1975 .

[20]  Danilo De Rossi,et al.  Cracks Faster than the Shear Wave Speed , 2022 .

[21]  K. Ravi-Chandar,et al.  An experimental investigation into dynamic fracture: III. On steady-state crack propagation and crack branching , 1984 .