Effects of CO2 laser conditioning of the antireflection Y2O3/SiO2 coatings at 351 nm

Y2O3/SiO2 coatings were deposited on fused silica by electron beam evaporation. A continuous wave CO2 laser was used to condition parts of the prepared samples at different scanning speeds in the air. LAMBDA 900 spectrometer was used to investigate the changes of the transmittance and residual reflection spectrum. A Nomarski microscope under dark field was used to examine the changes of the micro defect density. The changes of the surface roughness and the microstructure of the film before and after conditioning were investigated by AFM and X-ray diffraction, respectively. We found that laser-induced damage threshold (LIDT) of the films conditioning at 30 mm/s scanning speed was increased by more than a factor of 3 over the thresholds of the as-deposited films. The conditioning effect was correlated with an irradiation-induced decrease of the defect density and absorption of the films. (c) 2005 Elsevier B.V. All rights reserved.

[1]  W H Wang,et al.  Annealing effect on ion-beam-sputtered titanium dioxide film. , 1998, Optics letters.

[2]  J. O. Porteus,et al.  Infrared laser‐induced desorption of H2O and hydrocarbons from optical surfaces , 1982 .

[3]  Ea Teppo,et al.  Temporary laser damage threshold enhancement by laser conditioning of antireflection‐coated glass , 1987 .

[4]  Joseph A. Menapace,et al.  UV-laser conditioning for reduction of 351-nm damage initiation in fused silica , 2002, SPIE Laser Damage.

[5]  R. Wolf,et al.  Effect of the substrate preparation with CO2 laser radiation on the laser resistance of optical layers , 1986 .

[6]  Mark R. Kozlowski,et al.  Large-area conditioning of optics for high-power laser systems , 1994, Laser Damage.

[7]  Michael J. Runkel,et al.  Results of raster-scan laser conditioning studies on DKDP triplers using Nd:YAG and excimer lasers , 2002, SPIE Laser Damage.

[8]  Z. Fan,et al.  Surface inclusion adhesion of optical coatings , 1994 .

[9]  Jianda Shao,et al.  Evolutions of residual stress and microstructure in ZrO2 thin films deposited at different temperatures and rates , 2003 .

[10]  Jianda Shao,et al.  Annealing effects on structure and laser-induced damage threshold of Ta2O5/SiO2 dielectric mirrors , 2003 .

[11]  Herve Bercegol,et al.  What is laser conditioning: a review focused on dielectric multilayers , 1999, Laser Damage.

[12]  D Milam,et al.  Carbon dioxide laser polishing of fused silica surfaces for increased laser-damage resistance at 1064 nm. , 1982, Applied optics.