Effect of high strain rate on plastic deformation of a low alloy steel subjected to ballistic impact

Abstract Some results of an experimental study on high strain rate deformation of a low alloy steel are discussed in this paper. Cylindrical specimens of the steel in quench-hardened and tempered condition were subjected to high strain rate deformation by direct impact using a modified Split Hopkinson Pressure Bar (SHPB). The deformation process is dominated by stress collapse due to thermal softening effect of adiabatic heating in some narrow bands within the material under deformation. The time for the onset of the stress collapse leading to strain localization was found to increase with strain rate. The critical strain at which adiabatic shearing occurs depends on the strain rate and microstructure. Steel samples that were tempered at 425 °C exhibits greater tendency to adiabatic shearing than those tempered at 315 °C. The time and critical strain for the onset of stress collapse and adiabatic shearing are lower. Whereas single white adiabatic shear bands were observed to initiate and propagate during the high strain rate deformation in samples tempered at 315 °C, multiple shear bands were found to initiate and dynamically propagate in the samples tempered at 425 °C. Of these multiple shear bands, the one closest to the centre of the cylindrical test pieces were white etching bands while the rest appeared as deformed bands. The higher tendency of the samples tempered at 425 °C to formation of adiabatic shear bands has been attributed to increased perturbation in the steel samples as a result of the heat treatment procedure. The type of shear bands formed in the steel at high strain-rates can be explained as due to the accompanying fragmentation of martensite laths and dissolution of carbides during adiabatic heating and shearing, which eventually determines the size of the micro-constituents of the adiabatic shear band and the resolvability by optical microscopy.

[1]  J. Duffy,et al.  An experimental study of the formation process of adiabatic shear bands in a structural steel , 1988 .

[2]  Lynn Seaman,et al.  Development and Application of a Computational Shear Band Model. , 1980 .

[3]  Z. H. Chen,et al.  An investigation on the formation and propagation of shear band in fine-blanking process , 2003 .

[4]  I. Hutchings,et al.  The structure of adiabatic shear bands in a titanium alloy , 1985 .

[5]  M. Meyers,et al.  Effect of metallurgical parameters on shear band formation in low-carbon (∼0.20 Wt Pct) steels , 1990 .

[6]  M. Meyers,et al.  Self-organization in the initiation of adiabatic shear bands , 1998 .

[7]  J. Yu,et al.  Influence of specimen geometry on adiabatic shear instability of tungsten heavy alloys , 2002 .

[8]  M. N. Raftenberg,et al.  Metallographic observations of armor steel specimens from plates perforated by shaped charge jets , 1999 .

[9]  K. T. Ramesh,et al.  Localization of shearing deformations in tungsten heavy alloys , 1994 .

[10]  J. H. Hollomon,et al.  Effect of Strain Rate Upon Plastic Flow of Steel , 1944 .

[11]  M. Bassim,et al.  Characterization of the compression properties of rail steels at high temperatures and strain rates , 1991 .

[12]  J. Derep.  Microstructure transformation induced by adiabatic shearing in armour steel , 1987 .

[13]  Gerry Byrne,et al.  TEM study on the surface white layer in two turned hardened steels , 2002 .

[14]  M. Bassim.  Study of the formation of adiabatic shear bands in steels , 2001 .

[15]  M. Meyers,et al.  Self-organization of shear bands in titanium and Ti–6Al–4V alloy , 2002 .

[16]  W. C. Leslie,et al.  The nature of “white streaks” in impacted steel armor plate , 1971 .

[17]  U. S. Lindholm,et al.  Shock Wave and High-Strain-Rate Phenomena in Materials , 1992 .

[18]  H. Ockendon,et al.  A scaling law for the effect of inertia on the formation of adiabatic shear bands , 1996 .

[19]  J. Duffy,et al.  Measurement of the temperature profile during shear band formation in steels deforming at high strain rates , 1987 .

[20]  H. Rogers,et al.  Material Factors in Adiabatic Shearing in Steels , 1981 .

[21]  M. Bassim,et al.  Dynamic mechanical properties in relation to adiabatic shear band formation in titanium alloy-Ti17 , 2003 .

[22]  J. W. Walter,et al.  On stress collapse in adiabatic shear bands , 1987 .

[23]  J. Duffy,et al.  On the measurement of local strain and temperature during the formation of adiabatic shear bands , 1992 .

[24]  S. E. Schoenfeld,et al.  A failure criterion based on material instability , 2003 .

[25]  S. Nutt,et al.  Adiabatic shear band formation during dynamic torsional deformation of an HY-100 steel , 1993 .

[26]  M. Bassim,et al.  Finite element modeling of the formation of adiabatic shear bands in AISI 4340 steel , 1999 .

[27]  P. Thornton,et al.  Observations on adiabatic shear zones in explosively loaded thick-wall cylinders , 1971, Metallurgical Transactions.

[28]  A. Zurek.  The study of adiabatic shear band instability in a pearlitic 4340 steel using a dynamic punch test , 1994 .

[29]  Marc A. Meyers,et al.  Observation of an adiabatic shear band in AISI 4340 steel by high-voltage transmission electron microscopy , 1990 .

[30]  D. Grady,et al.  The growth of unstable thermoplastic shear with application to steady-wave shock compression in solids* , 1987 .