Fracture of solid state laser slabs

Fracture due to thermal stress limits the power output potential of modern, high average power slab lasers. Here the criteria for slab fracture and the nature of the surface flaws which constitute the strength‐controlling defects are reviewed. Specific fracture data for gadolinium scandium gallium garnet and LHG‐5 phosphate glass with different surface finishes are evaluated in the context of assigning appropriate slab operating parameters using Wiebull statistics. These examples illustrate both the danger of design using brittle components without adequate fracture testing, and the inadequacy of design methods which use a fixed safety factor, for this class of materials. Further consideration reveals that operation of slab lasers in contact with an aqueous coolant may lead to strength degradation with time. Finally, the evolution of the failure process in which a characteristic midplane crack forms is outlined, and the pertinent parameters for avoiding slab fracture are identified.