Development of biomechanical properties and morphogenesis of in vitro tissue engineered cartilage.

Neocartilage was engineered by culturing bovine chondrocytes on poly(glycolic acid) (PGA) fibrous nonwoven scaffolds. The biomechanical properties and morphologies of the PGA-chondrocyte constructs were studied over 12 weeks of in vitro culture. PGA scaffolds without cells lost their mechanical strength and structural integrity between week 2 and week 3 in culture. The thickness of the PGA-chondrocyte constructs decreased by 35% during the first 3 weeks, but the thickness increased from week 3 to week 9 to a thickness 42% higher than that of the starting scaffolds, which was then maintained. Safranin O staining of PGA-chondrocyte constructs revealed increasing proteoglycan formation over time. The compressive modules of PGA-chondrocyte constructs increased with in vitro culture time, and reached the same order of magnitude as that of normal bovine cartilage at week 9. The aggregate modulus of the PGA-chondrocyte constructs decreased by 57% over the first 2 weeks but then increased, reaching the same order of magnitude as normal bovine cartilage at week 12. The apparent permeability of the PGA-chondrocyte constructs, which was initially four orders of magnitude above that of normal cartilage, decreased between weeks 1 and 3 and thereafter remained the same order of magnitude as that measured for normal cartilage.

[1]  R Langer,et al.  Neocartilage formation in vitro and in vivo using cells cultured on synthetic biodegradable polymers. , 1993, Journal of biomedical materials research.

[2]  R Langer,et al.  Selective cell transplantation using bioabsorbable artificial polymers as matrices. , 1988, Journal of pediatric surgery.

[3]  V. C. Mow,et al.  Biphasic and Quasilinear Viscoelastic Theories for Hydrated Soft Tissues , 1990 .

[4]  David J. Mooney,et al.  Tissue engineering using cells and synthetic polymers , 1993 .

[5]  J. Vacanti,et al.  Tissue engineering : Frontiers in biotechnology , 1993 .

[6]  J. Vacanti,et al.  Tissue-engineered growth of bone and cartilage. , 1993, Transplantation proceedings.

[7]  J. Vacanti,et al.  Joint Resurfacing with Cartilage Grown in Situ from Cell-Polymer Structures , 1994, The American journal of sports medicine.

[8]  J. Vacanti,et al.  Tissue Engineering Using Synthetic Biodegradable Polymers , 1993 .

[9]  W M Lai,et al.  A finite deformation theory for cartilage and other soft hydrated connective tissues--I. Equilibrium results. , 1990, Journal of biomechanics.

[10]  V. Mow,et al.  Biphasic creep and stress relaxation of articular cartilage in compression? Theory and experiments. , 1980, Journal of biomechanical engineering.

[11]  Holly M. Brown-Borg,et al.  Culture of Animal Cells: A Manual of Basic Technique, R. Ian Freshney (Ed.). Wiley-Liss, Inc., New York (1994) , 1995 .

[12]  R Langer,et al.  Tissue engineering by cell transplantation using degradable polymer substrates. , 1991, Journal of biomechanical engineering.

[13]  J. Vacanti,et al.  Generation of neo-tendon using synthetic polymers seeded with tenocytes. , 1994, Transplantation proceedings.

[14]  T Ochi,et al.  Repair of rabbit articular surfaces with allograft chondrocytes embedded in collagen gel. , 1989, The Journal of bone and joint surgery. British volume.

[15]  R Langer,et al.  Joint resurfacing using allograft chondrocytes and synthetic biodegradable polymer scaffolds. , 1994, Journal of biomedical materials research.

[16]  R Langer,et al.  Kinetics of chondrocyte growth in cell‐polymer implants , 1994, Biotechnology and bioengineering.

[17]  G. Vunjak‐Novakovic,et al.  Composition of cell‐polymer cartilage implants , 1994, Biotechnology and bioengineering.

[18]  G. Vunjak‐Novakovic,et al.  Cultivation of cell‐polymer cartilage implants in bioreactors , 1993, Journal of cellular biochemistry.

[19]  Robert Langer,et al.  Biodegradable Polymer Scaffolds for Tissue Engineering , 1994, Bio/Technology.

[20]  Mark H. Holmes.  A nonlinear diffusion equation arising in the study of soft tissue , 1983 .

[21]  J. Vacanti,et al.  Formation of urothelial structures in vivo from dissociated cells attached to biodegradable polymer scaffolds in vitro. , 1992, The Journal of urology.

[22]  John Paul,et al.  Tissue culture: Methods and applications: Ed. by Paul F. Kruse, Jr and M. K. Patterson, Jr. 1973. New York and London: Academic Press. Pp. xxvii and 868; 264 text figs. £10.15. , 1974 .

[23]  R Langer,et al.  Design and Fabrication of Biodegradable Polymer Devices to Engineer Tubular Tissues , 1994, Cell transplantation.

[24]  J. Vacanti,et al.  Delivery of whole liver-equivalent hepatocyte mass using polymer devices and hepatotrophic stimulation. , 1993, Transplantation.

[25]  S. Woo,et al.  Histological and biomechanical assessment of articular cartilage from stored osteochondral shell allografts , 1989, Journal of orthopaedic research : official publication of the Orthopaedic Research Society.

[26]  J. Vacanti,et al.  Synthetic Polymers Seeded with Chondrocytes Provide a Template for New Cartilage Formation , 1991, Plastic and reconstructive surgery.

[27]  V C Mow,et al.  The biphasic poroviscoelastic behavior of articular cartilage: role of the surface zone in governing the compressive behavior. , 1993, Journal of biomechanics.

[28]  L. Rosenberg.  Chemical basis for the histological use of safranin O in the study of articular cartilage. , 1971, The Journal of bone and joint surgery. American volume.

[29]  V C Mow,et al.  Variations in the intrinsic mechanical properties of human articular cartilage with age, degeneration, and water content. , 1982, The Journal of bone and joint surgery. American volume.

[30]  C. Ohlsson,et al.  Treatment of deep cartilage defects in the knee with autologous chondrocyte transplantation. , 1994, The New England journal of medicine.

[31]  J. Steadman,et al.  Future directions. Collagen-based prostheses for meniscal regeneration. , 1990, Clinical orthopaedics and related research.