Preparation of multiphase block copolymers by redox polymerization process

SUMMARY Redox polymerization of methylmethacrylate (MMA) using Ce(1V) with poly(oxyethylene) having azo and hydroxy functions was carried out to yield methylmethacrylate-ethylene glycol block copolymers with labile azo linkages in the main chain. These prepolymers were used to initiate the radical polymerization of styrene through the thermal decomposition of the azo group, resulting in the formation of multiblock copolymers. Successful blocking has been confirmed by fractional precipitation, a strong change in the molecular weight distribution and spectral measurements. ZUSAMMENFASSUNG: Durch Ce(1V)-initiierte Redoxpolymerisation von Methylmethacrylat mit Poly(oxyethylen), das Azo- und Hydroxygruppen enthielt, wurden Copolymere mit labilen Azogruppen in der Hauptkette erhalten. Diese Prepolymeren wurden zur durch thermischen Zerfall der Azogruppen initiierten radikalischen Polymerisation von Styrol eingesetzt, wobei Multiblockcopolymere entstanden, was durch fraktionierte Filllung, Anderung der Molekulargewichtsverteilung und spektroskopische Messungen nachgewiesen wurde.