NiO/Al2O3 oxygen carriers for chemical-looping combustion prepared by impregnation and deposition-precipitation methods

Abstract Ni-based oxygen carriers (OC) with different NiO content were prepared by incipient wet impregnation, at ambient (AI), and hot conditions (HI) and by deposition–precipitation (DP) methods using γ-Al 2 O 3 and α-Al 2 O 3 as supports. The OC were characterized by BET, Hg porosimetry, mechanical strength, TPR, XRD and SEM/EDX techniques. Reactivity of the OC was measured in a thermogravimetric analyzer and methane combustion selectivity towards CO 2 and H 2 O, attrition rate, and agglomeration behavior were analyzed in a batch fluidized bed reactor during multicycle reduction–oxidation tests. XRD and TPR analysis showed the presence of both free NiO and NiAl 2 O 4 phases in most of the OC. The interaction of the NiO with the alumina during OC preparation formed NiAl 2 O 4 that affected negatively to the OC reactivity and methane combustion selectivity towards CO 2 and H 2 O during the reduction reaction. The NiO–alumina interaction was more affected by the support type than by the preparation method used. The NiO–alumina interaction was stronger in the OC prepared on γ-Al 2 O 3 . The OC were evaluated in the fluidized bed reactor with respect to the agglomeration process. OC prepared by the AI and HI methods with NiO contents up to 25 wt%, OC prepared by the DP method on γ-Al 2 O 3 with NiO content lower than 30 wt%, and OC prepared by the DP method on α-Al 2 O 3 with a NiO content lower than 26 wt% did not agglomerated. OC that agglomerated showed an external layer of NiO over the particles. It seems that the most important factor affecting to the formation of the external NiO layer on the OC, and so to the agglomeration process, was the metal content of the OC. The attrition rates of the OC prepared using γ-Al 2 O 3 as support were higher than the ones prepared using α-Al 2 O 3 as support, and in general the attrition rates of all the OC were low. The OC prepared by AI, HI or DP methods on α-Al 2 O 3 as support had appropriated characteristics to be used in the chemical-looping combustion process.

[1]  Hongguang Jin,et al.  A new type of coal gas fueled chemical-looping combustion , 2004 .

[2]  Anders Lyngfelt,et al.  Solid fuels in chemical-looping combustion , 2008 .

[3]  Wei-Ping Pan,et al.  Investigation of chemical looping combustion by solid fuels. 1. Process analysis , 2006 .

[4]  R. J. Copeland,et al.  Analysis of the sorbent energy transfer system (SETS) for power generation and CO2 capture , 2003 .

[5]  Mohammad. M. Hossain,et al.  Reactivity and stability of Ni/Al2O3 oxygen carrier for chemical-looping combustion (CLC) , 2008 .

[6]  Yu‐Wen Chen,et al.  Temperature-programmed-reduction studies of nickel oxide/alumina catalysts: effects of the preparation method , 1995 .

[7]  Jeong-Hoo Choi,et al.  Oxidation and reduction characteristics of oxygen carrier particles and reaction kinetics by unreacted core model , 2001, Korean Journal of Chemical Engineering.

[8]  Toshihiro Okamoto,et al.  A Fundamental Study of a New Kind of Medium Material for Chemical-Looping Combustion , 1996 .

[9]  T. Mattisson,et al.  Redox investigation of some oxides of transition-state metals, Ni, Cu, Fe, and Mn Supported on SiO2 , 2005 .

[10]  A. Lyngfelt,et al.  Comparison of iron-, nickel-, copper- and manganese-based oxygen carriers for chemical-looping combustion , 2004 .

[11]  Hongbin Zhao,et al.  Preparation and characterisation of nickel-modified ceramic filters , 2000 .

[12]  Mohammad. M. Hossain,et al.  Co–Ni/Al2O3 oxygen carrier for fluidized bed chemical-looping combustion: Desorption kinetics and metal–support interaction , 2007 .

[13]  Juan Adánez,et al.  Impregnated CuO/Al2O3 Oxygen Carriers for Chemical-Looping Combustion: Avoiding Fluidized Bed Agglomeration , 2005 .

[14]  Arvind Varma,et al.  Spinel-Supported Oxygen Carriers for Inherent CO2 Separation during Power Generation , 2007 .

[15]  M. Twigg,et al.  X-ray diffraction study of the hydrogen reduction of NiO/α-Al2O3 steam reforming catalysts , 2004 .

[16]  M. Ishida,et al.  Experimental results of chemical-looping combustion with NiO/NiAl2O4 particle circulation at 1200 °C , 2002 .

[17]  A. Lyngfelt,et al.  Construction and 100 h of operational experience of a 10-kW chemical looping combustor , 2005 .

[18]  Qiming Zhu,et al.  Effects of promoters and preparation procedures on reforming of methane with carbon dioxide over Ni/Al2O3 catalyst , 1996 .

[19]  A. Lyngfelt,et al.  Reactivity of some metal oxides supported on alumina with alternating methane and oxygen - Application for chemical-looping combustion , 2003 .

[20]  O. Levenspiel.  Chemical Reaction Engineering , 1972 .

[21]  S. D. Kim,et al.  Chemical-Looping Combustion with NiO and Fe2O3 in a Thermobalance and Circulating Fluidized Bed Reactor with Double Loops , 2006 .

[22]  M. Johansson,et al.  The use of NiO as an Oxygen Carrier in Chemical-Looping Combustion , 2006 .

[23]  Richard Blom,et al.  Chemical looping combustion using NiO/NiAl2O4 : Mechanisms and kinetics of reduction-oxidation (Red-Ox) reactions from in situ powder X-ray diffraction and thermogravimetry experiments , 2006 .

[24]  G. Ertl,et al.  Handbook of Heterogeneous Catalysis , 1997 .

[25]  L. M. Gandía,et al.  Influence of the preparation method and the nature of the support on the stability of nickel catalysts , 1994 .

[26]  Ningsheng Cai,et al.  Reduction of iron oxide as an oxygen carrier by coal pyrolysis and steam char gasification intermediate products , 2007 .

[27]  A. Abad,et al.  Chemical Looping Combustion in a 10 kWth Prototype Using a CuO/Al2O3 Oxygen Carrier: Effect of Operating Conditions on Methane Combustion , 2006 .

[28]  R. Villa.  Ni based mixed oxide materials for CH4 oxidation under redox cycle conditions , 2003 .

[29]  Juan Adánez,et al.  Nickel−Copper Oxygen Carriers To Reach Zero CO and H2 Emissions in Chemical-Looping Combustion , 2006 .

[30]  A. Abad,et al.  Selection of Oxygen Carriers for Chemical-Looping Combustion , 2004 .

[31]  Arvind Varma,et al.  Solution combustion synthesized oxygen carriers for chemical looping combustion , 2007 .

[32]  Stuart A. Scott,et al.  In situ gasification of a solid fuel and CO2 separation using chemical looping , 2006 .

[33]  A. Abad,et al.  Effect of support on reactivity and selectivity of Ni-based oxygen carriers for chemical-looping combustion , 2008 .

[34]  Juan Adánez,et al.  Development of Oxygen Carriers for Chemical-Looping Combustion , 2005 .

[35]  Mohammad. M. Hossain,et al.  Reduction kinetics of a fluidizable nickel–alumina oxygen carrier for chemical-looping combustion , 2008 .