Characterization of Mechanically Alloyed Powders for High-Cr Oxide Dispersion Strengthened Ferritic Steel

High-Cr oxide dispersion strengthened (ODS) ferritic steel powders with the nominal composition of Fe–16Cr–4Al–0.1Ti–0.35Y2O3 in wt% were produced by milling of elemental powders and Y2O3 particles in argon atmosphere to investigate changes in the particle properties during mechanical alloying (MA). SEM observation and PSD analysis revealed that the MA powders milled for different times were composed of agglomerated particles having multimodal distributions with substantial size variation ranging from several μm to 350 μm. The mean size of particles rapidly increased at the initial stage of MA, then gradually decreased to 22 μm with increasing milling time up to 48 h, and kept constant thereafter. During milling of the Fe–16Cr–4Al–0.1Ti–0.35Y2O3 powder, MA within 6 h had mainly taken place between Fe and Al to form a bcc-Fe(Al) solid solution. The lattice constant of bcc-Fe steadily increased with a drastic increase in the solute concentrations of Cr, Al, and Ti in Fe. Alloying between Fe and alloying elements is almost fulfilled after milling for 48 h. The MA powder milled in air was much smaller than that milled in gaseous argon under the same conditions. Milling in an air atmosphere is effective to reduce the particle size of the ODS ferritic steel powder, although the pickup of oxygen from environment causes too high excess oxygen content.

[1]  T. Okuda,et al.  Development of Oxide Dispersion Strengthened Ferritic Steels for FBR Core Application, (I). Improvement of Mechanical Properties by Recrystallization Processing.:Improvement of Mechanical Properties by Recrystallization Processing , 1997 .

[2]  K. Ishihara,et al.  Metastable phases of Al–Fe system by mechanical alloying , 1997 .

[3]  A. Kimura,et al.  Corrosion properties of oxide dispersion strengthened steels in super-critical water environment , 2004 .

[4]  T. Okuda,et al.  Tube manufacturing and characterization of oxide dispersion strengthened ferritic steels , 2000 .

[5]  Yucheng Wu,et al.  Structural evolution and grain growth kinetics of the Fe–28Al elemental powder during mechanical alloying and annealing , 2007 .

[6]  A. Kimura,et al.  Corrosion resistance of high-Cr oxide dispersion strengthened ferritic steels in super-critical pressurized water , 2007 .

[7]  Shigeharu Ukai,et al.  Tube manufacturing trials by different routes in 9CrW-ODS martensitic steels , 2004 .

[8]  T. Yoshitake,et al.  Burst properties of irradiated oxide dispersion strengthened ferritic steel claddings , 2002 .

[9]  S. Ukai,et al.  Improvement of 9Cr-ODS martensitic steel properties by controlling excess oxygen and titanium contents , 2004 .

[10]  G. Speich,et al.  Effects of Co, Cr, Ir, Pt, Re, Rh, and Ru on the lattice parameter and density of alpha iron , 1973 .

[11]  Shigeharu Ukai,et al.  Improvement of compatibility of advanced ferritic steels with super critical pressurized water toward a higher thermally efficient water-cooled blanket system , 2006 .

[12]  A. Kimura,et al.  Effect of milling on morphological and microstructural properties of powder particles for High-Cr oxide dispersion strengthened ferritic steels , 2007 .

[13]  S. Ukai,et al.  Production and Properties of Nano-scale Oxide Dispersion Strengthened (ODS) 9Cr Martensitic Steel Claddings , 2003 .

[14]  D. Gelles,et al.  Irradiation creep and swelling from 400 to 600 °C of the oxide dispersion strengthened ferritic alloy MA957 , 2004 .

[15]  Shigeharu Ukai,et al.  R&D of oxide dispersion strengthened ferritic martensitic steels for FBR , 1998 .

[16]  Shigeharu Ukai,et al.  Development of oxide dispersion strengthened steels for FBR core application, (II). Morphology improvement by martensite transformation , 1998 .