c-Si solar cells formed from spin-on phosphoric acid and boric acid

This paper reports the fabrication of c-Si based solar cells using spin-on dopants. Solar cells were developed by texturing both surfaces of the c-Si, and forming the p–n junction by spin-coating the n-type dopant followed by rapid thermal processing (RTP). For back surface field formation on the rear side, a similar spin-coating step was undertaken for one cell and e-beam Al deposition for the other. In the case of double-sided spin-coated cell, simultaneous p–n junction and back surface field were formed in one RTP cycle. Without using high performance features in the device, double-sided spin-on doped cell showed Voc of 600 ± 0.01 mV, Jsc of 33.1 ± 0.03 mA/cm2, FF of 74.26 ± 0.06% and efficiency of 14.74%. As compared to single-sided spin-on doped cell, an improvement in efficiency of about 1.3% has been obtained which can be attributed to boron back surface field. Double-sided spin-on process significantly reduces thermal budget and improves throughput. Besides texturization, high efficiency features have not been used in the device. The results clearly demonstrate that c-Si based solar cells are potentially cost effective to manufacture.

[1]  A. Rohatgi,et al.  Boron Diffusion with Boric Acid for High Efficiency Silicon Solar Cells , 2010 .

[2]  A. Rohatgi,et al.  Fabrication of 20 % efficient cells using spin-on based simultaneous diffusion and dielectric anneal , 2009, 2009 34th IEEE Photovoltaic Specialists Conference (PVSC).

[3]  J. Ramanujam,et al.  Photovoltaic Properties of a-Si:H Films Grown by Plasma Enhanced Chemical Vapor Deposition: A Review , 2012 .

[4]  L. Ventura,et al.  Simultaneous dopant diffusion and surface passivation in a single rapid thermal cycle , 1996 .

[5]  Hongbin Cao,et al.  N+ emitters realized using Ammonium Dihydrogen Phosphate for silicon solar cells , 2013 .

[6]  Chung-Hsiao E. Rd,et al.  17.9% E-ciency Silicon Solar Cells by Using Spin-on Films Processes , 2011 .

[7]  Rachid Chaoui,et al.  Improvement of Screen-Printed Textured Monocrystalline Silicon Solar Cell Performance by Metal-Assisted Chemical Etching , 2013 .

[8]  J. Y. Lee,et al.  Boron back surface field using spin-on dopants by rapid thermal processing , 2004 .

[9]  D. Biro,et al.  Microscopic homogeneity of emitters formed on textured silicon using in-line diffusion and phosphoric acid as the dopant source , 2009 .

[10]  R. Jeyakumar,et al.  Fabrication of c-Si solar cells using boric acid as a spin-on dopant for back surface field , 2014 .

[11]  M. Brito,et al.  First solar cells on silicon wafers doped using sprayed boric acid , 2010 .

[12]  M. González-Mañas,et al.  On the texturization of monocrystalline silicon with sodium carbonate solutions , 2007 .

[13]  Irena Zubel,et al.  The effect of isopropyl alcohol on etching rate and roughness of (1 0 0) Si surface etched in KOH and TMAH solutions , 2001 .

[14]  Jinsu Yoo,et al.  Reactive ion etching (RIE) technique for application in crystalline silicon solar cells , 2010 .

[15]  R. Mertens,et al.  Rapid thermal annealing of spin-coated phosphoric acid films for shallow junction formation , 1997 .

[16]  A. Rohatgi,et al.  Optimization of phosphoric acid based limited-source-diffusion to obtain high quality emitter for screen printed contacts , 2011, 2011 37th IEEE Photovoltaic Specialists Conference.

[17]  M. Boumaour,et al.  N+ silicon solar cells emitters realized using phosphoric acid as doping source in a spray process , 2006 .

[18]  J. J. Gandía,et al.  Optimisation of NaOH texturisation process of silicon wafers for heterojunction solar-cells applications , 2012 .

[19]  Pedro Rosales,et al.  A comparative study of wet and dry texturing processes of c-Si wafers for the fabrication of solar cells , 2014 .

[20]  Akira Usami,et al.  Shallow-junction formation on silicon by rapid thermal diffusion of impurities from a spin-on source , 1992 .

[21]  A. Rohatgi,et al.  20% Efficient screen-printed n-type solar cells using a spin-on source and thermal oxide/silicon nitride passivation , 2011, 2011 37th IEEE Photovoltaic Specialists Conference.