Enhanced Experimental Testing of New Erosion-Resistant Compressor Blade Coatings

Performance differences between bare 17-4PH steel V103 profile (NACA 6505 with rounded leading edge (LE) and trailing edge (TE)) gas turbine engine axial compressor blades, and those coated with either a chromium-aluminum-titanium nitride (CrAlTiN) or a titanium-aluminum nitride (TixAl1−xN) erosion-resistant coating were tested. A coating thickness of 16 μm was used, based on experimental results in the literature. Coatings were applied using arc physical vapor deposition at the National Research Council of Canada (NRC). All blades were tested under identical operating conditions in the Royal Military College of Canada (RMC) turbomachinery erosion rig. Based on a realism factor (RF) defined by the authors, this experimental rig was determined to provide the best known approximation to actual compressor blade erosion in aircraft gas turbine engine axial compressors. An average brown-out erosive media concentration of 4.9 g/m3 of air was used during testing. An overall defined Leithead–Allan–Zhao (LAZ) score metric, based on mass and blade dimension changes, compared the erosion-resistant performance of the bare and coated blades. Blade surface roughness data were also obtained. Based on the LAZ Score, CrAlTiN-coated blades performed at least 79% better than bare blades, and TixAl1−xN-coated blades performed at least 93% better than bare blades. The TixAl1−xN-coated blades performed at least 33% better than the CrAlTiN-coated blades. Extrapolation of results predicted that a V-22 Osprey tiltrotor military aircraft, for example, could fly up to 79 more missions with TixAl1−xN-coated compressor blades in brown-out sand concentrations than with uncoated blades.

[1]  Jack D. Mattingly,et al.  Elements of Propulsion: Gas Turbines and Rockets , 1996 .

[2]  Ronald H. Aungier.  Axial-Flow Compressors , 2003 .

[3]  Weiliang Lou,et al.  Separation Bubbles Under Steady and Periodic-Unsteady Main Flow Conditions , 2000 .

[4]  C Balan,et al.  Axial Flow Compressor Performance Deterioration , 1984 .

[5]  R. L. Elder,et al.  Experimental investigation of axial fan erosion and performance degradation , 2004 .

[6]  William Allan,et al.  Performance Metrics and Experimental Testing of Erosion-Resistant Compressor Blade Coatings , 2015 .

[7]  Garth V. Hobson,et al.  Impact of Nonuniform Leading Edge Coatings on the Aerodynamic Performance of Compressor Airfoils , 2011 .

[8]  Irwin E. Treager.  Aircraft Gas Turbine Engine Technology , 1978 .

[9]  G. Sundararajan,et al.  Solid particle erosion behaviour of metallic materials at room and elevated temperatures , 1997 .

[10]  S. A. Muboyadzhyan.  Erosion-resistant coatings for gas turbine compressor blades , 2009 .

[13]  William D. Callister,et al.  Materials Science and Engineering: An Introduction , 1985 .

[14]  Paul Fletcher,et al.  Gas Turbine Performance , 1998 .

[15]  Seung Jin Song,et al.  Effects of Reynolds Number and Surface Roughness Magnitude and Location on Compressor Cascade Performance , 2012 .

[16]  Michael G. Dunn,et al.  Performance deterioration of a turbofan and a turbojet engine upon exposure to a dust environment , 1987 .

[17]  Michael Pfitzner,et al.  Unsteady Boundary Layer Development Due to Wake Passing Effects on a Highly Loaded Linear Compressor Cascade , 2004 .

[18]  Mark Klein,et al.  The Development of Innovative Methods for Erosion Testing a Russian Coating on GE T64 Gas Turbine Engine Compressor Blades , 2004 .