Short crack initiation and growth at 600 °C in notched specimens of Inconel718

The natural initiation and growth of short cracks in Inconel®718 U-notch specimens has been studied at 600 °C in air. U notches were introduced through broaching, and hardness traces and optical microscopy on cross-sections through the U notch broaching showed that the broaching process had introduced a deformed, work hardened layer. Fatigue tests were conducted under load control using a 1-1-1-1 trapezoidal waveform, on specimens with as-broached and polished U-notches. Multi-site crack initiation occurred in the notch root. Many of the cracks initiated at bulge-like features formed by volume expansion of oxidising (Nb,Ti)C particles. In unstressed samples, oxidation of (Nb,Ti)C particles occurred readily, producing characteristic surface eruptions. Scanning electron microscopy on metallographic sections revealed some sub-surface (Nb,Ti)C oxidation and localised matrix deformation around oxidised particles. A mechanism for crack initiation by carbide expansion during oxidation is discussed. Surface short crack growth rates in the notch root of polished specimens were measured using an acetate replica technique. Observed short-crack growth rates were approximately constant across a wide range of crack lengths. However, there was a transition to rapid, accelerating crack growth once cracks reached several hundred micrometers in length. This rapid propagation in the latter stages of the fatigue life was assisted by crack coalescence. Polishing the U-notch to remove broaching marks resulted in a pronounced increase in fatigue life.

[1]  David A. Fletcher,et al.  The United Kingdom Chemical Database Service , 1996, J. Chem. Inf. Comput. Sci..

[2]  A. Pineau,et al.  The effect of microstructure and environment on the crack growth behaviour of Inconel 718 alloy at 650 °C under fatigue, creep and combined loading , 1982 .

[3]  K. Miller.  THE TWO THRESHOLDS OF FATIGUE BEHAVIOUR , 1993 .

[4]  S. Suresh.  Fatigue of materials , 1991 .

[5]  L. Rémy,et al.  High temperature low cycle fatigue of MAR-M 509 superalloy II: The influence of oxidation at high temperatures , 1983 .

[6]  J. Lankford,et al.  Relevance of the small crack problem to lifetime prediction in gas turbines , 1987 .

[7]  A. Pineau,et al.  ELEVATED TEMPERATURE FATIGUE CRACK GROWTH IN ALLOY 718—PART I: EFFECTS OF MECHANICAL VARIABLES , 1993 .

[8]  T. Radtke,et al.  FATIGUE CRACK GROWTH IN NICKEL‐BASED SUPERALLOYS AT 500‐700°C. II: DIRECT‐AGED ALLOY 718 , 1994 .

[9]  A. Pineau,et al.  ELEVATED TEMPERATURE FATIGUE CRACK GROWTH IN ALLOY 718—PART II: EFFECTS OF ENVIRONMENTAL AND MATERIAL VARIABLES , 1993 .

[10]  K. Sadananda,et al.  Short crack growth behavior , 1997 .

[11]  L. James.  The effect of grain size upon the fatigue-crack propagation behavior of alloy 718 under hold-time cycling at elevated temperature , 1986 .

[12]  J. Healy,et al.  Short-fatigue-crack growth in a nickel-base superalloy at room and elevated temperature , 1991 .

[13]  L. Rémy,et al.  High temperature low cycle fatigue of MAR-M 509 superalloy I: The influence of temperature on the low cycle fatigue behaviour from 20 to 1100°C , 1983 .

[14]  F. Schulte,et al.  The Modifications of Niobium Pentoxide , 1966 .